<![CDATA[Friction Stir Welding (FSW) is a solid welding process with a tool that rotates and softens the workpiece due to the heat of the friction tool and mechanically moves the metal to form a welded joint. This study aimed to determine the mechanical properties and microstructure of FSW process with variation of tool rotation 1555 rpm, 1175 rpm and 910 rpm using frais machine. The FSW process of aluminum 2024 used fixed tool parameters with threaded cylinder shape, 29 mm/min welding speed, tilt angle 0o and dwell time 3 min indicated no defect with largest tensile strength 269 MPa and highest hardness 125 HVN in weld area using tool rotation 1175 rpm. The FSW process of aluminum 2024 showed that the use of 1175 rpm rotational speed resulted in higher mechanical properties and finer microstructure compared to the rotational speed of 1500 rpm and 910 rpm.Friction Stir Welding (FSW) merupakan proses pengelasan kondisi padat dengan sebuah tool yang berputar dan melunakkan benda kerja akibat panas dari gesekan tool dan secara mekanis menggerakkan logam untuk membentuk sambungan las. Penelitian ini bertujuan untuk mengetahui sifat mekanik dan struktur mikro hasil proses FSW dengan variasi putaran tool 1555 rpm, 1175 rpm dan 910 rpm menggunakan mesin frais. Proses FSW aluminium 2024 menggunakan parameter tool tetap dengan bentuk silinder ulir, kecepatan pengelasan 29 mm/min, sudut kemiringan tool 0o dan dwell time 3 menit menunjukkan tidak adanya cacat dengan kuat tarik terbesar 269 MPa dan kekerasan tertinggi 125 HVN pada daerah lasan menggunakan kecepatan putar 1175 rpm. Proses FSW aluminium 2024 menunjukkan bahwa penggunaan kecepatan putar 1175 rpm menghasilkan sifat mekanik yang lebih tinggi dan struktur mikro yang lebih halus dibandingkan dengan kecepatan putar 1500 rpm dan 910 rpm.]]>
Copyrights © 2017