Article Per Year (5 Year)
p-Index From 2020 - 2025
0
P-Index
This Author published in this journals
All Journal Indonesian Mining Journal Indonesian Mining Journal
SYAFEI S. RASJAD
R & D Centre for Mineral and Coal Technology
Chemical Engineering, Chemistry & Bioengineering Chemistry Earth & Planetary Sciences Energy Engineering Environmental Science Materials Science & Nanotechnology

Published : 2 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 2 Documents
Search

 1 
PRETREATMENT OF KAOLIN INTO METAKAOLIN REZKY I. ANUGRAH; SYAFEI S. RASJAD
Indonesian Mining Journal Vol 13, No 3 (2010): INDONESIAN MINING JOURNAL Vol. 13 No. 3 October 2010
Publisher : Puslitbang tekMIRA

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (1899.617 KB) | DOI: 10.30556/imj.Vol13.No3.2010.517

Abstract

Most of metakaolin is used in portland cement industries as an additive to improve the compressive strength of the cement. Using Cicalengka and Bangka kaolin as metakaolin raw material, R & D Center for Mineral and Coal Technology found that Bangka kaolin was more suitable in metakaolin preparation because its initial Al2O3 content (32.80%) rises up to 37.50% after decantation, meanwhile Cicalengka one can not fulfill the requirements. The non-decanted Bangka kaolin (37.50% Al2O3) exceeds the Al2O3 content of metakaolin that has been produced commercially by Asian Ceratec Corporation. Calcination processing follows the decantation one. The decanted Bangka kaolin was then pelletized to have calcining burnt did well. The pellet was burnt in 1 x 0.5 m static laboratory furnace at some tempera- tures and holding times. Burning temperature of 9000 C and 20 minutes holding time showed common calcined kaolin characteristic; sheet-like structure, but at some parts it has developed into unregularly thicker sheet structure due to amorphous (non-reactive phase) formation. This phenomenon signs that recrystallization temperature has been achieved and many hydroxil ions has been lost.
PRETREATMENT OF KAOLIN INTO METAKAOLIN REZKY I. ANUGRAH; SYAFEI S. RASJAD
Indonesian Mining Journal Vol 13 No 3 (2010): INDONESIAN MINING JOURNAL Vol. 13 No. 3 October 2010
Publisher : Balai Besar Pengujian Mineral dan Batubara tekMIRA

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.30556/imj.Vol13.No3.2010.517

Abstract

Most of metakaolin is used in portland cement industries as an additive to improve the compressive strength of the cement. Using Cicalengka and Bangka kaolin as metakaolin raw material, R & D Center for Mineral and Coal Technology found that Bangka kaolin was more suitable in metakaolin preparation because its initial Al2O3 content (32.80%) rises up to 37.50% after decantation, meanwhile Cicalengka one can not fulfill the requirements. The non-decanted Bangka kaolin (37.50% Al2O3) exceeds the Al2O3 content of metakaolin that has been produced commercially by Asian Ceratec Corporation. Calcination processing follows the decantation one. The decanted Bangka kaolin was then pelletized to have calcining burnt did well. The pellet was burnt in 1 x 0.5 m static laboratory furnace at some tempera- tures and holding times. Burning temperature of 9000 C and 20 minutes holding time showed common calcined kaolin characteristic; sheet-like structure, but at some parts it has developed into unregularly thicker sheet structure due to amorphous (non-reactive phase) formation. This phenomenon signs that recrystallization temperature has been achieved and many hydroxil ions has been lost.
Co-Authors REZKY I. ANUGRAH