cover
Article Per Year (5 Year)
All
Home Page
OAI Link
Editorial Team
Contact
Reviewer
Google Scholar
Contact Name
-
Contact Email
-
Phone
-
Journal Mail Official
-
Editorial Address
-
Location
Kota semarang,
Jawa tengah
INDONESIA
Jurnal Pendidikan Fisika Indonesia
Published by Universitas Negeri Semarang
ISSN : -     EISSN : -     DOI : -
Core Subject : Science, Education,
Education Physics
Arjuna Subject : -
Articles 13 Documents
 1   2 
Search results for , issue " Vol 8, No 2 (2012)" : 13 Documents clear
PENGARUH PERGESERAN PUNCAK DIFRAKSI AKIBAT PERUBAHAN RASIO MOL BA2+/FE3+ TERHADAP SIFAT MAGNETIK BAFE12O19 SOL GEL Suastiyanti, D.; Soegijono, B.
Jurnal Pendidikan Fisika Indonesia Vol 8, No 2 (2012)
Publisher : Jurusan Fisika, Fakultas Matematika dan Ilmu Pengetahuan Alam, Universitas Negeri Semarang

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

Barium hexaferrite BaFe12O19 (BHF) merupakan magnet permanen yang sangat penting khususnya untuk magnetic recording pada peralatan microwave. Serbuk nanokristalin BHF pada penelitian ini disintesa de-ngan metode sol gel auto combustion. Rasio mol Ba2+/Fe3+ dibuat bervariasi  1:12; 1:11,5 dan 1:11.Proses pemanasan dilakukan pada 850oC 10 jam untuk memperoleh BHF nanokristalin. Data XRD memperlihatkan  bahwa BHF dengan rasio 1:12 mempunyai parameter kristal yang sama dengan rasio 1:11, posisi puncak pola difraksi yang saling mendekati khususnya pada 2 θ yang makin besar. Hal ini berkaitan dengan sifat magnetik kedua rasio tersebut yang mempunyai nilai remanen dan koersivitas yang ekstrim. BHF dengan rasio 1:11,5 dengan posisi puncak yang jauh dengan rasio 1:12 dan 1:11 mempunyai nilai remanen dan koersivitas terletak antara nilai remanen dan koersivitas sampel dengan rasio 1:12 dan 1:11. Sampel ini merupakan sampel dengan rasio yang terbaik karena merupakan fasa tunggal yang mempunyai pola difraksi yang hampir tepat sama dengan pola difraksi BHF standar dengan nilai kesesuaian (best FoM) yang paling tinggi 90%, mempunyai butir yang paling halus 22 nm dan sifat magnetik yang lebih baik.Barium hexaferrite BaFe12O19 (BHF) is an important permanent magnet used particularly for magnetic recording applied in microwave devices. Nanocrystalline BHF powder was prepared by sol gel auto combustion method. Hence the mole ratios of Ba2+/Fe3+ were varied at 1:12; 1:11.5 and 1:11. Heating at 850oC for 10 hours for each sample was than done to get final formation of nanocrystalline BHF. The data from XRD confirmed that BHF of ratio 1:12 has same crystall parameters as of ratio 1:11. In addition, position of  diffraction pattern peak of sample of ratio 1:12and 1:11 was almost getting nearerespecially at a greater value of 2 θ. This result has relation with their magnetic properties having an extrim value of remanent and coersive. BHF of ratio 1:11.5 which the peak position is far from ratio 1:12 and 1:11 has value of remanent and coersive between of ratio 1:12 and 1:11. This sample is the samplehaving best ratio sinceit hasa single phase with diffraction pattern  fits with those of BHF standard with the highest value of best FoM of 90%,the finest grain of 22 nm and better magnetic properties
PENINGKATAN KUALITAS FILM TIPIS CdTe SEBAGAI ABSORBER SEL SURYA DENGAN MENGGUNAKAN DOPING TEMBAGA (Cu) Marwoto, P.; Darmaputra, N.M.; -, Sugianto; Othaman, Z.; Wibowo, E.; Astuti, S.Y.
Jurnal Pendidikan Fisika Indonesia Vol 8, No 2 (2012)
Publisher : Jurusan Fisika, Fakultas Matematika dan Ilmu Pengetahuan Alam, Universitas Negeri Semarang

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

Film tipis CdTe dengan doping tembaga (Cu) berkonsenterasi 2% telah berhasil ditumbuhkan di atas substrat Indium Tin Oxide (ITO) dengan metode dc magnetron sputtering. Penelitian ini dilakukan untuk mengetahui pengaruh doping Cu(2%) terhadap struktur morfologi, struktur kristal, fotoluminisensi dan resistivitas listrik film CdTe. Citra morfologi Scanning Electron Microscopy (SEM) dan hasil analisis struktur dengan X-Ray Diffraction (XRD) menunjukkan bahwa film CdTe:Cu(2%) mempunyai citra permukaan dan struktur kristal yang lebih sempurna dibandingkan film CdTe tanpa doping. Hasil analisis spektrometer fotoluminisensi menunjukkan bahwa film CdTe dan CdTe(2%) mempunyai puncak fotoluminisensi pada tiga panjang gelombang yang identik yaitu 685 nm (1,81 eV), 725 nm (1,71 eV) dan 740 nm (1,67 eV). Film CdTe dengan doping Cu(2%) memiliki intensitas puncak fotoluminisensi yang lebih tajam pada pita energi 1,81 eV dibandingkan dengan film CdTe tanpa doping. Pengukuran arus dan tegangan (I-V) menunjukkan bahwa pemberian doping Cu(2%) dapat menurunkan resistivitas film dari 8,40x109 Ωcm menjadi 6,92x105 Ωcm. Sebagai absorber sel surya, kualitas film tipis CdTe telah berhasil ditingkatkan dengan pemberian doping Cu(2%).CdTe:Cu(2%) thin film has been successfully grown on Indium Tin Oxide (ITO) substrates by using dc magnetron sputtering. This study was carried out in order to investigate the effect of Cu(2%) doping on the morphologycal structure, crystal structure, photoluminesence, and resistivity of CdTe thin film. Scanning Electron Microscopy (SEM)  images and X-Ray Diffraction (XRD) results showed that CdTe:Cu(2%) thin film has morphologycal and crystal structures more perfect than undoped CdTe film. Photoluminesence spectroscopy results showed that CdTe and CdTe:Cu(2%) thin films have luminesence peak at three identical wevelength regions i.e. 685 nm (1.81 eV), 725 nm (1.71 eV) and 740 nm (1.67 eV) however CdTe:Cu(2%) film shows sharper photoluminescence peak at band energy of 1.81 eV. Current-Voltage (I-V) measurement showed that the presenting of Cu doping on CdTe film configuration could decrease its electrical resistivity from 8.40x109 Ωcm to 6.92x105 Ωcm. Indeed, as absorber layer of solar cell, the performance of CdTe thin film has been succsesfully improved by using Cu(2%) as doping.
PENGARUH PENAMBAHAN NiO TERHADAP KARAKTERISTIK KERAMIK FILM TEBAL Fe2O3 UNTUK SENSOR GAS ASETON Suhendi, E.; Hasanah, L.; Gustaman, D.S.
Jurnal Pendidikan Fisika Indonesia Vol 8, No 2 (2012)
Publisher : Jurusan Fisika, Fakultas Matematika dan Ilmu Pengetahuan Alam, Universitas Negeri Semarang

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

Pembuatan keramik film tebal Fe2O3-NiO telah dilakukan dengan menggunakan Fe2O3 lokal sebagai bahan dasar untuk sensor gas aseton.  Serbuk Fe2O3 dicampur dengan serbuk NiO dengan konsentrasi 0, 10 dan 50% mol secara homogen. Serbuk campuran kemudian dicampur dengan organic vehicle (OV) terbuat dari campuran terpineol dan etil selulose dengan komposisi 75% berat serbuk campuran dan 25% berat OV dan diaduk membentuk pasta. Pasta dilapiskan di atas substrat alumina dengan metode screen printing lalu dibakar pada suhu 900oC selama 90 menit hingga membentuk keramik film tebal. Film tebal dianalisis dengan difraksi sinar-x (XRD) dan mikroskop elektron (SEM). Resistansi listrik keramik film tebal diukur pada berbagai suhu di ruangan berisi udara dan berisi gas aseton. Karakterisasi XRD menunjukkan bahwa struktur kristal yang terbentuk adalah Fe2O3 hematit dan NiFe2O4 kubik spinel sebagai fase kedua untuk penambahan konsentrasi NiO 10% dan 50%. Penambahan NiO diketahui memperkecil ukuran butir film tebal Fe2O3 dan meningkatkan resistansi listriknya. Keramik film tebal yang dibuat sensitif terhadap gas aseton.Fabrication of thick film Fe2O3-NiO ceramics for acetone gas sensor has been carried out using local Fe2O3as raw material.  The Fe2O3 powder was mixed with NiO powder homogeneously with NiO concentration of 0, 10 and 50 mole %. The mixed powder was then mixed with organic vehicle (OV) made of alpha terpineol and ethyl cellulose with composition of 75 weight % mixed powder and 25 weight % OV forming a paste. The paste was coated on alumina substrates by screen printing method, then fired at 900oC for 90 minutes to produce thick film ceramics. The thick film was analyzed using x-ray diffraction (XRD) and scanning electron microscope (SEM). Resistance of the thick films was measured at different temperatures in chamber containing air and containing acetone gas. XRD characterization showed that the crystal structures are hematite Fe2O3 and NiFe2O4 cubic spinel as second phase for the addition of 10% and 50% NiO concentration. It was known that the addition of NiO decreases grain size of the thick film of Fe2O3 and increases its electrical resistance. The produced thick films were sensitive to acetone gas.

Page 2 of 2 | Total Record : 13

 1   2 

Filter by Year

2012 2012


Reset
Filter By Issues
All Issue Vol 20, No 1 (2024) Vol 19, No 2 (2023) Vol 19, No 1 (2023) Vol 18, No 2 (2022) Vol 18, No 1 (2022) Vol 17, No 2 (2021) Vol 17, No 1 (2021) Vol 16, No 2 (2020) Vol 16, No 1 (2020) Vol 15, No 2 (2019) Vol 15, No 1 (2019) Vol 14, No 2 (2018) Vol 14, No 1 (2018) Vol 13, No 1 (2017): January 2017 Vol 13, No 2 (2017) Vol 13, No 1 (2017) Vol 12, No 2 (2016): July 2016 Vol 12, No 1 (2016): January 2016 Vol 12, No 2 (2016) Vol 12, No 1 (2016) Vol 11, No 2 (2015): July 2015 Vol 11, No 1 (2015): January 2015 Vol 11, No 2 (2015) Vol 11, No 1 (2015) Vol 10, No 2 (2014): July 2014 Vol 10, No 1 (2014): January 2014 Vol 10, No 2 (2014) Vol 10, No 1 (2014) Vol 9, No 1 (2013) Vol 8, No 2 (2012) Vol 8, No 1 (2012) Vol 7, No 2 (2011) Vol 7, No 1 (2011) Vol 6, No 1 (2010): January 2010 Vol 6, No 2 (2010) Vol 6, No 1 (2010) Vol 6, No 1 (2010) Vol 5, No 2 (2009) Vol 5, No 1 (2009) Vol 4, No 2 (2006) More Issue