IMPREGNASI LOGAM Cu PADA HIDROKSIAPATIT DARI KULIT KERANG DARAH (Anadara granosa) Zultiniar '; Yelmida A. '; Nuruzzaman Shiqhi
Jurnal Sains dan Teknologi Vol 16, No 1 (2017): Jurnal Sains dan Teknologi
Publisher : Fakultas Teknik Universitas Riau

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (275.874 KB) | DOI: 10.31258/jst.v16.n1.p20-23

Abstract

Hidroksiapatit (HAp, Ca10(PO4)6(OH)2) adalah senyawa yang berasal dari kalsium posfat yang termasuk unsur pokok komponen anorganik dari jaringan keras seperti tulang dan gigi. Hidroksiapatit (Hap) adalah material yang digunakan sebagai implan tulang, adsorben, dan katalis. Pada studi (penelitian) ini, Hidroksiapatit yang disangga katalis Cu, disiapkan menggunakan metode impregnasi basah. Katalis Cu-HAp disiapkan dengan memvariasikan jumlah Cu yaitu 3, 6 and 12 % b/b. Larutan dikeringkan dengan pengadukan pada kecepatan 350 rpm pada suhu 30 oC selama 24 jam. Sampel yang kering kemudian dioven pada suhu 105 oC selama 1 jam. Katalis yang telah kering, kemudian dikalsinasi pada suhu 500 oC selama 3 jam. Hasil terbaik yang didapat dari katalis Cu-HAp digunakan sebagai rasio logam Co dan Ni. Hasil impregnasi dianalisis menggunakan spektofotomter FTIR, Surface Area Analyzer (SAA), X-ray diffraction (XRD) dan Scanning Electron Microscopy- Electron Dispersive X-ray (SEM-EDX). Berdasarkan analisis SAA, luas permukaan HAp adalah 17.753 m²/g, sedangkan logam HAp yang paling optimal pada rasio Cu-Hap (3%) mencapai 31.138 m²/g, yang berarti peningkatan luas permukaan mencapai 75%. Analisa dari difraksi X-ray menunjukkan hasil yang tidak signifikan, berbeda dibandingkan dengan katalis H-Ap. Hasil analisa unsur dengan SEM-EDX menunjukkan bahwa proses impregnasi logam pada hidroksiatpatit cukup berhasil. Proses impregnasi dipengaruhi oleh pengadukan, pengeringan, dan proses kalsinasi.
Impregnasi Logam Co, Cu Dan Ni Pada Hidroksiapatit Yang Disintesis Dari Kulit Kerang Lokan (Gelonia Expansa) Nuruzzaman Shiqhi; Yelmida A; Zultiniar Zultiniar
Jurnal Online Mahasiswa (JOM) Bidang Teknik dan Sains Vol 3, No 1 (2016): Wisuda Februari Tahun 2016
Publisher : Jurnal Online Mahasiswa (JOM) Bidang Teknik dan Sains

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

Hydroxyapatite (HAp, Ca10(PO4)6(OH)2) is a compound of calcium phosphate which is the main constituent of the inorganic component of human hard tissue such as bone and teeth. Hydroxyapatite (HAp) is a material used as a bone implant, adsorbents and catalysts. In this study, hydroxyapatite supported Cu catalyst was prepared using wet impregnation method. A series of Cu-HAp catalysts have been prepared by varying the amount of Cu viz., 3, 6 and 12 % w/w. The solutions were dried with stirring 350 rpm at 30 oC for 24 h. The dried samples were kept in oven maintained at 105 oC for a duration of 1 h. Finally, the dried catalyst were calcined at 500 oC for 3 h. The best results of the catalyst Cu-HAp used as the ratio to the metal Co and Ni. Impregnation results were analyzed using FTIR spectrophotometer, Surface Area Analyzer (SAA), X-ray diffraction (XRD) and Scanning Electron Microscopy - Electron Dispersive X-ray (SEM-EDX). Based on the analysis SAA synthesized HAp surface area was 17.753 m²/g, while the metal-HAp most optimal in Cu-HAp (3%) reached 31.138 m²/g, meaning that the increase in surface area reaches 75%. Results of analysis by X-ray diffraction, it shows insignificant different compare to HAp catalyst. Results of elemental analysis by SEM-EDX showed that the metal impregnation process on hydroxyapatite was quite successful. The impregnation process is influenced by stirring, drying and calcination process. Keywords: calcination, catalyst, hydroxyapatite, impregnation, metals (Cu, Co and Ni)