Optic Properties on AgGaSe2 Polycristal Fabrication

Soepardjo, A. Harsono (Unknown)
Janusetiawan, I Dewa Made (Unknown)

Article Info

Publish Date
03 Dec 2004

Abstract

Optic Properties on AgGaSe2 Polycristal Fabrication. Polycristal AgGaSe2, is compound (I-III-VI2) a semiconductor as basic material for thin film for solar cell. Polycristal was succesfully grown using Bridgmann Method, heated on sequential temperature treatment until 850°C and cooled down slowly until room temperature. Results observed were in the form of ingot (bars) with more or less 3 cm length and 13 mm in diameter. By using X-Ray Fefraction, composition obtained of each element (weight %) was Ag = 29,3996 %, Ga = 36,8123 % and Se = 30,29 % while using X-Ray Difraction lattice parameter obtained/calculated a = 4,4112 Å, c = 8,8854 Å, and c/a = 2,01426.

Copyrights © 2004




Citation Download
RIS
EndNote, Reference Manager, ProCite
BibTex
Latex, Jabref
Original Source
Download Original
Google Scholar
Check in Google Scholar
Journal Info
Makara Journal of Technology
Website

Abbrev

publication:mjt

Publisher

Universitas Indonesia

Subject

Chemical Engineering, Chemistry & Bioengineering Civil Engineering, Building, Construction & Architecture Electrical & Electronics Engineering Engineering Materials Science & Nanotechnology Mechanical Engineering

Description

MAKARA Journal of Technology is a peer-reviewed multidisciplinary journal committed to the advancement of scholarly knowledge and research findings of the several branches of Engineering and Technology. The Journal publishes new results, original articles, reviews, and research notes whose content ...