Article Per Year (5 Year)
p-Index From 2020 - 2025
0
P-Index
This Author published in this journals
All Journal Jurnal Rekayasa, Teknologi, dan Sains
R, Tumpal Ojahan
Unknown Affiliation
Chemical Engineering, Chemistry & Bioengineering Civil Engineering, Building, Construction & Architecture Environmental Science Industrial & Manufacturing Engineering Mechanical Engineering

Published : 3 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 3 Documents
Search

 1 
ANALISA VARIASI ARUS MENGGUNAKAN LAS GTAW PADA MATERIAL SS JIS410J1 DENGAN FILLER ER308L R, Tumpal Ojahan; Putra, Ferry Mahardika; Hendronursito, Yusup
Jurnal Rekayasa Teknologi dan sains Vol 2, No 1 (2018): Jurnal Rekayasa, Teknologi, dan Sains
Publisher : Fakultas Teknik Universitas Malahayati

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.33024/jrets.v2i1.1115

Abstract

Tujuan penelitian ini adalah mengetahui pengaruh las GTAW menggunakan Filler ER308L pada material SS JIS410J1 terhadap nilai uji tarik dan struktur mikro. Proses penelitian ini menggunakan las GTAW dengan variasi arus 150A, 200A, 250A dan menggunakan kampuh V. Untuk mengetahui hasil penelitian diatas maka dilakukan beberapa pengujian yaitu uji penetran, uji komposisi kimia, uji tarik serta struktur mikro. Dari hasil pengujian penetran tidak didapatkan cacat pada semua sampel. Dari hasil uji komposisi kimia setelah dilakukan perbandingan dengan standar JISG4303(2015), menunjukan bahwa material dasar adalah SS JIS410J1. Dari hasil pengujian uji tarik nilai yang terbaik terdapat pada proses pengelasan dengan variasi arus 150 A, dimana tegangan luluh 386,388 MPa, tegangan maksimal 830,392 MPa, perpanjangan 42,86 mm, regangan 40,81%. Hasil struktur mikro sebelum dilakukan pengelasan adalah fasa martensite, setelah dilakukan pengelasan terdapat penambahan fasa ferrite dan karbida crom pada HAZ dan fasa austenite pada daerah lasan.Kata kunci : stainless steel JIS410J1, sifat mekanik, variasi arus, pengelasan GTAWABSTRACT: Analysis Of Flow Variation Using Gtaw Ware On Ss Jis410j1 Material With Filler Er308l. The purpose of this research is to know the effect of GTAW welding using Filler ER308L on SS JIS410J1 material to tensile test value and micro structure. The research process uses GTAW welding with current variations of 150 A, 200 A, 250 A and using V. To find out the results of the above research then performed some testing that is penetrant test, chemical composition test, tensile test and micro structure. From the result of penetrant testing there is no defect in all samples. From the result of chemical composition test after comparison with JISG4303 (2015) standard, it shows that the basic material is SS JIS410J1. From the best value of tensile test result, there is welding process with variation of current 150 A, where yield stress 386,388 MPa, maximum voltage 830,392 MPa, extension 42,86 mm, strain 40,81%. The result of microstructure before welding is martensite phase, after welding there is addition of ferrite phase and carbide crom at HAZ and austenite phase in weld area. Keywords: stainless steel JIS410J1, mechanical properties, current variation, GTAW welding.
ANALISA FLUIDA PENDINGIN TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO PADA MATERIAL STAINLESS STEEL 304 R, Tumpal Ojahan; Hendronursito, Yusup; Hidayat, Arif
Jurnal Rekayasa Teknologi dan sains Vol 1, No 2 (2017): Jurnal Rekayasa, Teknologi, dan Sains
Publisher : Fakultas Teknik Universitas Malahayati

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.33024/hjk.v12i2.1103

Abstract

Material stainless steel banyak digunakan di dunia industri dan alat-alat kesehatan karena memiliki sifat korosif yang baik, mampu mencegah kontaminasi, dapat didaur ulang, dekoratif dan mudah dibersihkan. Penggunaan stainless steel tidak lepas dari proses pengelasan, oleh karena itu penulis melakukan penelitian dengan memvariasikan Fluida Pendingin (Air, Oli dan Udara) menggunakan las GTAW dengan parameter debit aliran gas 17 liter/menit, arus 130 Amper dan Elektroda EWTh-2. Tujuan penelitian ini untuk mengetahui pengaruh pendinginan terhadap sifat mekanik dan struktur mikro. Hasil Pengujian Tarik nilai rata-rata σy = 374,0 MPa, σmax = 626,0 MPa, ΔL = 27,5 mm dan ε= 54,8 % fluida air. Nilai rata-rata σy = 335,3 MPa, σmax = 543,7 MPa, ΔL = 22,1 mm dan ε = 44,2 % fluida oli. Nilai rata-rata σy = 299,3 MPa, σmax = 481,3 MPa, ΔL = 19,4 mm dan ε = 38,8 % fluida udara.Hasil Pengujian Kekerasan nilai rata-rata fluida air daerah weld = 74,93 HRb, HAZ = 75,50 HRb. Nilai rata-rata fluida oli daerah weld = 74,77 HRb, HAZ = 74,60 HRb. Nilai rata-rata fluida udara daerah weld = 73,40 HRb, HAZ = 74,43 HRb. Fasa yang terbentuk sebelum pengelasan adalah fasa austenite, setelah dilakukan pengelasan terdapat penambahan fasa karbida crom. Dari hasil pengujian sifat mekanik yang telah dilakukan dapat disimpulkan bahwa untuk pengelasan GTAW dengan material stainless steel jenis 304 fluida pendingin yang terbaik adalah dengan menggunakan fluida pendingi air.Kata Kunci: GTAW, fluida pendingin, stainless steel 304, sifat mekanik, struktur mikro.ABSTRACT: Cooling fluid analysis of mechanical properties and micro structure on stainless steel 304 material. Stainless steel materials widely used in the industrial and medical equipment becausehaving the nature of corrosive, capable of preventing contamination, can be recycled, decorative and easily cleared. The use of stainless steel can’t be separated from the process of welding, writer do research by varying fluid cooling (Water, Oli and Air) using GTAW welding with discharge of the parameters a stream of gas 17 liters per minute, the current 130 Ampere and Electrodes EWTh-2. The purpose of this research to know the cooling influence against mechanical properties and micro structure. The results of tensile test value is σy = 374,0 MPa, σmax = 626,0 MPa, ΔL = 27,5 mm and ε = 54,8 % water fluid. The value is σy = 335,3 MPa, σmax = 543,7 MPa, ΔL = 22,1 mm and ε = 44,2 % oil fluid. The value is σy = 299,3 MPa, σmax = 481,3 MPa, ΔL = 19,4 mm and ε = 38,8 % airfluid. The results of hardness test value of water fluid in welding area = 74,93 HRb, HAZ = 75,50 HRb. The results value of oil fluid in welding area = 74,77 HRb, HAZ = 74,60 HRb. The results value of air fluid in welding area = 73,40 HRb, HAZ = 74,43 HRb. The phase that is formed before welding is the austenite phase, through welding there are adding the phase carbide crom. From the testing mechanical properties that has been in conclusion that for GTAW welding with the material stainless steel 304 cooling kind of fluid the list is water cooling fluid.Keywords: GTAW, cooling fluid, stainless steel 304, mechanical properties, micro structure.
PENGARUH VARIASI TEMPERATUR PENCELUPAN TERHADAP SIFAT MEKANIK PADA BAJA KARBON RENDAH (0.02% C) DENGAN METODE PELAPISAN HOT DIP GALVANIZING R, Tumpal Ojahan; Sumardi, Slamet; Yoga, Dwi
Jurnal Rekayasa Teknologi dan sains Vol 1, No 1 (2017): Jurnal Rekayasa, Teknologi, dan Sains
Publisher : Fakultas Teknik Universitas Malahayati

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.33024/jrets.v1i1.987

Abstract

Tujuan penelitian ini adalah mengetahui pengaruh temperatur pencelupan terhadap nilai kekerasan, nilai ketebalan lapisan, struktur mikro serta pengamatan SEM. Proses penelitian ini menggunakan metode pelapisan Hot Dip Galvanizing dengan variasi temperatur 420 oC, 440 oC, 460 oC, 480 oC serta waktu pencelupan selama 6 menit. Untuk mengetahui hasil penelitian diatas maka dilakukan beberapa pengujian yaitu uji komposisi kimia, uji kekerasan HRb, uji ketebalan lapisan, uji struktur mikro serta uji SEM. Hasil uji kekerasan tertinggi pada variasi temperatur 480 oC sebesar 76.51 HRb, hasil uji ketebalan lapisan tertinggi pada variasi temperatur 440 oC sebesar 200.09 μm dan hasil uji struktur mikro menunjukkan susunan struktur lapisan Zn dengan baja terbentuk Eta, Zeta, Delta dan Gamma. Pengamatan SEM terdapat unsur yang terkandung pada material yang dilapisi. Dari penelitian ini dapat disimpulkan bahwa variasi temperatur juga mempengaruhi hasil dari sifat mekanik.Kata kunci : baja karbon rendah, sifat mekanik, variasi temperatur pencelupan, hot dip galvanizing. ABSTRACT: The Immersion Temperature Variations Influence Of Mechanical Properties In Steel Low Carbon (0,02% C) With The Coating Hot Dip Galvanizing Method.The objective of the study was to identify the effect of temperature variation on dip process towards hardness index, layer thickness rate, micro structure and SEM observation. This study occupied Hot Dip Galvanizing with 420 oC, 440 oC, 460 oC, 480 oC temperature variations and 6 minutes dip process duration. To achieve the above objectives, some test were done, they are chemical composition, HRb Hardness test, layer thickness test, micro structure test and SEM test. The highest hardness test on 480 oC was 76.51 HRb, the thickest was on 440 oC temperature with 200.09 μ m, and the result of micro structure showed structural composition consisting of Eta, Zeta, Delta and Gamma. SEM observation revealed elements contained in coated material. This study concluded that temperature variation effected mechanica l properties.Keywords : low carbon steel, mechanical, dip temperature variation, hot dip galvanizing 