Garuda - Garba Rujukan Digital

p-Index From 2020 - 2025

3.725

P-Index

This Author published in this journals

All Journal Jurnal Sains Materi Indonesia JURNAL ILMIAH PENDIDIKAN FISIKA AL BIRUNI EduChemia: Jurnal Kimia dan Pendidikan Gravity : Jurnal Ilmiah Penelitian dan Pembelajaran Fisika Journal of Teaching and Learning Physics Akta Kimia Indonesia JURNAL EKSAKTA PENDIDIKAN (JEP) KONSTAN - JURNAL FISIKA DAN PENDIDIKAN FISIKA Jurnal Pendidikan Fisika dan Teknologi DIFFRACTION: Journal for Physics Education and Applied Physics Indonesia Natural Research Pharmaceutical Journal (INRPJ) Optika : Jurnal Pendidikan Fisika Jurnal Pendidikan Fisika dan Sains (JPFS) Computational and Experimental Research in Materials and Renewable Energy (CERiMRE) Jurnal Pembelajaran Fisika Natural Science Education Research (NSER) Charm Sains : Jurnal Pendidikan Fisika Lontar Physics Today SEGARA : Jurnal Pengabdian Kepada Masyarakat

Rahmat Firman Septiyanto, Rahmat Firman

Jurusan Pendidikan Fisika FKIP UNTIRTA

Author-ID : 599739

Agriculture, Biological Sciences & Forestry Humanities Astronomy Biochemistry, Genetics & Molecular Biology Chemical Engineering, Chemistry & Bioengineering Chemistry Computer Science & IT Decision Sciences, Operations Research & Management Dentistry Earth & Planetary Sciences Education Electrical & Electronics Engineering Energy Environmental Science Health Professions Immunology & microbiology Materials Science & Nanotechnology Mathematics Medicine & Pharmacology Physics Social Sciences Other

Published : 32 Documents Claim Missing Document

Claim Missing Document

Articles

Title

Monte Carlo Simulation on TiO2 : Water Thickness Determination and Electron Scattering Study on Wet Material Rahmat Firman Septiyanto; Isriyanti Affifah
Gravity : Jurnal Ilmiah Penelitian dan Pembelajaran Fisika Vol 7, No 2 (2021)
Publisher : Universitas Sultan Ageng Tirtayasa

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.30870/gravity.v7i2.11592

Analysis of the three-dimensional (3D) structure of a material is indispensable in various fields of science, especially in materials science. Several studies have been conducted to observe the 3D structure of wet samples in a water-soluble environment using ESEM (Environmental Scanning Electron Microscopy) with tomography. The principle of tomography is based on the acquisition of a series of image projections at different angles of inclination and the calculation of the volume of the 3D reconstruction with a special algorithm. In this study, Monte Carlo simulation was used to analyze the optimum water thickness that could be detected in TiO2 wet material and the number of electron scattering captured to calculate the interaction volume dimensions. The results showed that the optimum thickness was achieved at 400 nm for the thickness of the wet sample and 10 nm for the thickness of the water.

PERBANDINGAN SIFAT MEKANIK BIOPLASTIK TERHADAP PENAMBAHAN ZINC OXIDE (ZnO) Syamsul Hidayat; Akbar Hanif Dawam Abdullah; Rahmat Firman Septiyanto; Yus Rama Denny Muchtar; Isriyanti Affifah
Gravity : Jurnal Ilmiah Penelitian dan Pembelajaran Fisika Vol 5, No 2 (2019)
Publisher : Universitas Sultan Ageng Tirtayasa

Bioplastik merupakan jenis plastik yang terbuat dari bahan alami sehingga dapat dengan mudah terdegradasi oleh aktivitas mikroorganisme salah bahannya adalah pati singkong. Akan tetapi bioplastik belum bisa diproduksi secara masal dan digunakan sehari-hari karena mamiliki sifat yang belum sesuai untuk menggantikan plastik yang ada saat ini. Penelitian ini bertujuan untuk mengetahui perbandingan sifat dan karakterisasi bioplastik tanpa penambahan filler lain dan bioplastik dengan penambahan nanopartikel Zinc Oxide. Beberapa pengujian dan karakterisasi dilakukan dalam penelitian ini, meliputi struktur morfologi, kekuatan mekanik, dan biodegradasi. Dari karakterisasi SEM dihasilkan bahwa bioplastik dengan penambahan nanopartikel Zinc Oxide cenderung memiliki morfologi yang lebih baik, tidak retak, walaupun terdapat agregasi partikel. Pengujian lain menunjukan bahwa nanopartikel Zinc Oxide mampu meningkatkan kekuatan tarik bioplastik namun menghambat pertumbuhan mikroorganisme

PENGARUH MODEL PEMBELAJARAN BERBASIS PROYEK PADA MATA KULIAH FISIKA DASAR TERHADAP HIGH ORDER THINKING SKILL MAHASISWA Rahmat Firman Septiyanto; Dina Rahmi Darman
Gravity : Jurnal Ilmiah Penelitian dan Pembelajaran Fisika Vol 4, No 1 (2018)
Publisher : Universitas Sultan Ageng Tirtayasa

Comparison of the mechanical properties of four-layer epoxy composite reinforced with natural jute fibers and symmetrical e-glass synthetic fibers Rahmat Firman Septiyanto; Hanif Akbar Dawam Abdullah; Isriyanti Affifah; Fatah Sulaiman; Syamsul Hidayat; Rahmat Awaludin Salam
Gravity : Jurnal Ilmiah Penelitian dan Pembelajaran Fisika Vol 6, No 1 (2020)
Publisher : Universitas Sultan Ageng Tirtayasa

ABSTRACTResearch that produces environmentally friendly products continues to be developing. Research related to the natural fiber jute material and epoxy matrix has done. Epoxy composite jute empowered do with the preparation of symmetry with four layers of fiber volume fraction of 27.89% and composite epoxy e-glass Fiber empowered four balance with 28.86% fiber volume fraction. Mechanical testing is done via Drag test to determine the tensile strength and stretch. From the analysis, it's finding that the tensile strength of the symmetry jute fiber reinforced epoxy tensile strength was 48,378 MPa, and the strain was 11,998%. Meanwhile, the tensile strength and pressure in empowered epoxy e-glass fiber symmetry of four layers, each for 95.516 MPa and 7.7032%. Characterization has also been carried out through SEM testing. The results show that e-glass fiber fractures can still be seen as regular and tend to be straight and flat rods compared to symmetrical fiber-reinforced jute composite epoxy composites whose fibers are irregular. So that shows that the strength of the epoxy composite reinforced e-glass fiber is very large compared to the strength of the four-layer jute fiber-reinforced epoxy composite symmetry.

PERBANDINGAN KOMPOSIT SERAT ALAM DAN SERAT SINTETIS MELALUI UJI TARIK DENGAN BAHAN SERAT JUTE DAN E-GLASS Rahmat Firman Septiyanto; Akbar Hanif Dawam Abdullah
Gravity : Jurnal Ilmiah Penelitian dan Pembelajaran Fisika Vol 2, No 1 (2016)
Publisher : Universitas Sultan Ageng Tirtayasa

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.30870/gravity.v2i1.912

Penelitian komposit dengan matriks epoksi berpenguat serat jute telah dilakukan dengan penyusunan 3 lapis simetri dengan fraksi volme serat sebesar 33,57%. Komposit epoksi berpenguat serat jute tersebut dilakukan pengujian tarik untuk mengetahui sifat mekanik. Sifat mekanik tersebut meliputi: kekuatan tarik, pertambahan panjang, dan kekuatan tarik spesifik. Kekuatan tarik komposit epoksi berpenguat serat jute 3 lapis simetri sebesar 45,961%. Pertambahan panjang sebesar 8,9278%. Kekuatan tarik spesifik tertinggi pada komposit epoksi berpenguat serat jute 3 lapis simetri sebesar 42,517 MPa/g.cm-3. Selain itu dibuat komposit epoksi berpenguat serat e-glass sebagai pembanding. Jika dibandingkan komposit epoksi berpenguat serat jute dengan komposit epoksi berpenguat serat e-glass maka kekuatan tarik rata-rata komposit epoksi berpenguat serat e-glass masih belum bisa menyamai. Akan tetapi, kekuatan komposit epoksi berpenguat jute memiliki potensi untuk menggantikan serat sintetis tersebut.

Perbandingan Komposit Serat Alam dan Serat Sintetis melalui Uji Tarik dengan Bahan Serat jute dan e-glass Rahmat Firman Septiyanto; Akbar Hanif Dawam Abdullah
Gravity : Jurnal Ilmiah Penelitian dan Pembelajaran Fisika Vol 1, No 1 (2015)
Publisher : Universitas Sultan Ageng Tirtayasa

. Penelitian komposit dengan matriks epoksi berpenguat serat jute telah dilakukan dengan penyusunan 3 lapis simetri dengan fraksi volme serat sebesar 33,57%. Komposit epoksi berpenguat serat jute tersebut dilakukan pengujian tarik untuk mengetahui sifat mekanik. Sifat mekanik tersebut meliputi: kekuatan tarik, pertambahan panjang, dan kekuatan tarik spesifik. Kekuatan tarik komposit epoksi berpenguat serat jute 3 lapis simetri sebesar 45,961%. Pertambahan panjang sebesar 8,9278%. Kekuatan tarik spesifik tertinggi pada komposit epoksi berpenguat serat jute 3 lapis simetri sebesar 42,517 MPa/g.cm-3. Selain itu dibuat komposit epoksi berpenguat serat e-glass sebagai pembanding. Jika dibandingkan komposit epoksi berpenguat serat jute dengan komposit epoksi berpenguat serat e-glass maka kekuatan tarik rata-rata komposit epoksi berpenguat serat e-glass masih belum bisa menyamai. Akan tetapi, kekuatan komposit epoksi berpenguat jute memiliki potensi untuk menggantikan serat sintetis tersebut.

Co-Authors Akbar Hanif Dawam Akbar Hanif Dawam Abdullah Akbar Hanif Dawam Abdullah Akbar Hanif Dawam Abdullah Akbar Hanif Dawam Abdullah Alfarouqy, Ahmad Haekal Amalia, Rizkika Anang Suryana Andri Suherman Andri Suherman Asep Saefullah Asep Saefullah Asep Saefullah Atifah Alya Ramadhina Agustin Atika Diah Isnaeni Putri Ayu, Widya Purbo Kusumaning Azmar, Azmar Bunbun Bundjali Dina Rahmi Darman Dinda Aulia Oktaviana Fatah Sulaiman Fauziah, Siti Sepiyanti Fida Madayanti Warganegara Fida Madayanti Warganegara Firmanul Catur Wibowo Fitri, Amelia Febriana Guntara, Yudi Guntara, Yudi Firman Hanif Akbar Dawam Abdullah Indri Sari Utami Irah Namirah Isriyanti Affifah, Isriyanti Junitasari, Junitasari Kurnia, Selvi M, Yus Rama Denny Masitoh Mangsur Mukhtar, Yus Rama Denny Mustaqim, Ilham Namirag, Irah Nisa Sa'diah Novita Aulia Safitri Prayoga, Adam Fori PUTRI HANDAYANI Qothrunnada, Qothrunnada Rahmat Awaludin Salam Rifdah Hanifah Sinda Intandiana Siti Nala Farihah Syamsul Hidayat Syamsul Hidayat Utami, Indri Sari Utami, Indri Sari Widyawati, Dian Yayat Ruhiat Yudi Guntara Yus Rama Denny Yusifa, Agni Yuvita Oktarisa, Yuvita

Title Search

Found 6 Documents Search Journal : Gravity : Jurnal Ilmiah Penelitian dan Pembelajaran Fisika

Abstract

Abstract

Abstract

Abstract

Abstract

Abstract

Title

Found 6 Documents
Search
Journal : Gravity : Jurnal Ilmiah Penelitian dan Pembelajaran Fisika