<![CDATA[Recycled aggregate concrete (RAC) is a sustainable alternative construction material to reduce natural resource exploitation and manage construction and demolition waste. However, predicting the mechanical performance of RAC remains a challenge due to the high variability of recycled aggregate properties. The purpose of this study is to develop a machine learning model to predict the compressive strength of recycled aggregate-based concrete and compare its performance with normal concrete. The dataset used consists of 2165 samples (1600 normal concrete and 565 recycled aggregate concrete) collected from various scientific publications. Three tree-based machine learning algorithms (Random Forest, XGBoost, and LightGBM) were implemented and optimized using RandomizedSearchCV with 5-fold cross-validation. The results showed that LightGBM provided the best performance with R² = 0.92, MAE = 2.45 MPa, and RMSE = 3.52 MPa on the test set. This model is able to predict the compressive strength of normal concrete (R² = 0.92) and recycled aggregate concrete (R² = 0.91) with almost the same accuracy, indicating strong generalization. Feature importance analysis revealed that curing age, cement content, and water content are the most important factors in compressive strength prediction, while for RAC, recycled aggregate water absorption (WRCA) also makes a significant contribution. Error analysis shows that residuals are random and normally distributed without systematic bias. This model can reliably predict concrete compressive strength in the range of 20-60 MPa with an average error of ±3-4 MPa and can be integrated into mix proportioning design software to improve the efficiency of the design process and support the use of sustainable construction materials.]]>
Copyrights © 2026