PENGARUH VARIASI CAMPURAN OKSI-ASETILEN PADA PROSES FLAME HEATING TERHADAP SIFAT FISIS DAN MEKANIK ALUMINIUM SERI 7075 Purnadityanto Purnadityanto; Teguh Triyono; Nurul Muhayat
Mekanika: Majalah Ilmiah Mekanika Vol 18, No 2 (2019): MEKANIKA: Majalah Ilmiah Mekanika
Publisher : Universitas Sebelas Maret

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.20961/mekanika.v18i2.35406

Abstract

The optimum properties of aluminum can be achieved by the addition of alloy and heat treatment. An experimental study was conducted to investigate the effect of the oxy-acetylene mixture on the flame heating process on the physical and mechanical properties of aluminum 7075. Aluminum was heated to 480° C using an oxy-acetylene flame and then cooled rapidly. Then the results were compared with the specimen with flame heating + aging treatment. Variations of oxygen and acetylene mixtures were 0.75, 0.875 and 1 liter/min. The distance of the torch to the specimen's surface is 3 cm and the water flow rate is 1400 cc/min. The aging process is carried out with a temperature of 120°C for 3 hours + 165 for 1 hour. The results showed that the highest hardness value in flame heating treatment was 143,10 HVN with acetylene variation 0,875 liter/minute. The result of the impact test does not change much from the initial material toughness value, due to the average flame heating time that is not too long.
Co-Authors Nurul Muhayat Purnadityanto Purnadityanto