Pengaruh Variasi Waktu Hidrotermal terhadap Sintesis dan Karakterisasi Nanokristal Zeolit A dari Abu Sekam Padi

Pungki Hanipa (Chemistry Department, Faculty of Sciences and Mathematics, Diponegoro University, Jl. Prof. Soedarto, SH., Tembalang, Semarang|Diponegoro University|Indonesia)
Pardoyo Pardoyo (Chemistry Department, Faculty of Sciences and Mathematics, Diponegoro University, Jl. Prof. Soedarto, SH., Tembalang, Semarang|Diponegoro University|Indonesia)
Taslimah Taslimah (Chemistry Department, Faculty of Sciences and Mathematics, Diponegoro University, Jl. Prof. Soedarto, SH., Tembalang, Semarang|Diponegoro University|Indonesia)
Arnelli Arnelli (Chemistry Department, Faculty of Sciences and Mathematics, Diponegoro University, Jl. Prof. Soedarto, SH., Tembalang, Semarang|Diponegoro University|Indonesia)
Yayuk Astuti (Chemistry Department, Faculty of Sciences and Mathematics, Diponegoro University, Jl. Prof. Soedarto, SH., Tembalang, Semarang|Diponegoro University|Indonesia)

JURNAL KIMIA SAINS DAN APLIKASI
Vol 20, No 2 (2017): Volume 20 Issue 2 Year 2017

Sekam padi merupakan salah satu produk samping dari penggilingan padi. Silika amorf hasil ektraksi dari sekam padi dapat di manfaatkan untuk pembuatan zeolit. Penelitian ini bertujuan untuk memperoleh nanokristal zeolit A dari abu sekam padi dan menentukan karakter dari produk nanokristal zeolit A hasil sintesis. Hasil dari penelitian ini adalah diperoleh zeolit berupa serbuk putih menggunakan metode hidrotermal dengan variasi waktu hidrotermal selama 1, 2, dan 3 hari. Analisis menggunakan XRD menunjukkan bahwa ketiga zeolit hasil sintesis merupakan zeolit A dengan ukuran bulir kristal semakin menurun dengan bertambahnya waktu hidrotermal di mana masing- masing ukurannya adalah 34,321; 34,21; dan 34,144nm dan puncak utama berada pada 2theta 21°, 23°, 27°, 29° dan 34°. Analisis morfologi permukaan zeolit sintesis menunjukkan ketiga zeolit sintesis memiliki morfologi permukaan berupa kubus.