Article Per Year (5 Year)
p-Index From 2021 - 2026
0
P-Index
This Author published in this journals
All Journal Berkala Fisika Indonesia : Jurnal Ilmiah Fisika, Pembelajaran dan Aplikasinya
_ Darminto
Program Studi Magíster Fisika, Bidang Keahlian Material, Jurusan Fisika FMIPA, Institut Teknologi Sepuluh Nopember, Kampus ITS Sukolilo, Surabaya 60111
Astronomy Earth & Planetary Sciences Education Environmental Science Materials Science & Nanotechnology Physics

Published : 1 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 1 Documents
Search

 1 
NANOKRISTALISASI SUPERKONDUKTOR (Bi,Pb)2 Sr2 CaCu 2O8+? DENGAN METODE PENCAMPURAN BASAH Lydia Rohmawati; _ Darminto
Berkala Fisika Indonesia : Jurnal Ilmiah Fisika, Pembelajaran dan Aplikasinya Vol 4, No 1 & 2 (2012)
Publisher : Universitas Ahmad Dahlan

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.12928/bfi-jifpa.v4i1 & 2.236

Abstract

Bi2Sr2CaCu2O8+?(Bi-2212) merupakan bahan superkonduktif yang memiliki suhu kritis (Tc) sekitar 80 K. Pada penelitian ini dilakukan sintesis Bi-2212 murni dan Bi-2212 doping Pb dengan menggunakan metode pencampuran basah, untuk memperoleh ukuran kristal ?100 nm. Hasil sintesis dengan metode tersebut dikalsinasi dengan variasi suhu 400°C, 500°C dan 600°C selama satu jam serta 780°C selama 3 jam. Selanjutnya dilakukan sintering pada suhu 825°C dengan variasi waktu 1-5 jam. Hasil analisis dengan XRD menunjukkan bahwa Bi-2212 tanpa doping dengan sintering selama 1-5 jam memiliki ukuran kristal yang mencapai ~ 90 nm dengan fraksi volume 68%, sedangkan Bi-2212 doping Pb dengan sintering selama 1-3 jam menghasilkan ukuran kristalnya ~ 100 nm dengan fraksi volume mencapai 85%.