Article Per Year (5 Year)
p-Index From 2021 - 2026
0.23
P-Index
This Author published in this journals
All Journal Jurnal BETA (Biosistem dan Teknik Pertanian)
Anna Sukma Muthia
Program Studi Teknik Pertanian, Fakultas Teknologi Pertanian, Universitas Udayana. Kampus Bukit Jimbaran, Badung-Bali
Agriculture, Biological Sciences & Forestry Biochemistry, Genetics & Molecular Biology

Published : 1 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 1 Documents
Search

 1 
Pengaruh Suhu Gelatinisasi dan Durasi Pengadukan terhadap Karakteristik Film Kemasan Cerdas Bioplastik Anna Sukma Muthia; Ni Luh Yulianti; I Wayan Widia
Jurnal BETA (Biosistem dan Teknik Pertanian) Vol 10 No 2 (2022): September
Publisher : Program Studi Teknik Pertanian dan Biosistem, Fakultas Teknologi Pertanian, Universitas Udayana, Badung, Bali, Indonesia

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.24843/JBETA.2022.v10.i02.p18

Abstract

Packaging characteristics can be affected by gelatinization temperature and stirring duration. This research was conducted to obtain gelatinization temperature and stirring duration effect to bioplastic smart packaging film characteristics and to obtain a combination of gelatinization temperature and stirring duration that can produce the best packaging characteristic. The experimental design used was a Randomized Block Design (RBD) with the first-factor treatment is gelatinization temperature (T) which consisted of 3 levels: 75oC, 80oC, and 85oC. The second factor is stirring duration (D) which consisted of 3 levels: 5, 10 dan 15 minutes, with two repetitions to produce 18 experimental units. The data obtained were analyzed by using Analysis of variance (ANOVA) and if the treatment affected the observed parameters, the test was continued with Duncan's test. Gelatinization temperature treatment and stirring duration in the making of starch and bioplastic smart packaging affect the value of tensile strength, elongation, elasticity, water resistance, thickness, and color change of smart packaging films. The gelatinization temperature treatment of 80oC and the stirring duration of 5 minutes resulted in smart packaging with the characteristics of tensile strength of 14.10 MPa, elongation 3.73%, elasticity 397.75 MPa, water resistance 96.58%, and thickness 0.40mm and show responsive color changes.