SYNTHESIS OF POLYURETHANE MICROCAPSULE USING INTERFACIAL POLYMERIZATION AS SELF HEALING COATING MATERIAL Athanasia Amanda Septevani; Evi Triwulandari; Dewi Sondari
Widyariset Vol 15, No 2 (2012): Widyariset
Publisher : Pusbindiklat - LIPI

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (1939.576 KB) | DOI: 10.14203/widyariset.15.2.2012.265–272

Abstract

Polyurethane microcapsule had been made as self healing coating material. Polyurethane microcapsule synthesis had been conducted by interfacial polymerization both spontaneous polymerization and prepolymer polyurethane polymerization using glycerol as renewable palm oil polyol. Based on FTIR-Spectra showed the functional group of polyurethane formed both spontaneous and prepolymer polyurethane polymerization. Polyurethane microcapsule formed was in spherical form. The particle size prepared by spontaneous polimerization was smaller than particle prepared by prepolymer polymerization at range 20,51±12,7 and 139,2±72,3 μm respectively.
SYNTHESIS OF POLYURETHANE MICROCAPSULE USING INTERFACIAL POLYMERIZATION AS SELF HEALING COATING MATERIAL Athanasia Amanda Septevani; Evi Triwulandari; Dewi Sondari
Widyariset Vol 15, No 2 (2012): Widyariset
Publisher : Pusbindiklat - LIPI

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.14203/widyariset.15.2.2012.265–272

Abstract

Polyurethane microcapsule had been made as self healing coating material. Polyurethane microcapsule synthesis had been conducted by interfacial polymerization both spontaneous polymerization and prepolymer polyurethane polymerization using glycerol as renewable palm oil polyol. Based on FTIR-Spectra showed the functional group of polyurethane formed both spontaneous and prepolymer polyurethane polymerization. Polyurethane microcapsule formed was in spherical form. The particle size prepared by spontaneous polimerization was smaller than particle prepared by prepolymer polymerization at range 20,51±12,7 and 139,2±72,3 μm respectively.