Article Per Year (5 Year)
p-Index From 2020 - 2025
0.702
P-Index
This Author published in this journals
All Journal Journal Mechanical Engineering
Pattikayhattu, Erwin B.
Unknown Affiliation
Industrial & Manufacturing Engineering Mechanical Engineering

Published : 4 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 4 Documents
Search

 1 
ANALISIS PERUBAHAN KETEBALAN PIPA AKIBAT PENGARUH KOROSI DAN SISA UMUR PAKAI PIPA DI PLTD NAMLEA KABUPATEN BURU Pratama, Ahmad Zulfikri; Pattikayhattu, Erwin B.; Effendy, Edison
Journal Mechanical Engineering Vol. 2 No. 1 (2024): April
Publisher : Jurusan Teknik Mesin

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

In modern industry, pipelines play an important role, especially in the oil and gas sector. Pipes are susceptible to corrosion, especially those in aggressive environments such as PLTD Namlea, which is directly adjacent to the coast. Corrosion, as a natural process of metal degradation, is inevitable, but it can be controlled to extend the life of the pipe. This study measured the thickness of the pipes at PLTD Namlea using Ultrasonic Testing (UT) to determine the corrosion rate and remaining service life. Based on measurements, the minimum thickness of pipes at various measuring points (Measuring Points / MP) still meets the API 574 standard, which must not be less than 1.8 mm. The average corrosion rate ranges from 0.336 to 0.358 mm/year. These values affect the rate of degradation of the pipe and the remaining service life, which ranges from 5.5 to 6.1 years at various measurement points. Pipes that have a higher corrosion rate will have a shorter remaining service life. Overall, the pipeline at PLTD Namlea is still laid. Keywords: Pipe, Corrosion Rate, Remaining Life
ANALISIS CORROSION RATE TERHADAP REMAINING LIFE STORAGE TANK T03-300 KL DI PLTD POKA DENGAN MENGGUNAKAN METODE RISK BASED INSPECTION (RBI) Fazrian, Rian; Pattikayhattu, Erwin B.; Patty, Alexander A.
Journal Mechanical Engineering Vol. 2 No. 3 (2024): Desember
Publisher : Jurusan Teknik Mesin

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.31959/jme.v2i3.2897

Abstract

AbstractThis study is entitled "Corrosion Rate Analysis of Remaining Life Storage Tank T03-300 KL at PLTD Poka Using the Risk Based Inspection (RBI) Method". The purpose of this study is to evaluate the corrosion rate and residual life of the T03-300 KL storage tank used at PLTD Poka, as well as to provide recommendations related to appropriate inspection strategies based on risk analysis. The method used in this study is Risk Based Inspection (RBI), which allows the determination of the probability of failure (PoF) and the consequences of failure (CoF) of the storage tank. The data collected includes primary data through observation, measurement, and direct inspection of tanks, as well as secondary data from relevant literature.Keyword : Corrosion Rate, Remaining Life, Storage Tank Risk Based Inspection (RBI), Probability of Failure (PoF), Consequence of Failure (CoF)
ANALISIS PERUBAHAN KETEBALAN PIPA AKIBAT PENGARUH KOROSI DAN SISA UMUR PAKAI PIPA DI PLTD NAMLEA KABUPATEN BURU Pratama, Ahmad Zulfikri; Pattikayhattu, Erwin B.; Effendy, Edison
Journal Mechanical Engineering Vol. 2 No. 1 (2024): April
Publisher : Jurusan Teknik Mesin

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

In modern industry, pipelines play an important role, especially in the oil and gas sector. Pipes are susceptible to corrosion, especially those in aggressive environments such as PLTD Namlea, which is directly adjacent to the coast. Corrosion, as a natural process of metal degradation, is inevitable, but it can be controlled to extend the life of the pipe. This study measured the thickness of the pipes at PLTD Namlea using Ultrasonic Testing (UT) to determine the corrosion rate and remaining service life. Based on measurements, the minimum thickness of pipes at various measuring points (Measuring Points / MP) still meets the API 574 standard, which must not be less than 1.8 mm. The average corrosion rate ranges from 0.336 to 0.358 mm/year. These values affect the rate of degradation of the pipe and the remaining service life, which ranges from 5.5 to 6.1 years at various measurement points. Pipes that have a higher corrosion rate will have a shorter remaining service life. Overall, the pipeline at PLTD Namlea is still laid. Keywords: Pipe, Corrosion Rate, Remaining Life
ANALISIS CORROSION RATE TERHADAP REMAINING LIFE STORAGE TANK T03-300 KL DI PLTD POKA DENGAN MENGGUNAKAN METODE RISK BASED INSPECTION (RBI) Fazrian, Rian; Pattikayhattu, Erwin B.; Patty, Alexander A.
Journal Mechanical Engineering Vol. 2 No. 3 (2024): Desember
Publisher : Jurusan Teknik Mesin

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.31959/jme.v2i3.2897

Abstract

AbstractThis study is entitled "Corrosion Rate Analysis of Remaining Life Storage Tank T03-300 KL at PLTD Poka Using the Risk Based Inspection (RBI) Method". The purpose of this study is to evaluate the corrosion rate and residual life of the T03-300 KL storage tank used at PLTD Poka, as well as to provide recommendations related to appropriate inspection strategies based on risk analysis. The method used in this study is Risk Based Inspection (RBI), which allows the determination of the probability of failure (PoF) and the consequences of failure (CoF) of the storage tank. The data collected includes primary data through observation, measurement, and direct inspection of tanks, as well as secondary data from relevant literature.Keyword : Corrosion Rate, Remaining Life, Storage Tank Risk Based Inspection (RBI), Probability of Failure (PoF), Consequence of Failure (CoF)