 1 
SINTESIS DAN KARAKTERISASI NANOPARTIKEL CO2+ DOPED ZNO DENGAN MENGGUNAKAN METODE SOL-GEL Kasuma Warda Ningsih, Sherly; Bahrizal, Bahrizal; Nasra, Edi; Rahayu, Yanna
Indonesian Journal of Chemical Science Vol 9 No 1 (2020)
Publisher : Universitas Negeri Semarang

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

Penelitian tentang sintesis dan karakterisasi Co2+ doped ZnO telah dilakukan dengan menggunakan metode sol-gel. Zink klorida dan kobal klorida heksahidrat digunakan sebagai prekursor. Metanol digunakan sebagai pelarut dan monoetanolamin (MEA) digunakan sebagai penstabil sol. Konsentrasi dopan yang digunakan yakni 3%, 5% dan 7% dengan suhu kalsinasi 400 oC. Sampel Co2+ doped ZnO dianalisis dengan menggunakan FTIR, UVDRS dan XRD. Analisis FTIR menunjukkan regangan pada bilangan gelombang 566 cm-1 untuk Zn-O dan Co2+ doped ZnO menunjukkan Zn-O-Co 660 cm? . Nilai band gap diukur dengan UV-DRS untuk sampel Co2+ doped ZnO pada suhu 400 oC untuk 3, 5, 7% sebesar 2,4 eV, 2,3 eV dan 2,4 eV berturut-turut. Struktur kristal ZnO doped Co2+ yang dihasilkan adalah struktur wurtzite (Heksagonal) dengan rentangan ukuran kristalit berkisar antara 35-86 nm.
Sintesis Mg2+ Doped ZnO dengan Penambahan Albumen Ayam Ras Menggunakan Gabungan Metode Sol-Gel dan Sonokimia Kasuma Warda Ningsih, Sherly; Kalmar Nizar, Umar; Bahrizal, Bahrizal; Nasra, Edi; Fatimah Mutiara R, Siti
Jurnal Riset Kimia Vol 12, No 1 (2021): March
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.25077/jrk.v12i1.374

Abstract

Mg2+ doped ZnO has been successfully synthesized using a combination of sol-gel and sonochemical methods. Zinc acetate dihydrate was used as a precursor, magnesium chloride hexahydrate as a source of Mg dopant, methanol as a solvent, and chicken albumen was used as an additive to replace monoethanolamine. The sol was heated at 110 °C for 1 hour. The gel formed was calcined at 600 °C for 3 hours. FTIR analysis shows that the absorbance band around 400-450 cm-1 indicates Mg-O stretching, the absorbance band around 500-550 cm-1 indicates Zn-O stretching, the absorbance band around 400-550 cm-1 shows Zn-O-Mg bonds. Mg. Measurements with UV-DRS, obtained the smallest ZnO band gap value doped Mg2+ around 2.7 eV with the addition of 10 mL albumen. The resulting crystal structure was wurtzite with crystal size with the addition of 10, 20, 30, 40 and 50 mL albumen were 25.22-55.91 nm, 32.99-75.87 nm, 45.92-83.91 nm, 45.92-75.89 nm and 46.15-71.47 nm respectively. SEM photo of Mg2+ doped ZnO with the addition of 10 mL of albumen has a hexagonal surface morphology.
Sintesis dan Karakterisasi Nanopartikel Co2+ doped ZnO dengan Menggunakan Metode Sol-Gel Kasuma Warda Ningsih, Sherly; Bahrizal, Bahrizal; Nasra, Edi; Rahayu, Yanna
Indonesian Journal of Chemical Science Vol 9 No 1 (2020)
Publisher : Universitas Negeri Semarang

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.15294/ijcs.v9i1.37135

Abstract

Penelitian tentang sintesis dan karakterisasi Co2+ doped ZnO telah dilakukan dengan menggunakan metode sol-gel. Zink klorida dan kobal klorida heksahidrat digunakan sebagai prekursor. Metanol digunakan sebagai pelarut dan monoetanolamin (MEA) digunakan sebagai penstabil sol. Konsentrasi dopan yang digunakan yakni 3%, 5% dan 7% dengan suhu kalsinasi 400 oC. Sampel Co2+ doped ZnO dianalisis dengan menggunakan FTIR, UVDRS dan XRD. Analisis FTIR menunjukkan regangan pada bilangan gelombang 566 cm-1 untuk Zn-O dan Co2+ doped ZnO menunjukkan Zn-O-Co 660 cm‑ . Nilai band gap diukur dengan UV-DRS untuk sampel Co2+ doped ZnO pada suhu 400 oC untuk 3, 5, 7% sebesar 2,4 eV, 2,3 eV dan 2,4 eV berturut-turut. Struktur kristal ZnO doped Co2+ yang dihasilkan adalah struktur wurtzite (Heksagonal) dengan rentangan ukuran kristalit berkisar antara 35-86 nm.