<![CDATA[This aim of this research was to determine the effects of using hydrogenated natural rubber to the oxidation and ozone resistance in producing rubber goods, especially motorcycle grip handle that fulfill the standard requirement. The experiment was done using rubber compound mixture of RSS, EPDM, and RHG with different ratio formula. The result show that the addition of natural rubber (RSS), synthetic rubber (EPDM), and hydrogenated rubber RHG) had significant effect on the visual test, hardness, tensile strength, tear resistance, density, and ozone. The result of these compounds shows that the best rubber compound for grip handle is the formulation which fulfills the qualification of national standard of Indonesia for motorcycles grip handle, SNI 06-7031-2004 is the formula with natural rubber 70 phr and hydrogenated rubber 30 phr. This formulation fulfill the qualification for visual test which is not defect, hardness 72.85 shore A, tensile strength 89.75 kg/cm2, tear resistance 34.75 kg/cm2, density 1256.23 g/cm3, and ozone resistance, 25 phm, 20% strain at 40 oC for 48 hours.Keywords : Hydrogenated rubber (RHG), natural rubber (RSS), synthetic rubber (EPDM), rubber compound of grip handleAbstrakPenelitian ini bertujuan untuk mengetahui pengaruh penggunaan karet alam hidrogenasi terhadap ketahanan oksidasi dan ozon dalam pembuatan barang jadi karet, serta mendapatkan formula kompon karet pegangan setang (grip handle) sepeda motor yang memenuhi persyaratan. Kompon karet dibuat dari campuran karet alam (RSS), karet sintetis (EPDM), dan karet hidrogenasi (RHG) dengan variasi perbandingan yaitu formula 1 (karet alam 70 phr dan karet sintetis 30 phr), formula 2 (karet alam 80 phr dan karet hidrogenasi 20 phr), formula 3 (karet alam 70 phr dan karet hidrogenasi 30 phr), formula 4 (karet alam 50 phr dan karet hidrogenasi 50 phr), dan formula 5 (karet alam 30 phr dan karet hidrogenasi 70 phr). Hasil penelitian menunjukkan bahwa penambahan karet alam (RSS), karet sintetis (EPDM), dan karet hidrogenasi (RHG) berpengaruh nyata terhadap uji visual, Kekerasan, Tegangan putus, Ketahanan sobek, Berat jenis dan Ketahanan terhadap ozon. Hasil penelitian terghadap 5 (lima) jenis kompon menunjukkan bahwa formula kompon pegangan setang yang terbaik adalah yang memenuhi persyaratan Standar Nasional Indonesia (SNI) untuk karet pegangan setang sepeda motor, SNI 06- 7031-2004, yaitu formula 3 (karet alam 70 phr dan karet hidrogenasi 30 phr). Formula ini memenuhi persyaratan untuk pengujian visual yaitu tidak cacat, kekerasan 72,85 Shore A, tegangan putus 89,75 kg/cm2, ketahanan sobek 34,75 kg/cm2, berat jenis 1256,23 g/cm3, dan ketahanan terhadap ozon 25 phm, 20% regangan 40 oC selama 48 jam tidak retak.Kata Kunci : Karet alam (RSS), karet sintetis (EPDM), karet hidrogenasi (RHG), kompon karet pegangan setang]]>
Copyrights © 2012