Cellular Glass Manufactured by Microwave Irradiation of Residual Glass, Eggshell and Borax

Lucian Paunescu (Bilmetal Industries SRL Popesti Leordeni-Ilfov, Romania & Daily Sourcing & Research SRL Bucharest, Romania)
Sorin Mircea Axinte (Daily Sourcing & Research SRL Bucharest, Romania & Department of Applied Chemistry and Materials Science, University “Politehnica” of Bucharest, Romania)
Felicia Cosmulescu (Cosfel Actual SRL Bucharest, Romania)

Journal La Multiapp
Vol. 2 No. 5 (2021): Journal La Multiapp

The paper presents an improved method of manufacturing cellular glass using residual glass (91 %), sodium borate (5 %), eggshell waste (4 %) and added water (9 %). Compared to methods using eggshell as an expanding agent producing cellular glass with low compression strength, the technique adopted by the authors is original by the addition of sodium borate, which contributes to increasing the compression strength and the use of the unconventional electromagnetic wave heating method, which ensures very economical specific energy consumption. The optimal variant of cellular glass had the following characteristics: density of 0.40 g/cm3, porosity of 81 %, heat conductivity of 0.086 W/m·K, compression strength of 4.3 MPa and the cell dimension between 0.3-0.9 mm. The specific energy consumption of the process was 0.80 kWh/kg. The product has adequate features for using as a heat insulation material under conditions of quite high mechanical loading.