Search

 1 
Pengaruh Waktu Aging pada Pembuatan Nano Particle Geothermal Silica (NPGS) wisnu pambudi; Muh. Wahyu Sya’bani; Warmiati Warmiati; Muhammad Ikhwan
Jurnal Teknologi Vol 10, No 1 (2022): Jurnal Teknologi
Publisher : Universitas Jayabaya

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.31479/jtek.v10i1.199

Abstract

Pembangkit Listrik Tenaga Panas Bumi (PLTP) Dieng menghasilkan lumpur geothermal (silica scaling) yang kandungan terbesarnya adalah silika. Silica scaling tersebut akan menjadi bahan baku natrium silikat. Natrium silikat tersebut selanjutnya digunakan untuk membuat nanosilika. Tujuan penelitian ini adalah untuk mengetahui pengaruh waktu aging terhadap ukuran partikel pada pembuatan nanosilika. Metode yang digunakan untuk mensintesis nanosilika yaitu metode sol-presipitasi. Penelitian diawali dengan membuat larutan natrium silikat primer dan sekunder dan dilanjutkan pengasaman dengan asam sulfat. Kemudian dilakukan tahap aging dengan variasi waktu aging terhadap campuran yang terbentuk. Nanosilika yang dihasilkan pada penelitian ini dikarakterisasi menggunakan FTIR dan TEM. Hasil karakterisasi FTIR nanosilika menunjukkan adanya gugus siloksan (Si-O-Si). Hasil karakterisasi TEM nano partikel dengan waktu aging 1 hari, 3 hari dan 5 hari yaitu 19,31 nm; 19,67 nm dan 19,75 nm berturut-turut.
STUDI KINETIKA CURING DARI RESIN PHENOL-FORMALDEHID DENGAN MODIFIER SODIUM METASILIKAT M. Wahyu Sya'bani; Warmiati Warmiati; Kutut Aji Prayitno
Berkala Penelitian Teknologi Kulit, Sepatu, dan Produk Kulit Vol 15 No 2 (2016): Berkala Penelitian Teknologi Kulit, Sepatu, dan Produk Kulit
Publisher : Politeknik ATK Yogyakarta

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (320.122 KB)

Abstract

This study aims to obtain the curing kinetics of modified PF resin using sodium metasilicate. Three process steps are involved; polimerization of PF resin, thermal analysis and evaluation. In polimerization, phenol and formaldehyde are reacted with sodium hidroxide or sodium metasilicate as catalyst in batch reactor. Dynamic kinetics are done by calculating the heat flow during curing process using Differential Scanning Calorimetry (DSC). The temperature and heatflow data obtained at peak exotherm curve are used for calculating the kinetics. Resin structures are studied using FT-IR and SEM. The calculation result show that the activation energy (Ea) is 105.100 J/mol for PF resin with sodium metasilicate and 118.070 J/mol for PF resin without modifier. Whereas, FTIR analysis shows that there are O-H, aldehyde and C=C aromatics functional groups as the structures of PF Resin. The lower value of activation energy and curing temperature indicates the sodium metasilicate is potential as modifier for PF Resin.
Co-Authors Kutut Aji Prayitno M. Wahyu Sya'bani Muh. Wahyu Syabani Muhammad Ikhwan Wisnu Pambudi