Search

 1 
Analisis Kegagalan Retak dan Teknologi Perbaikan Sudu Turbin Jenis Inconel 792 pada Pesawat Terbang Suharno .; Arif Sugiyanto; Yuyun Estriyanto; Budi Harjanto
Jurnal Teknik Mesin (Sinta 3) Vol. 14 No. 1 (2013): APRIL 2013
Publisher : Institute of Research and Community Outreach, Petra Christian University

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

Penelitian untuk melakukan analisis terhadap kegagalan retak telah dilakukan pada sudu turbin dari Auxiliary Power Unit (APU) pesawat terbang. Bahan sudu turbin adalah paduan super  Inconel 792. Pengujian yang dilakukan meliputi inspeksi visual, pengujian komposisi kimia, fractography, pengujian kekerasan, dan metalografi.Hasilnya menunjukkan bahwa patah dimulai dari celah dan retak makro dan kemudian menjalar/merambat menjadi retak terbuka di permukaan.Hal ini kemungkinan disebabkan oleh mekanisme retak panas selama perbaikan las sebelumnya. Kandungan Aluminium dan Titanium yang tinggi pada logam las, menjadikan material menjadi rapuh, hal ini ditunjukkan oleh fitur intergranular dibandingkan dengan aspek pembelahan transgranular menunjukkan bahwa keuletan pada lasan rendah. Dibandingkan dengan sudu yang tidak rusak (gagal), ukuran butir dari sudu turbin yang rusak adalah sangat berbeda menunjukkan eksposisi terhadap panas baik dari siklus termal pengelasan atau lingkungan operasi normal pada suhu tinggi.Teknik perbaikan lebih lanjut dikembangkan berdasarkan keberhasilan PQTR yang di uji dengan kekerasan mikro, destructive dan non destructive test.Untuk tujuan ini maka dipilih las GTAW yang diikuti dengan solution dan aging treatment.
Studi Penelitian Panjang Kritis Serat Alam Dengan Perlakuan Perendaman Natrium Hidroksida Rangga Yanuarestu Ramadhan; Yuyun Estriyanto; Budi Harjanto
Nozel : Jurnal Pendididikan Teknik Mesin Vol 3, No 4 (2021)
Publisher : Fakultas Keguruan dan Ilmu Pendidikan Universitas Sebelas Maret Surakarta

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.20961/nozel.v3i4.63009

Abstract

The purpose of this study was to determine the critical length of palm fiber, kenaf fiber, pineapple fiber, agave fiber, and coconut fiber with NaOH immersion treatment. This study was determine the effect of NaOH immersion treatment on the critical length of fiber. This research is an experimental exploratory research. The independent variables in this study were palm fiber, kenaf fiber, pineapple fiber, agave fiber, and coconut fiber with the dependent variable is the critical fiber length. To find the critical length of fiber using single fiber tensile test and single fiber pull out test. The data obtainde from the test results are then analyzed using formula equation to determine the critical length of each fiber. Data analysis techniques using quantitative descriptive analysis techniques. The results showed that the critical length of palm fiber, kenaf fiber, agave fiber, and coconut fiber with NaOH immersion treatment was shorter than the critical length of fiber without NaOH immersion treatment. Agave fiber has the shortest critical fiber length. The critical length of the fiber with NaOH immersion treatment are palm fiber 4.6 mm, kenaf fiber 5.4 mm, pineapple fiber 3.6 mm, agave fiber 2.2 mm, and coconut fiber 3.0 mm. 