KARAKTERISASI INGOT PADUAN Zr-Mo-Fe-Cr PASCA PERLAKUAN PANAS Sungkono .; Isfandi .
Urania : Jurnal Ilmiah Daur Bahan Bakar Nuklir Vol 16, No 1 (2010): Januari 2010
Publisher : website

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (707.415 KB) | DOI: 10.17146/urania.2010.16.1.2436

Abstract

ABSTRAK KARAKTERISASI INGOT PADUAN Zr-Mo-Fe-Cr PASCA PERLAKUAN PANAS. Ingot paduan Zr-Mo-Fe-Cr hasil leburan (as melt) mempunyai mikrostruktur tidak homogen, yaitu campuran butir dendrit dan acicular. Ingot paduan Zr-Mo-Fe-Cr perlu diperlakupanaskan agar diperoleh mikrostruktur ekuiaksial dan homogen. Sasaran yang ingin dicapai dengan mikrostruktur tersebut adalah ingot paduan bersifat lunak sehingga memudahkan proses pengerjaan berikutnya dengan deformasi besar tanpa retak. Tujuan penelitian adalah mendapatkan karakteristik ingot paduan Zr-Mo-Fe-Cr pasca perlakuan panas, yang meliputi mikrostruktur, kekerasan, dan komposisi kimia. Metoda yang digunakan adalah perlakuan panas terhadap ingot paduan Zr-0,3%Mo-0,5%Fe-0,5%Cr;  dan Zr-0,4%Mo-0,5%Fe-0,5% Cr pada temperatur 650 °C dengan waktu penahanan 1 jam, pengamatan mikrostruktur menggunakan mikroskop optik, uji kekerasan menggunakan microhardness Vickers, dan uji komposisi kimia menggunakan X-ray Fluorescence (XRF). Hasil penelitian menunjukkan bahwa mikrostruktur Zr-0,3%Mo-0,5%Fe-0,5% Cr relatif homogen dengan struktur butir ekuiaksial berukuran kecil. Sementara itu, mikrostruktur Zr-0,4%Mo-0,5%Fe-0,5%Cr belum homogen dengan struktur butir batang pipih dan ekuiaksial. Kekerasan paduan  Zr-0,3%Mo-0,5%Fe-0,5% Cr adalah 490,80 VHN, sedangkan paduan Zr-0,4%Mo-0,5%Fe-0,5% Cr adalah 536,80 VHN. Komposisi kimia paduan Zr-0,3%Mo-0,5%Fe-0,5%Cr adalah     Zr = 98,8537 %, Mo = 0,2860 %, Fe = 0,4371%, Cr = 0,4232 % berat, sedangkan paduan Zr-0,4%Mo-0,5%Fe-0,5%Cr adalah Zr = 98,8033 %, Mo = 0,3467 %, Fe = 0,4804 %, Cr = 0,3696 % berat. Karakter paduan yaitu mikrostruktur, kekerasan, dan komposisi kimia dipengaruhi oleh perlakuan panas dan kandungan unsur Mo dari ingot paduan Zr-Mo-Fe-Cr. Kata kunci : Karakterisasi, perlakuan panas,  mikrostruktur,  kekerasan, komposisi  kimia. ABSTRACT CHARACTERIZATION OF Zr-Mo-Fe-Cr ALLOY INGOT AFTER HEAT TREATMENT. As-melt Zr-Mo-Fe-Cr alloy ingot possesses microstructure that is inhomogeneous, which is a mixture of dendrite grains and acicular. The Zr-Mo-Fe-Cr alloy ingot requires heat treatment in order to obtain an equiaxial and homogeneous microstructure. The aim to attain such microstructure is to produce soft alloy ingot so as to allow easy treatment in the next stage, with large deformation without cracking. The objective of this study is to acquire the characteristics of Zr-Mo-Fe-Cr alloy ingot after heat treatment, which include microstructure, hardness and chemical composition. The methods being employed are heat treatment for Zr-0.3%Mo-0.5%Fe-0.5%Cr and Zr-0.4%Mo-0.5%Fe-0.5%Mo alloy ingots at a temperature of 650 °C with soaking time of 1 hour, observation of microstructure using optical microscope, hardness testing using Vickers microhardness, and chemical composition testing using X-ray Fluorescence (XRF). The results of the study shows that the microstructure of Zr-0.3%Mo-0.5%Fe-0.5%Cr is relatively homogeneous with small equiaxial grain structure. Meanwhile, the microstructure of Zr-0.4%Mo-0.5%Fe-0.5%Cr is not homogeneous with columnar and equiaxial grain structure, The hardness of Zr-0.3%Mo-0.5%Fe-0.5%Cr alloy is 490.80 VHN, whereas the hardness for Zr-0.4%Mo-0.5%Fe-0.5%Cr alloy is 536.80 VHN. The chemical composition of Zr-0.3%Mo-0.5%Fe-0.5%Cr is Zr = 98.9137 wt%, Mo = 0.2460 wt%, Fe = 0.4371 wt%, Cr = 0.4032 wt%; whereas the chemical composition for Zr-0.4%Mo-0.5%Fe-0.5%Cr alloy is Zr = 98.8733 wt%, Mo = 0.3067 wt%, Fe = 0.4804 wt%, Cr = 0.3696 wt%. The alloy characteristics which include microstructure, hardness, and chemical composition are influenced by heat treatment and  the Mo content in the Zr-Mo-Fe-Cr alloy ingot. Free terms : Characterization, heat treatment, microstructure, hardness, chemical compositions. Keyword : Characterization, heat treatment, microstructure, hardness, chemical composition.
PENGARUH PERLAKUAN HOMOGENISASI TERHADAP KEKERASAN, LAJU KOROSI DAN MIKROSTRUKTUR PADUAN Zr-0,3%Mo-0,5%Fe-0,5%Cr Sungkono .; Isfandi .
Urania : Jurnal Ilmiah Daur Bahan Bakar Nuklir Vol 15, No 4 (2009): Oktober 2009
Publisher : website

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.17146/urania.2009.15.4.2563

Abstract

ABSTRAK PENGARUH PERLAKUAN HOMOGENISASI TERHADAP KEKERASAN, LAJU KOROSI, DAN MIKROSTRUKTUR PADUAN Zr-0,3%Mo-0,5%Fe-0,5%Cr. Ingot paduan Zr-0,3%Mo-0,5%Fe-0,5%Cr as melt belum mempunyai mikrostruktur yang homogen, sehingga perlu dihomogenisasi terlebih dahulu agar diperoleh mikrostruktur yang homogen. Tujuan penelitian adalah mendapatkan pengaruh perlakuan panas terhadap kekerasan, laju korosi, dan mikrostruktur paduan Zr-0,3%Mo-0,5%Fe-0,5% Cr.  Metoda yang digunakan adalah perlakuan homogenisasi terhadap ingot paduan Zr-0,3%Mo-0,5%Fe-0,5% Cr pada temperatur 650 dan 750 °C dengan waktu penahanan 30 menit, uji kekerasan menggunakan microhardness Vickers, uji korosi menggunakan metoda gravimetri tidak kontinyu, dan pengamatan mikrostruktur menggunakan mikroskop optik. Hasil penelitian menunjukkan bahwa kekerasan paduan Zr-0,3%Mo-0,5%Fe-0,5% Cr turun seiring dengan naiknya temperatur homogenisasi. Mikrograp paduan Zr-0,3%Mo-0,5%Fe-0,5%Cr (650oC, 30 menit) mempunyai lapisan oksida tipis di permukaan logam paduan pada waktu uji 32 jam (T = 250°C) dan 24-32 jam (T = 300°C). Mikrograp paduan Zr-0,3%Mo-0,5%Fe-0,5%Cr (750oC, 30 menit) mempunyai lapisan oksida tipis di permukaan logam paduan pada waktu uji 28-32 jam (T = 250°C) dan  24-32 jam (T = 300°C). Laju korosi paduan Zr-0,3%Mo-0,5%Fe-0,5%Cr dalam media uap air jenuh pada temperatur 250 dan 300 ºC mengikuti aturan kubik. Kekerasan, laju korosi, dan mikrostruktur dipengaruhi oleh perlakuan homogenisasi terhadap ingot paduan Zr-0,3%Mo-0,5%Fe-0,5%Cr. Kata kunci : Homogenisasi, kekerasan, mikrostruktur, laju korosi, ingot, paduan Zr-0,3%Mo-0,5%Fe-0,5%Cr. ABSTRACT THE INFLUENCE OF HOMOGENIZATION TREATMENT TO HARDNESS, CORROSION RATE, AND MICROSTRUCTURE OF Zr-0,3%Mo-0,5%Fe-0,5%Cr ALLOY. The ingot of Zr-0,3%Mo-0,5%Fe-0,5%Cr as melt not yet had homogeneous microstructure, so that need homogenized to be obtained by homogeneous microstructure. The objective of this research is to get influence of homogenization treatment to hardness, corrosion rate, and microstructure of Zr-0,3%Mo-0,5%Fe-0,5 % Cr alloy. The used method is homogenization treatment to ingot of Zr-0,3%Mo-0,5%Fe-0,5% Cr alloy at temperature 650 and 750 °C with soaking time 30 minutes, the hardness testing use Vickers micro hardness, the corrosion rate testing use method of discontinue gravimetric, and the microstructure testing use optical microscope. The result of this research indicate that hardness of Zr-0,3%Mo-0,5%Fe-0,5%Cr alloy are decreasing with increasingly of homogenization temperature. Micrograph of Zr-0,3%Mo-0,5%Fe-0,5%Cr alloy ( 650°C, 30 minute) having thin oxide layer on the surface of alloy at time 32 hours (T = 250 C) and 24-32 hours (T = 300 C). Micrograph of Zr-0,3%Mo-0,5%Fe-0,5%Cr alloy (750°C, 30 minute) having thin oxide layer on the surface of alloy at time 28-32 hours (T = 250°C) and 24-32 hours (T = 300°C). Micrograph of Zr-0,3%Mo-0,5%Fe-0,5%Cr alloy (750°C, 30 minute) having thin oxide layer on the surface of alloy at time 28-32 hours (T = 250°C) and 24-32 hours (T = 300°C). The rate corrosion of Zr-0,3%Mo-0,5%Fe-0,5%Cr alloy in saturated steam medium at temperature 250 and 300 ºC follow cubic law. The hardness, microstructure, and rate corrosion influenced by homogenization treatment to previous ingot of Zr-0,3%Mo-0,5%Fe-0,5%Cr alloy. Keyword : homogenization,   hardness,  corrosion  rate,  microstructure,  ingot,  Zr-0,3%Mo- 0,5%Fe-0,5%Cr alloy.