Pengaruh rasio MBTS/ZDEC pada campuran karet alam dan etilen propilen diena yang dibuat dengan teknik kontrol migrasi curatives Ihda Novia Indrajati; Muhammad Sholeh
Majalah Kulit, Karet, dan Plastik Vol 30, No 1 (2014): Majalah Kulit, Karet, dan Plastik
Publisher : Center for Leather, Rubber, and Plastic Ministry of Industry, Indonesia

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.20543/mkkp.v30i1.124

Abstract

The objective of this research was to observe the effect of MBTS/ZDEC ratio on dynamic properties, curing characteristic, morphology as well as hardness and resiliency of the NR/EPDM blends prepared by curatives migration control technique. The MBTS/ZDEC ratio were 1.6/0.0; 1.5/0.1; 1.4/0.2; 1.3/0.3 and 1.2/0.4 respectively on a fixed NR/EPDM ratio of 60/40. Compounds (EPDM and NR) were prepared separately using two roll mill. The blends with binary accelerator MBTS/ZDEC showed synergistic activity which provided higher crosslink density than those of single accelerator MBTS. Reduction of ts2 and t90 as well as cure rate index (CRI) indicated the more homogeneous crosslink density distribution within the rubber phase. Scanning electron micrograph showed that the blends with binary accelerator gave smoother surface. Binary accelerator resulted higher hardness. Increasing of ZDEC raised hardness followed by reduction of the resillience property.ABSTRAKPenelitian ini bertujuan mempelajari pengaruh rasio MBTS/ZDEC pada sifat dinamik, karakteristik curing, karakteristik morfologi serta kekerasan dan sifat pegas pantul campuran NR/EPDM yang dibuat dengan teknik kontrol migrasi curatives. Rasio MBTS/ZDEC yang digunakan dalam penelitian ini secara berurutan 1,6/0,0; 1,5/0,1; 1,4/0,2; 1,3/0,3; dan 1,2/0,4 pada rasio NR/EPDM tetap 60/40. Kompon dibuat secara terpisah (kompon EPDM dan NR) menggunakan two roll mill. Campuran NR/EPDM dengan akselerator biner MBTS/ZDEC menunjukkan sinergi aktivitas yang memberikan kerapatan ikatan silang lebih tinggi daripada akselerator tunggal MBTS. Kemampuan proses kompon akselerator biner lebih rendah daripada akselerator tunggal. Penurunan ts2 dan t90 serta kenaikan indeks kecepatan reaksi (CRI) mengindikasikan distribusi ikatan silang yang merata pada kedua fasa karet. Mikrograf pemindaian elektron (SEM) menunjukkan campuran dengan akselerator biner mempunyai permukaan yang lebih halus. Kekerasan vulkanisat sistem biner lebih tinggi. Penambahan ZDEC meningkatkan kekerasan dan diikuti dengan penurunan sifat pegas pantul.
Pengaruh variasi rasio HAF/SRF terhadap sifat vulkanisat NBR Ihda Novia Indrajati; Indiah Ratna Dewi; Dodi Irwanto
Majalah Kulit, Karet, dan Plastik Vol 28, No 2 (2012): Majalah Kulit, Karet, dan Plastik
Publisher : Center for Leather, Rubber, and Plastic Ministry of Industry, Indonesia

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.20543/mkkp.v28i2.106

Abstract

ABSTRACTThe objectives of the research were to study the effect of HAF/SRF black ratio and the loading of sulfur on vulcanization characteristic, swelling behaviour and compression set of NBR vulcanizates. The ratio of HAF/SRF were 0/70; 10/60; 20/50; 30/40; 35/35; 40/30; 50/20 and 70/0 phr, respectively. The observation of this research consist of curing characteristic, morphology property and swelling equilibrium. Curing characteristic was determined from cure rate index (CRI), vulcanizates morphology was studied by SEM and swelling equilibrium was conducted by immersion test using benzene. The data were analyzed qualitatively to see the respond of the variable on physical properties. The curing characteristic of double filler vulcanizates was higher than those with single filler. Solvent uptake for double filler present in between to those with HAF or SRF. All of vulcanizates indicate the anomalous mass tranfer, with n>0,5 and constant k showed the same trend. The intrinsic diffusivity (D*), sorption and permeation coefficient showed similar trend and the maximum was obtained by the ratio HAF/SRF 0/70.ABSTRAKTujuan penelitian adalah mempelajari pengaruh rasio HAF/SRF terhadap karakteristik vulkanisat, kesetimbangan swelling dan perpindahan massa pada vulkanisat NBR. Rasio HAF/SRF yang digunakan berturut – turut 0/70; 10/60; 20/50; 30/40; 35/35; 40/30; 50/20 dan 70/0 phr. Pengamatan dilakukan pada karakteristik vulkanisasi, sifat morfologi dan kesetimbangan swelling. Data dianalisa secara kualitatif untuk melihat respon variabel penelitian terhadap sifat fisis vulkanisat. Karakteristik vulkanisasi ditentukan dari nilai indeks kecepatanvulkanisasi (cure rate index/CRI), morfologi vulkanisat dipelajari menggunakan alat SEM, dan kesetimbangan swelling dilakukan dengan cara perendaman dalam benzen dengan menghitung kecepatan penetrasi dan koefisien difusinya. Karakteristik vulkanisasi vulkanisat bahan pengisiganda memberikan nilai lebih tinggi daripada dengan bahan pengisi tunggal. Konsumsi pelarut (uptake) vulkanisat dengan bahan pengisi HAF dan SRF mempunyai nilai berada diantara vulkanisat dengan bahan pengisi tunggal. Mekanisme perpindahan massa untuk keseluruhan rasio HAF/SRF mengindikasikan anomali dengan nilai n>0,5 dan konstanta k yang relatif sama. Koefisien difusi intrinsik (D*), koefisien serapan (S) dan koefisien permeasi (P) secara umum menunjukkan kecenderungan dan nilai maksimum diberikan oleh rasio 0/70.