Article Per Year (5 Year)
p-Index From 2021 - 2026
0
P-Index
This Author published in this journals
All Journal Journal of Mechanical Engineering Science and Technology Journal of Energy, Mechanical, Material and Manufacturing Engineering
Kaiser, Samiul
Unknown Affiliation
Energy Engineering Industrial & Manufacturing Engineering Materials Science & Nanotechnology Mechanical Engineering

Published : 2 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 2 Documents
Search

 1 
WEAR BEHAVIOR OF COMMERCIAL TIRE RUBBER AGAINST MILD STEEL IN DRY, WET AND 3.5% NACL CORROSIVE ENVIRONMENT Kaiser, Samiul; Kaiser, Mohammad Salim; Ahmed, Sheikh Reaz
JEMMME (Journal of Energy, Mechanical, Material, and Manufacturing Engineering) Forthcoming Issue
Publisher : University of Muhammadiyah Malang

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.22219/jemmme.v5i1.10428

Abstract

The tribological performance of commercially used tire rubber was evaluated at ambient conditions under dry, wet and 3.5% NaCl corrosive environment. A pin-on-disc apparatus was used for the experiment. Applied load of 2.5N at sliding velocity of 0.246 ms-1 distance ranging from 75m-2650m were used for this study. The results showed that the nature of the wear rate was similar in all environments as initially increases afterwards decreases to more or less a constant value. Moreover, the wear rate in dry environment was significantly higher than that of wet and corrosive environment. Water tends to lubricate the contact, reduce the heat generation as well as for sealing effects thus the wear rate is reduced. Coefficient of friction in wet and corrosive environment showed the lower value due to sealing and lubricating effect between the particles. The damage behaviors of worn surfaces were analyzed by optical microscope and SEM. At dry sliding condition greater voids and holes are observed.
Physical Behaviour of Thermally Affected Bronze and Brass Kaiser, Samiul; Kaiser, Mohammad Salim
Journal of Mechanical Engineering Science and Technology (JMEST) Vol 4, No 1 (2020)
Publisher : Universitas Negeri Malang

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.17977/um016v4i12020p001

Abstract

The physical behavior of thermally affected cast copper, aluminium bronze and brass has been studied by subjecting to heating isochronally for one hour at a range of 600°C. It shows that solid-solution hardening takes place into the Al added bronze and Zn added brass metal. Due to heating Al forms hard and brittle intermetallic of copper aluminites into bronze metal which responses some age hardening effects. The electrical conductivity of the metals increases initially through heat treatment due to stress relieving and finally decreases due to formation of intermetallic precipitates. The color of the heated samples are also studied through tristimulus color ‘L*’, ‘a*’ and ‘b*’ values which were analyzed and evaluated in MATLAB software. It is found that incorporation of Al and Zn affects the colour of cast Cu. The overall change of color occurs with increasing heating temperature due to chemical changes like oxidization, intermetallic formation, dissolution of phases, precipitation coarsening and recrsystallization. Due to change of hardness and microstructural properties of the experimental metals the sound intensity level also decreases at high heating temperature. A microstructural study confirms that the cast alloys contents the different phases of grains and bring about re-crystallized state after heating at 500°C for one hour.
Co-Authors Ahmed, Sheikh Reaz Kaiser, Mohammad Salim