Article Per Year (5 Year)
p-Index From 2021 - 2026
0.61
P-Index
This Author published in this journals
All Journal Jurnal Bahan Alam Terbarukan Creative Research Journal Jurnal Teknologi Terapan JTRM (Jurnal Teknologi dan Rekayasa Manufaktur) INJECTION: Indonesian Journal of Vocational Mechanical Engineering
Purwadi, Wiwik
Politeknik Manufaktur Negeri Bandung
Agriculture, Biological Sciences & Forestry Chemical Engineering, Chemistry & Bioengineering Civil Engineering, Building, Construction & Architecture Computer Science & IT Control & Systems Engineering Decision Sciences, Operations Research & Management Economics, Econometrics & Finance Electrical & Electronics Engineering Energy Engineering Industrial & Manufacturing Engineering Materials Science & Nanotechnology Mechanical Engineering Social Sciences Other

Published : 7 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 2 Documents
Search
Journal : Creative Research Journal

 1 
PENINGKATAN KEKERASAN PERMUKAAN FERRO CASTING DUCTILE (FCD) 700 MELALUI PROSES NITRIDASI DENGAN MEDIA UREA Wiwik Purwadi; Dewi Idamayanti; Firman
CR JOURNAL (CREATIVE RESEARCH FOR WEST JAVA DEVELOPMENT) Vol. 1 No. 01 (2015): Creative Research For West Java Development
Publisher : Badan Penelitian dan Pengembangan Daerah Provinsi Jawa Barat

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

Ferro Casting Ductile (FCD) 700 is widely used for products requiring strength, ductility and impact resistance such as crank shaft. Surface hardening can be aplied to improve the performance of this material which can be accomplished through nitriding process. This research deals with nitriding process by using urea as the nitrogen source to achieve the surface hardness of 700 HV(600 HRC). Nitriding has been accomplished by varying the temperature (530oC, 550oC, 580oC, 600oC, and 620oC) and holding time (1-2hrs). The ratio between the amount of urea and surface area is constantly maintained at 0,25 g/mm2, while the room pressure in the nitriding tube was 0,3 Mpa. The hardness value and the microstructure are used to analyse the result. 1 hr of holding time with at the temperature of 580oC, 600oC, 620oC and 2 hrs holding time at 530oC, 550oC, 580oC, 600oC, dan 620oC has resulted white layer on the surface of the material. The maximum depth of white layer (4,83 μm) has been achieved at 2 hrs holding time and temperature of 620oC. The maximum hardness of 733 HV is resulted after holding the temperature at 580oC for 2 hrs.
PENINGKATAN KEKERASAN PERMUKAAN FERRO CASTING DUCTILE (FCD) 700 MELALUI PROSES NITRIDASI DENGAN MEDIA UREA Purwadi, Wiwik; Idamayanti, Dewi; Firman
CREATIVE RESEARCH JOURNAL Vol 1 No 01 (2015): Creative Research Journal
Publisher : Badan Penelitian dan Pengembangan Daerah Provinsi Jawa Barat

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.34147/crj.v1i01.195

Abstract

Ferro Casting Ductile (FCD) 700 digunakan untuk produk yang memerlukan kekuatan, duktilitas dan ketahanan impak, misalnya pada poros engkol. Untuk meningkatkan kinerja material dapat dilakukan pengerasan permukaan antara lain dengan proses nitridasi. Proses nitridasi dengan menggunakan urea sebagai sumber nitrogen dilakukan untuk meningkatkan kekerasan permukaan hingga 700 HV (60 HRC). Pada penelitian ini proses nitridasi dilakukan berdasarkan rasio urea per luas permukaan nitridasi. Variabel parameter yang diaplikasikan adalah temperatur (530 0C, 550 0C, 580 0C, 600 0C, dan 620 0C) dan waktu proses (1 jam dan 2 jam). Parameter yang digunakan secara konstan adalah rasio ketersediaan urea per luas permukaan sebesar 0,25 g/mm2 dan tekanan ruangan nitridasi 0,3 Mpa. Verifikasi hasil dilakukan dengan pengujian kekerasan dan struktur mikro. Berdasarkan analisa struktur mikro yang didapat, pada variasi temperatur dan waktu nitridasi (580 0C, 600 0C, dan 620 0C dengan waktu proses nitridasi 1 jam dan 530 0C, 5500C, 580 0C, 600 0C, dan 620 0 dengan waktu proses 2 jam) dihasilkan white layer pada permukaan FCD 700. Kedalaman white layer maksimum terjadi pada temperatur nitridasi 620 0C dengan waktu nitridasi 2 jam sebesar 4,83 μm. Kekerasan permukaan tertinggi sebesar 733 HV dihasilkan pada temperatur 580 0C dengan waktu proses 2 jam