Search

 1 
PENGGUNAAN KAOLIN SEBAGAI FILLER BAN PADAT PADA STROLLER BABY ELLE MINI CAPSULE Aprillena Tornadez Bondan; Nasruddin Nasruddin; Rori Andhika
Jurnal Dinamika Penelitian Industri Vol 32, No 1 (2021): JURNAL DINAMIKA PENELITIAN INDUSTRI
Publisher : Balai Riset dan Standardisasi Industri Palembang

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.28959/jdpi.v32i1.6961

Abstract

Penelitian tentang penggunaan kaolin dan zeosil sebagai pengisi ban padat untuk kereta bayi telah dilakukan. Kaolin sebagai pengisi dalam penelitian ini dengan perbandingan 45 phr hingga 65 phr. Rasio zeosil sebagai bahan pengisi penguat untuk memperbaiki sifat mekanik ban padat dan bahan aditif lainnya dikondisikan. Percobaan dilakukan dengan 5 (lima) formula. Parameter yang digunakan untuk melihat sifat mekanik ban padat terdiri dari specific gravity, hardness, abrasion resistance, dan tensile strength. Hardness sebagai parameter utama ban padat dari penelitian ini dibandingkan dengan hasil pengujian ban padat stroller baby elle kapsul mini dari pasaran. Data dari hasil pengujian, untuk formula STS-01 sampai STS-03 sebelum pengusangan nilai hardness 56 sampai 60 shore A. Nilai hardness setelah pengusangan 58-65 Shore A. Hardness sebelum pengusangan dari hasil penelitian ini memenuhi nilai hardness ban padat stroller baby elle mini capsule dari pasar yaitu 50 hingga 62 Shore A. Sebagai parameter pendukun dilakukan pengujian specific gravity sebelum pengusangan 1,335 - 1,360 g/cm3 , Specific gravity setelah pengusangan 1,327 - 1,355 g/cm3 . Abrasion resistance sebelum pengusangan 9,045-13,902 mm3 , Abrasion resistance setelah pengusangan 6,327-17,467 mm3 , dan tensile strength 9,875 hingga 11,07 MPa.
KARAKTERISTIK KOMPON KARET PAVING BLOCK DARI LIMBAH KARET SKIM BERBAHAN PENGISI PASIR KUARSA Aprillena Tornadez Bondan; Rahmaniar Rahmaniar
Jurnal Dinamika Penelitian Industri Vol 29, No 2 (2018): JURNAL DINAMIKA PENELITIAN INDUSTRI
Publisher : Balai Riset dan Standardisasi Industri Palembang

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (996.115 KB) | DOI: 10.28959/jdpi.v29i2.3840

Abstract

The aim of this research was to know the characteristic of paving block rubber which made from skim rubber waste as the main material, the quartz sand as the filler, and also get its formulation. The raw material used in the research was skim rubber waste 100 phr. This research used Completed Randomized Design (CRD) with 2 factorials. The first factor was the size of quartz sand (A) with the variations, respectively: A1= 200 mesh , A2=  400 mesh. The second factor was quartz sand concentration (B), respectively: B1= 50 phr, B2= 60  phr, B3 = 70 phr, B4= 80 phr. Quality testing for the characteristics of a rubber compound  were tensile strength, elongation at break, ozone resistance and volume changing. The quality testing results showed that the value of the physical characteristics of the compound with the best treatment results were the formula 6, which used skim rubber waste 100 phr, quartz sand size 400 mesh with concentration 60 phr. The test result value of tensile strength was 560 N/cm3, elongation at break  was 40%, ozone resistance  was no crack, and volume changing in SAE oil 40 at 70oC for 72 hours was 17,97%.
Co-Authors Nasruddin Nasruddin Rahmaniar Rahmaniar Rori Andhika