<![CDATA[Candlenut shells have high lignin content (54.46%) so that they have potential to be used as fuel. In this study, adhesive used was resin which was used to increase the calorific value and accelerate the ignition process. This study aims to analyze the effect of variations in the addition of resin on the quality and rate of combustion based on the Indonesian National Standard (SNI). This study used a completely randomized design (CRD) method and in this study there was only one factor (Factor A = candlenut shell charcoal and adhesive), 5 treatments with 3 replications. The results of the research of candlenut shell charcoal briquettes using resin adhesives produced an average value of water content testing 4.4626 - 6.0681%, volatile matter testing 39.0411 - 49.8596%, ash content testing 6.4745 - 12.0787% , bonded carbon test 32.3519 - 39.8396 %, density test 1.0718 - 1.2233 g/cm3, calorific value test 5141.52 - 6523.13 cal/g and combustion rate test 0.4469 - 0.6633 g/minute. Water content, density and calorific value tests have met the Indonesian standard, while volatile matter and bound carbon content tests have not met Indonesian standards. Ash content only A5 treatment that mets Indonesian standards and there is no Indonesian standard for testing the combustion rate. Best quality of candlenut shell charcoal briquettes was in treatment A5 and best combustion rate was in A1 treatment. Results of this study indicate that the percentage of resin adhesive can affect the characteristics and rate of burning of candlenut shell charcoal briquettesCangkang kemiri memiliki lignin yang tinggi (54,46%) sehingga potensial untuk dimanfaatkan sebagai bahan bakar. Pada penelitian ini perekat yang digunakan adalah getah damar yang berfungsi untuk meningkatkan nilai kalor dan mempercepat proses penyalaannya. Penelitian yang dilakukan memiliki tujuan menganalisis pengaruh penambahan getah damar terhadap kualitas dan laju pembakaran berdasarkan standar nasional Indonesia (SNI). Penelitian memakai metode rancangan acak lengkap (RAL) dan penelitian ini hanya ada satu faktor (Faktor A= serbuk arang cangkang kemiri dan perekat damar) sebanyak 5 perlakuan dengan 3 kali ulangan. Hasil penelitian dari briket arang cangkang kemiri menggunakan perekat damar menghasilkan nilai rata-rata pengujian kadar air 4,4626 - 6,0681%, pengujian kadar zat terbang 39,0411 - 49,8596%, pengujian kadar abu 6,4745 - 12,0787%, pengujian karbon terikat 32,3519 - 39,8396%, pengujian kerapatan 1,0718 - 1,2233 g/cm3, pengujian nilai kalor 5141,52 - 6523,13 kal/g dan pengujian laju pembakaran 0,4469 - 0,6633 g/menit. Pengujian dari kerapatan, kadar air dan nilai kalor telah sesuai dengan standar negara indonesia (SNI 01-6235-2000) sedangkan untuk pengujian kadar zat terbang dan karbon terikat tidak memenuhi standar. Pengujian kadar abu hanya perlakuan A5 yang memenuhi standar indonesia dan pengujian laju pembakaran belum ada standar indonesia. Kualitas briket arang cangkang kemiri yang terbaik pada perlakuan A5 (65% serbuk arang cangkang kemiri + 35% perekat damar) dan laju pembakaran yang terbaik pada perlakuan A1 (85% serbuk arang cangkang kemiri + 15% perekat damar). Hasil penelitian ini menunjukkan bahwa persentasi perekat damar dapat mempengaruhi karakteristik dan laju pembakaran briket arang cangkang kemiri.]]>
Copyrights © 2023
