Agriculture, Biological Sciences & Forestry Automotive Engineering Chemical Engineering, Chemistry & Bioengineering Computer Science & IT Control & Systems Engineering Education Electrical & Electronics Engineering Industrial & Manufacturing Engineering Materials Science & Nanotechnology Mathematics Mechanical Engineering

Published : 1 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 1 Documents
Search

 1 
Pengaruh Dimensi Saluran Masuk pada Scrap Aluminium Sand Casting Pulley terhadap Kekerasan, Ketangguhan dan Struktur Mikro Sumpena; Hb. Sukarjo
Politeknosains Vol 15 No 2 (2016): Jurnal Politeknosains Volume 15 Nomor 2 - September 2016
Publisher : Lembaga Penelitian dan Pengabdian kepada Masyarakat (LPPM) Politeknik Pratama Mulia Surakarta

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (789.148 KB)

Abstract

The purpose of this study for determine influence size of the inlet to the hardness, toughness and microstructure pulley with casting mold sand raw materials aluminum scrap. The smelting process using crucible furnace. Sand molds be made 3 kinds of different inlets, each inlet same was made 4 sand molds. Hardness testing is done by using the Vickers hardness test. the load to pressure 100 gf, the time to pressure 5 seconds. Toughness testing with use standard ASTM D256-03 machine test impact charpoy. Observation of microstructure was observed on each specimen by using an optical microscope. The hardness test results show that hardness value of the highest on the dimensions of the inlet height 6 mm is 64.4 VHN while the lowest value to the dimensions of the inlet height 5 mm is 60.96 VHN. The toughness test results show that toughness value from the three specimens almost the same is 0.057 joules / mm2; 0.0565 joule / mm2 and 0.0565 joules / mm2. While the structure micro of castings with high dimensional inlet 5 mm and 7 mm occurred structure micro which is almost the same, while the dimensions of the inlet height 6 mm has a spread of Fe, Si and Mg is more evenly distributed.