Jurnal Riset Industri Hasil Hutan
Published by Kementerian Perindustrian Republik Indonesia
ISSN : 20861400     EISSN : 25030779     DOI : -
Core Subject : Science, Agriculture, Engineering,
Agriculture, Biological Sciences & Forestry Chemical Engineering, Chemistry & Bioengineering Chemistry Industrial & Manufacturing Engineering Materials Science & Nanotechnology
Jurnal Riset Industri Hasil Hutan (JRIHH) adalah jurnal yang diterbitkan oleh Balai Riset dan Standardisasi Industri Banjarbaru. JRIHH terbit 2 (dua) kali setiap tahun pada bulan Juni dan Desember dengan E-ISSN: 2503-0779 dan P-ISSN : 2086-1400. JRIHH fokus pada isu-isu sektor industri yang berhubungan dengan: 1. Pengembangan Teknologi Pengolahan Kayu dari Hasil Hutan Alam, Hutan Tanaman Industri, dan Hasil Hutan Perkebunan. 2. Pengembangan Teknologi Pengolahan/ Pemanfaatan Limbah Industri Hasil Hutan Kayu (limbah padat dan cair). 3. Pengembangan Teknologi Pengolahan Hasil Hutan lainnya (Rotan, Bambu, dan Hasil Hutan sampingan termasuk pemanfaatan hasil limbahnya).
Arjuna Subject : -
Articles 12 Documents
 1   2 
Search results for , issue "Vol 6, No 1 (2014)" : 12 Documents clear
SIFAT FISIK DAN KIMIA WOOD PELLET DARI LIMBAH INDUSTRI PERKAYUAN SEBAGAI SUMBER ENERGI ALTERNATIF Effendi Arsad
Jurnal Riset Industri Hasil Hutan Vol 6, No 1 (2014)
Publisher : Kementerian Perindustrian

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (1228.837 KB) | DOI: 10.24111/jrihh.v6i1.1219

Abstract

Carakteristic physical and chemistry of Wood pellet from Industrial Disposal of Wood as Sources  Energy Alternatif The research to gaved for physical and chemistry of Wood pellet from Industrial. Processing approximately 12%, sawdust dried to moisture content of  sieved that is size of 15 mesh, 25 mesh and 35 mesh. Heating temperature were 60 0C and 110 0C. Moisture content of flawer wood pellet 4,46% - 9,95%, acacia wood pellet were 4.38% - 7.52% and tarap wood pellet were  4.60% - 9.98%. Density of flawer  wood pellet  were 0.51 - 0.78, acacia wood pellet were 0.61 - 0.78 and tarap wood pellet were   0.56 - 0.71, ash content of wood  flawer  from 0.87 - 2.04%, acacia 0.54 - 0.94% and ash content of  tarap wood 1.71 - 2.05%. Calorific value of wood pellets flawers wood 3921,12 - 4150,19 cal/g, acacia wood 4022,29 - 4254,91 cal/g and tarap wood  3920,13 - 4125,28 cal/g. The higher temperature of the heating effect on reality the reduction of water and the weight of ash wood pellets  while it was increasing calorific value.Keywords: waste wood, flawers wood, acacia wood, tarap wood, wood pellet
PAPAN PARTIKEL DARI CAMPURAN LIMBAH ROTAN DAN PENYULINGAN KULIT KAYU GEMOR (Alseodaphne spp) Cahyana, Budi Tri
Jurnal Riset Industri Hasil Hutan Vol 6, No 1 (2014)
Publisher : Kementerian Perindustrian

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (219.045 KB) | DOI: 10.24111/jrihh.v6i1.1224

Abstract

Utilization of rattan waste and gemor bark (Alseodaphne spp) distillation  for particle board had been carried out. The aim of this research was to know physical mechanical particle board from rattan waste mixed with gemor bark distillation. The raw materials used were cut-rattan waste of 2 cm and gemor bark distillation mashed in 16 mesh. The adhesive used were starch and PVAC. Composition variety of the mixture of rattan waste and gemor bark distillation particle were 50%: 50%, 60%: 40%, 70%: 30% and 5% adhesive. The results showed that highest average of modulus of rupture (26,62 kg/cm2) was obtained in 60% : 40% comparison of rattan waste and gemor bark distillation with starch adhesive (a2b1) and the density was 0.75 gr/cm3. The highest average of modulus of elasticity (633,76 kg/cm2) was in composition of 60%: 40% with PVAc adhesive (a2b2) and the density was 0,71 gr/cm3. The highest average of tensile strength (3,15 kg/cm2) was obtained in composition of 60%: 40% with starch adhesive (a2b1) and the density was  0.75 gr/cm3.Keywords: rattan waste, gemor bark distillation, particle board

Page 2 of 2 | Total Record : 12

 1   2 

Filter by Year

2014 2014


Reset
Filter By Issues
All Issue Vol 14, No 2 (2022) Vol 14, No 1 (2022) Vol 13, No 2 (2021) Vol 13, No 1 (2021) Vol 12, No 2 (2020) Vol 12, No 1 (2020) Vol 11, No 2 (2019) Vol 11, No 1 (2019) Vol 10, No 2 (2018) Vol 10, No 1 (2018) Vol 9, No 2 (2017) Vol 9, No 2 (2017) Vol 9, No 1 (2017) Vol 9, No 1 (2017) Vol 8, No 2 (2016) Vol 8, No 2 (2016) Vol 8, No 1 (2016) Vol 8, No 1 (2016) Vol 7, No 2 (2015) Vol 7, No 2 (2015) Vol 7, No 1 (2015) Vol 7, No 1 (2015) Vol 6, No 2 (2014) Vol 6, No 2 (2014) Vol 6, No 1 (2014) Vol 6, No 1 (2014) Vol 5, No 2 (2013) Vol 5, No 2 (2013) Vol 5, No 1 (2013) Vol 5, No 1 (2013) Vol 4, No 2 (2012) Vol 4, No 2 (2012) Vol 4, No 1 (2012) Vol 4, No 1 (2012) Vol 3, No 2 (2011) Vol 3, No 2 (2011) Vol 3, No 1 (2011) Vol 3, No 1 (2011) Vol 2, No 2 (2010) Vol 2, No 2 (2010) Vol 2, No 1 (2010) Vol 2, No 1 (2010) Vol 1, No 2 (2009) Vol 1, No 2 (2009) Vol 1, No 1 (2009) Vol 1, No 1 (2009) More Issue