Preparasi dan Karakterisasi Katalis CoMo/H-Zeolit Y Musta, Rustam
Jurnal Fisika FLUX Vol 7, No 2 (2010): Jurnal Fisika Flux Edisi Agustus 2010
Publisher : Lambung Mangkurat University Press

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.20527/flux.v7i2.3090

Abstract

Preparation and characterization of catalyst CoMo/H-zeolite Y hasbeen done. Catalyst was prepared from NH4Y-zeolite then heated 115oC for 1 hto eliminate water then calcined at 550oC for 2 h to evaporate ammonia,produced HY-zeolite (HYZ) sample. Impregnation of CoMo metals on the HYZsample was done by co-impregnation method, where the HYZ (10 g) was mixedwith (NH4)6MO7O24.4H2O in 24 mL aquabidest and 3 mL of ammonia thenstirred of 60oC for 2 h. This mixture was then mixed with Co(NO3)2.6H2O in 24mL aquabidest and 3 mL of ammonia then stirred of 60oC for 2 h. The resultingsample was filtered and dried. The dried sample was then calcined under N2stream at temperature of 550oC for 2 h, followed by oxidized with O2 thenreduced with H2 stream at temperature 400oC for 2 h, respectively producedCoMo/HY catalyst. Characterization of the catalyst included analysis of NH3groups was done with by infra red spectrofotometry (IR), the crystallinity with Xraydiffraction (XRD) and the acidity was calculated with NH3 absorption bygravimetry method, metal content on the catalyst was determined by atomicabsorption spectroscopy (AAS). FTIR result of CoMo/HY catalyst showed thatdisappeared ammonia was after heating. The XRD date indicated the increase ofcatalyst crystallinity as the following: NH4Y< died NH4Y < HY< CoMo/HY.CoMo/HY catalyst has average acidity = 6,87 mmol/g where as the HY hasaverage acidity = 7,66 mmol/g. The metal content in the HY was 8023 and 7681ppm, for Co and Mo respectively.
HIDRODESULFURISASI TIOFEN MENGGUNAKAN KATALIS CoMo/H-ZEOLIT Y Musta, Rustam
Jurnal Fisika FLUX Vol 8, No 1 (2011): Jurnal Fisika Flux Edisi Februari 2011
Publisher : Lambung Mangkurat University Press

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.20527/flux.v8i1.3100

Abstract

Telah dilakukan penelitian terhadap reaksi hidrodesulfurisasi (HDS) tiofenmenggunakan katalis CoMo/H-zeolit Y. Proses hidrodesulfurisasi (HDS) tiofendilakukan dalam reaktor sistem batch dengan variasi temperatur 200, 250, 300, 350,400 oC dan variasi laju alir gas pembawa (H2) 40, 55, 70, 85, 100 mL/menit. Produkcair dianalisis dengan gas chromatography mass spectrometry (GC-MS). Konversiproduk gas dihitung berdasarkan persentase berat produk gas terhadap umpan. Hasilanalisis GCMS produk hasil reaksi hidrosulfurisasi tiofen menunjukkan adanya 1puncak utama tiofen pada waktu retensi 3,764 menit. Konversi gas maksimumtercapai pada suhu 350oC sebesar 82,07% (b/b) dengan konstanta laju reaksi (k)sebesar 49,56 menit-1.