Pengaruh Lingkungan Terhadap Efisiensi Inhibisi Asam Askorbat (Vitamin C) pada Laju Korosi Tembaga

Soejono Tjitro (Faculty of Industrial Technology, Petra Christian University)
Juliana Anggono (Faculty of Industrial Technology, Petra Christian University)

Jurnal Teknik Mesin
Vol. 1 No. 2 (1999): OCTOBER 1999

Corrosion rate can be reduced by adding inhibitor and inhibition efficiency is a measure if its ability to suppress corrosion. The result of the immersion tests show that the inhibition efficiencies are different on each environment. Addition of 50 ppm of ascorbic acid results in the highest efficiency for NaC1 and CaCO3 environment while for Ca SO4 environment needs 100 ppm. Abstract in Bahasa Indonesia : Pemberian inhibitor dapat mengurangi laju korosi dan kemampuannya untuk menginhibisi diukur dari efisiensinya. Hasil penelitian menunjukkan bahwa efisiensi inhibisi berbeda-beda pada lingkungan yang berbeda. Penambahan inhibitor yang paling efisien untuk lingkungan NaCl dan CaCO3 dalah 50 ppm asam askorbat sedangkan untuk lingkungan CaSO4 adalah 100 ppm asam askorbat. Kata kunci : laju korosi, efisiensi inhibisi, asam askorbat.