Preparation of Layered Double Hydroxide-Polyoxometalate Based Composite

Yulizah Hanifah (Graduate School, Faculty of Mathematics and Natural Sciences, Sriwijaya University, Palembang, 30139, Indonesia)
Amri Amri (Research Center of Inorganic Materials and Coordination Complexes, Faculty of Mathematics and Natural Sciences, Sriwijaya University, Palembang, 30139, Indonesia)

Indonesian Journal of Material Research
Vol. 1 No. 2 (2023): July

Material NiAl-K3[α-PW12O40], NiAl-K4[α-SiW12O40], ZnAl-K4[α-SiW12O40] and ZnAl-K3[α-PW12O40] were created. FTIR, XRD and SEM were used to characterize the substance. The findings of the successfully completed synthesis showed that peak diffraction angle for NiAl-LDH were at 11.58°, 23.18°, 35.01°, 39.41°, 46.70°, 60.94°, and 62.26° and diffraction at 10.29°, 20.07°, 34.02°, and 60.16° for ZnAl-LDH. The composite material LDH-polyoxometalate NiAl-PW12O40 that was at angles 10.76°, 26.59°, 30.8° and 63.1° and 8.61°, 25.27°, 33.8°, 66.34° for ZnAl-plyoxometalate. The typical polyoxometalate band on the composite material’s FTIR spectrum proved tha intecalation of the substance. SEM examination revealed the aggregat for nearly all intercalated and synthesized materials.