Agriculture, Biological Sciences & Forestry Automotive Engineering Chemical Engineering, Chemistry & Bioengineering Computer Science & IT Control & Systems Engineering Education Electrical & Electronics Engineering Industrial & Manufacturing Engineering Materials Science & Nanotechnology Mathematics Mechanical Engineering

Published : 1 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 1 Documents
Search

 1 
Pengaruh Siklus Panas pada Komposit Limbah Plastik HDPE-Serat Cantula sebagai Bahan Material Alternatif Melalui Uji Mekanik Sunaryo; Burhan Ibnu Mubtadi
Politeknosains Vol 15 No 2 (2016): Jurnal Politeknosains Volume 15 Nomor 2 - September 2016
Publisher : Lembaga Penelitian dan Pengabdian kepada Masyarakat (LPPM) Politeknik Pratama Mulia Surakarta

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (633.912 KB)

Abstract

This research is to determine the effect of thermal cycling on mechanical properties of such composites. Mechanical properties test in the tensile strength, bending strength and impact strength. Composite materials using HDPE powder as a cosmetic bottle waste cantula matrix and fibers as reinforcement, fiber volume fraction is 40% composed of random. Specimens were made using a hot molding machine. Temperature thermal cycle with a variation of 60 ° C, 70 ° C, 80 ° C, 90 ° C and 100 ° C. Variations in the number of cycles performed 100 times. Testing of mechanical properties of the composite tensile strength using ASTM standard 3039, bending strength ASTM D 6272 standard, and impact strength testing with ASTM D 5941. Results of testing the mechanical properties of composites obtained the data that the composite thermal cycle with a temperature of 60 ° C were carried out as many as 100 times. The tensile strength of 26 MPa, bending strength of 29 MPa and impact strength 45 kJ / m². Composites with a thermal treatment at temperatures above 70 ° C resulted in the degradation of the material so that the mechanical strength decreases.