Article Per Year (5 Year)
p-Index From 2020 - 2025
0
P-Index
This Author published in this journals
All Journal Indonesian Journal of Physics (IJP)
Ngurah Ayu Ketut Umiati
1) Laboratorium Fisika Material Elektronik Jurusan Fisika ITB. 2) Jurusan Fisika FMIPA UNDIP, Semarang
Astronomy Computer Science & IT Earth & Planetary Sciences Electrical & Electronics Engineering Energy Engineering

Published : 1 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 1 Documents
Search

 1 
Efek Annealing Pada Penumbuhan Film Tipis Ferroelektrik PbZr0,625Ti0,375O3 (PZT) Ngurah Ayu Ketut Umiati; Irzaman Irzaman; Maman Budiman; M. Barmawi
Indonesian Journal of Physics Vol 12 No 4 (2001): Vol. 12 No.4, Oktober 2001
Publisher : Institut Teknologi Bandung

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (550.968 KB)

Abstract

Ferroelectric materials have many advantages including microactuator (piezoelectric properties), Dynamic Random Access Memory, DRAM (permitivity and polarisability) and infrared sensor (pyroelectric properties). PbZr1-xTixO3 (PZT) is ferroelectric materials, that can be piezoelectric and pyroelectric materials. In this experiment, annealing effect on growing process of thin films PbZr1-xTixO3 (PZT) using dc unbalanced magnetron sputtering is studies. PZT thin films were deposited at temperature 550oC – 650oC on Si (100) substrate with annealing condition and without annealing condition. Ratio of gas flow Ar/O2 was 50 sccm : 10 sccm, basic pressure was 0.051 Torr, and deposition pressure was 1.3 Torr. Annealing temperature was 650oC at pressure 0.58 Torr. The XRD results showed that annealing process caused crystal orientation of thin films more oddered. Some orientations that appear in the results without annealing process disappear after annealing process. This can also be seen in the morphological form of grain size PZT obtained from SEM characterization.
Co-Authors Irzaman, Irzaman M. Barmawi Maman Budiman