Effect of Basalt Size and Composition on Mechanical Properties of Wood Powder Polymer Biocomposite Material and Basalt as Reinforcement Prabowo, Singgih; Astuti; Birawidha; Amin; Bahfie; Dwi Yanti; Savitri; Karo Karo; Irwanto
Jurnal Sains Materi Indonesia Vol. 26 No. 1 (2024): Jurnal Sains dan Materi Indonesia
Publisher : BRIN Publishing (Penerbit BRIN)

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.55981/jsmi.2024.4568

Abstract

Utilization of waste for raw materials for new materials is very potential for research. Wood waste from door and window craftsmen is widely available as the property business develops. Wood waste mixed with polyester resin is modified by adding basalt to produce a biocomposite material with better mechanical properties. This research on the effect of adding the composition and size of basalt to the wood-polyester biocomposite material was studied to see changes in hardness values according to the ASTM E384 standard, compressive strength according to ASTM D695 standard, and its effect on density according to ASTM D1622 standard. The results showed that the higher the composition and the smaller the basalt hardness value, the compressive strength and density increased. The highest values of hardness, compressive strength and density were 36.6 HV0.5, 151.14 MPa, and 0.1420 kg/m3, an increase compared to that without the addition of basalt 26.7 HV0.5, 95.97 MPa, and 0.1288 kg/m3. Changes in the properties of hardness, compressive strength and density are taken into consideration in the formulation of using basalt to obtain new materials according to the desired specifications by utilizing wood waste.
Transformasi Sampah Plastik Menjadi Campuran Batako Bangunan Ramah Lingkungan di Desa Karangsari Zaenal Mustofa; Buntara Adi Purwanto; Achmad Faisal Abda’; Singgih Prabowo; Muhammad Nafis; Miftahul Fuadi; Riziq Anta Yahya; Rosita Dwi Widya Ningrum; Gita Amalia; Sela Asyifa Dalila; Lupita Orisativa Aprilia; Annur Trihardiyanti; Nova Nur Ramadhani; Ikka Rusmawardani Afsah; Putri Avinda; Kun Mabruroh
Jurnal Pengabdian Masyarakat dan Riset Pendidikan Vol. 4 No. 3 (2026): Jurnal Pengabdian Masyarakat dan Riset Pendidikan Volume 4 Nomor 3 (Januari 202
Publisher : Lembaga Penelitian dan Pengabdian Masyarakat

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.31004/jerkin.v4i3.5336

Abstract

Permasalahan sampah plastik di Desa Karangsari terus meningkat seiring bertambahnya aktivitas masyarakat sehari-hari. Sampah plastik merupakan limbah yang sulit terurai dan berpotensi mencemari lingkungan apabila tidak dikelola dengan baik. Pengolahan sampah plastik di desa tersebut masih belum optimal dan sebagian besar berakhir sebagai limbah tanpa pemanfaatan lanjutan. Kegiatan pengabdian ini bertujuan untuk memanfaatkan sampah plastik jenis HDPE dan PP sebagai campuran batako ramah lingkungan guna mengurangi pencemaran lingkungan sekaligus menciptakan produk bangunan bernilai guna dan bernilai ekonomi. Metode pelaksanaan meliputi edukasi masyarakat, pemilahan sampah plastik, serta pelatihan pembuatan batako skala desa dengan teknologi sederhana menggunakan campuran semen, pasir, air, dan plastik cacah. Hasil kegiatan menunjukkan bahwa pemanfaatan sampah plastik sebagai campuran batako mampu mengurangi volume limbah plastik, menghasilkan material bangunan non-struktural yang layak digunakan, serta meningkatkan kesadaran dan keterampilan masyarakat dalam pengolahan sampah. Program ini juga membuka peluang usaha baru yang mendukung pemberdayaan ekonomi masyarakat desa. Dengan demikian, transformasi sampah plastik menjadi batako ramah lingkungan berkontribusi positif terhadap pembangunan Desa Karangsari yang berkelanjutan.