Studi Pengaruh Ketebalan Elektroda Karbon Aktif dari Kulit Buah Kakao terhadap Kinerja Elektrokimia Superkapasitor Irsya Dunnas; Widi Mulia Nasution; Mulda Muldarisnur; Yuli Yetri
Jurnal Fisika Unand Vol 13 No 4 (2024)
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.25077/jfu.13.4.594-601.2024

Abstract

Sintesis karbon aktif dari kulit kakao dengan variasi ketebalan elektroda 0,4; 0,5; dan 0,6 mm bertujuan untuk melihat pengaruhnya terhadap kinerja superkapasitor. Tebal elektroda yang berbeda diberi kode sampel yaitu tebal 0,4 mm dengan kode CC-0,4; tebal 0,5 dengan kode CC-0,5 mm dan tebal 0,6 mm dengan kode CC-0,6. Pembuatan elektroda karbon dari kulit kakao dilakukan dalam beberapa tahap yaitu pengeringan organik, prakarbonasi, aktivasi kimia menggunakan aktivator KOH 0,4 M dan pencetakan pelet menggunakan press hidrolik dengan tekanan 8 ton. Pelet yang telah dicetak dikarbonasi menggunakan gas N2 pada suhu 600 ⁰C dan aktivasi fisika menggunakan gas CO2 pada suhu 700 °C. Sifat elektrokimia dari sel superkapasitor ditinjau melalui sistem dua elektroda dalam elektrolit 1 M KOH. elektroda karbon aktif optimum yang diperoleh pada sampel CC-0,5 dengan kapasitansi spesifik yang tinggi  mencapai 366,67 F/g pada rapat arus 1,0 A/g. Rapat energi maksimum yang didapatkan sebesar 660 Wh/Kg pada rapat daya optimum 2378,39 W/Kg. Potensi kulit kakao sebagai sumber karbon aktif dengan ketebalan 0,5 mm menunjukan kinerja perangkat penyimpanan energi elektrokimia superkapasitor yang tinggi dan stabil dengan ketahanan bahan yang baik.
Analisis Pengaruh Variasi Elektrolit H2SO4, KOH, dan Na2SO4 terhadap Kinerja Elektrokimia Superkapasitor berbasis Biomassa Kulit Kakao Exaudi Pratama Rajagukguk; Widi Mulia Nasution; Mulda Muldarisnur; Yuli Yetri
Jurnal Fisika Unand Vol 13 No 5 (2024)
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.25077/jfu.13.5.610-616.2024

Abstract

Utilization of cocoa pod waste (Theobroma cacao) as a supercapacitor carbon electrode through electrolyte optimisation was successfully conducted with 0.5M KOH chemical activator. Carbon production starts with slicing cocoa pods, sun drying, pre-carbonisation, crushing of carbon particles with mortar and ball milling, and particle size uniformity using a sieve. The obtained particle powder was chemically activated with 0.5M KOH, coin-molded into of carbon monolith and finished with integrated pyrolysis. Samples were subjected to one-stage integrated pyrolysis by carbonisation from room temperature to 600˚ C in an N2 gas environment, followed by physical activation to 700˚ C in a CO2 gas environment. Testing the electrochemical properties of carbon electrodes based on different types of electrolytes (H2SO4, KOH, and Na2SO4) IM using cyclic voltammetry (CV) and galvanostatic charge discharge (GCD) methods. The sample provided with H2SO4 electrolyte was confirmed to have the highest specific capacitance of 412.94 F/g at a current of 1 A/g. Based on the results of this study, it is confirmed that cocoa pods have the potential to be a source of electrode base material with H2SO4 electrolyte solution as a source of charge carrier in supercapacitor cell devices.