Biocompatibility of Silicone Elastomer Incorporated with Chitosan: Morphology, Mechanical, Biodegradation Assessment and the Potential for Injectable Biomaterials

Rasyida, Amaliya (Department of Materials and Metallurgical Engineering, Institut Teknologi Sepuluh Nopember Surabaya, Indonesia)
Maharsipu, Yohannes Gabriel Adven Christy (Department of Materials and Metallurgical Engineering, Institut Teknologi Sepuluh Nopember Surabaya, Indonesia)
Purniawan, Agung (Department of Materials and Metallurgical Engineering, Institut Teknologi Sepuluh Nopember Surabaya, Indonesia)
Fikri Kurniawan, Muhammad (Department of Materials and Metallurgical Engineering, Institut Teknologi Sepuluh Nopember Surabaya, Indonesia)
Tri Wicaksono, Sigit (Department of Materials and Metallurgical Engineering, Institut Teknologi Sepuluh Nopember Surabaya, Indonesia)
Ardhyananta, Hosta (Department of Materials and Metallurgical Engineering, Institut Teknologi Sepuluh Nopember Surabaya, Indonesia)

IPTEK The Journal for Technology and Science
Vol 35, No 3 (2024)

One of the major concerns associated with the use of silicone material is microorganisms and fungal growth which can result in degradation of the material, inflammation, and chronic infection. Thus, the development of antimicrobial silicone elastomer is becoming necessary. The aim of this study was to evaluate the effect of adding different concentrations of chitosan particles into the silicone matrix. The samples were characterized using a Universal Testing Machine (UTM), Scanning Electron Microscopy (SEM), MTT Assay, antibacterial and hydrolytic material degradation for a month. The addition of 50% chitosan recorded the highest value in the pore area of 29.282 with the widest zone of bacterial inhibition of 6.4 ± 0.4 mm as well as the highest% cell viability of 80.08 ± 1.21%, the furthermore, the shortest lifetime predicted from biodegradation test was around 36 weeks.