Pemanfaatan limbah padat industri karet remah (crumb rubber) untuk pembuatan kompos Supraptiningsih Supraptiningsih; Nursamsi Sarengat
Majalah Kulit, Karet, dan Plastik Vol 30, No 1 (2014): Majalah Kulit, Karet, dan Plastik
Publisher : Center for Leather, Rubber, and Plastic Ministry of Industry, Indonesia

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (528.046 KB) | DOI: 10.20543/mkkp.v30i1.122

Abstract

The objective of the research was to create a compost formula for plant fertilizer. Composts containing 100, 90, 80, 70, 60, and 50 parts of crumb rubber industry solid waste and 10, 20, 30, 40, and 50 parts of bran were prepared. The mixing was done by adding 20 ml of molasses and 20 ml of EM4. Moisture content was maintained at 40-60%. The compost was mature in 40 days. The resulting compost was compared to SNI 2803:2010 Solid NPK Fertilizer and Regulation of the Minister of Agriculture No. 70/Permentan/SR-140/10/2011 on Organic Fertilizer. The best compost that met the requirements (except kalium) was the compost with 20 parts of bran, 80, 90, and 100 parts of solid waste. The physical properties of the compost were dark brown similar to the color of the soil, insoluble in water, C/N ratio of 20.74 to 25.44, temperature approximately equal to the ambient, and odorless. ABSTRAK Tujuan penelitian adalah membuat formula kompos untuk pupuk tanaman. Variasi dalam pembuatan kompos yaitu jumlah limbah padat industri crumb rubber sebesar 100, 90, 80, 70, 60, dan 50 bagian, serta jumlah bekatul sebesar 10, 20, 30, 40, dan 50 bagian. Pencampuran dilakukan dengan penambahan tetes sebanyak 20 ml dan EM4 sebanyak 20 ml. Air ditambahkan sampai campuran mempunyai kelembaban 40-60%. Kompos matang pada hari ke-40. Hasil pupuk kompos dibandingkan dengan SNI 2803:2010 Pupuk NPK Padat serta Peraturan Menteri Pertanian No:70/Permentan/SR-140/10/2011 tentang Pupuk Organik. Kompos hasil penelitian terbaik dan memenuhi persyaratan (kecuali kalium) adalah kompos dengan formulasi bekatul 20 bagian dan limbah padat crumb rubber 80, 90, dan 100 bagian. Kompos tersebut memiliki sifat fisika antara lain berwarna coklat tua agak hitam mirip dengan warna tanah, tidak larut dalam air, C/N rasio sebesar 20,74-25,44, suhu kurang lebih sama dengan suhu lingkungan, dan tidak berbau.
Pengaruh serbuk serat batang pisang sebagai filler terhadap sifat mekanis dari komposit PVC– CaCO3 Supraptiningsih Supraptiningsih
Majalah Kulit, Karet, dan Plastik Vol 28, No 2 (2012): Majalah Kulit, Karet, dan Plastik
Publisher : Center for Leather, Rubber, and Plastic Ministry of Industry, Indonesia

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (809.238 KB) | DOI: 10.20543/mkkp.v28i2.108

Abstract

ABSTRACTThe aim of research was to study the effect to the mechanical properties of banana fiber as a filler of PVC-calcium carbonate composite. Banana stem powder was made from banana stem which was grounded and soaked in 15 % NaOH for 24 hours to remove the lignin, dried andscreened to 200 mesh, PVC-calcium carbonate composite was made using a Two Roll Mill attemperature of 50oC, for 10 minutes and 50 rpm. The composition of PVC and additives were no varied, while the variations made on banana fiber, ie 0, 10; 20, 30, and 40 phr (per hundred resin). The observation showed the mechanical properties of PVC- calcium carbonate composite has value of weight per unit area between 4.55 to 5.90 kg/m2, bulk densities from 1.503 to 1.999 g/cm3, tensile strength from 67.56 to 79.03 kg/cm2, hardness 55.00 to 66.66 shore D, water absorption from 0.960 to 3.322 %, flexibility test from 118.99 to 165.09 kg/cm2, flash point 0.032 0.075 inc / sec, water density was good (not drop happened) and the ability of sawed and nailed was good (no defected/cracked). When the test results of PVC-calcium carbonate composite with banana fiber compared with SNI 15-0233-1989 Mutu dan Cara Uji Lembaran Serat Semen, indicates that all PVC-calcium carbonate composite with banana fiber as filler fulfilled SNI requirements. ABSTRAKPenelitian bertujuan untuk mempelajari pengaruh penambahan serbuk serat batang pisang sebagai filler terhadap sifat mekanis komposit PVC-CaCO3. Serbuk serat batang pisang dibuat dari pelepah pisang yang dihaluskan, dan direndam dalam NaOH 15% selama 24 jam untuk menghilangkan lignin yang ada. Sesudah itu dikeringkan, dan diayak dengan ayakan 200 mesh. Komposit PVC-CaCO o 3 dibuat dengan alat Two Roll Mill pada suhu 50 C, selama 10 menit dan kecepatan perputaran rol 50 rpm. Komposisi PVC dan bahan aditif dibuat tetap, sedangkan jumlah serbuk serat batang pisang divariasi berturut-turut 10 ; 20 ; 30; dan 40 phr (per hundred resin) dan dibuat kontrol atau tanpa ditambah serbuk serat batang pisang. Sifat mekanis komposit PVC-CaCO 2 3 mempunyai berat persatuan luas antara 4,55 – 5,90 kg/m , bobot isi 1,50 – 1,99 g/cm3, kekuatan tarik 67,56 – 79,03 kg/cm2, kekerasan 55,00 - 66,66 shore D, penyerapan air 0,96 – 3,32 %, kuat lentur 118,99 – 165,09 kg/cm2, titik nyala 0,03 - 0,08 inc/detik, kerapatan air baik (tidak terjadi tetesan) dan kemampuan digergaji dan dipaku baik (tidak cacat/retak). Komposit PVC-CaCO3 dengan filler serbuk serat batang pisang jika dibandingkan dengan SNI 15-0233- 1989 Mutu dan Cara Uji Lembaran Serat Semen, menunjukkan bahwa semua komposit PVCCaCO3 dengan variasi jumlah filler serbuk serat batang pisang memenuhi persyaratan seperti yang ditetapkan oleh SNI tersebut diatas.
Co-Authors Nursamsi Sarengat