Article Per Year (5 Year)
p-Index From 2020 - 2025
0
P-Index
This Author published in this journals
All Journal JURNAL DINAMIKA VOKASIONAL TEKNIK MESIN
Nurdjito Nurdjito
Jurusan Pendidikan Teknik Mesin, Universitas Negeri Yogyakarta
Education Mechanical Engineering Social Sciences

Published : 2 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 2 Documents
Search

 1 
Pengembangan Tool Holder untuk Meningkatkan Kompetensi Mahasiswa pada Pembelajaran Praktik Pemesinan Surono Surono; Febrianto Amri Ristadi; Nurdjito Nurdjito; Asnawi Asnawi
Jurnal Dinamika Vokasional Teknik Mesin Vol. 3 No. 1 (2018): April
Publisher : Department of Mechanical Engineering Education

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.21831/dinamika.v3i1.19123

Abstract

This research aims to: (1) design a tool holder specified for existing machine tools in Machining Workshop at Mechanical Engineering Education of Universitas Negeri Yogyakarta; (2) Assess the feasibility of the developed design. The research used Research and development (R&D) design incorporating ADDIE Model. Data collection were performed using observation, questionnaire, and documentation. Data were analyzed using descriptive quantitative technique. The results are: (1) tool holder design was suited to the needs of the tools in the workshop, which are mill bits, internal turning tool holder, and tap holder; (2) the overall interpretation are "Agree" that the tool holder is feasible to use in machining practice.Tujuan penelitian ini adalah untuk: (1) menciptakan desain tool holder yang disesuaikan dengan mesin perkakas yang ada di bengkel pemesinan Jurusan Pendidikan Teknik Mesin, Universitas Negeri Yogyakarta; (2) mengetahui kelayakan tool holder yang telah dikembangkan. Desain penelitian  yang  digunakan  adalah Penelitian dan Pengembangan/Reseach and Development (R&D) dengan menggunakan ADDIE Model. Pengumpulan data menggunakan teknik observasi, angket, dan dokumentasi. Analisis data menggunakan teknik deskriptif kuantitatif. Hasil penelitian ini adalah: (1) desain tool holder yang dikembangkan disesuaikan dengan tingkat kebutuhan pemakaian peralatan tersebut di bengkel mesin, yaitu mill bits, holder pahat bubut dalam, dan holder tap; (2) berdasarkan intepretasi data penilaian terhadap tool holder yang telah dikembangkan, secara keseluruhan diperoleh intepretasi "Setuju" bahwa alat (tool holder) tersebut layak digunakan sebagai alat bantu pemegang pahat pada proses pemesinan.
Karakterisasi Grinding Balls Produksi CV Baja Ellips Arianto Leman; Tiwan Tiwan; Nurdjito Nurdjito
Jurnal Dinamika Vokasional Teknik Mesin Vol. 3 No. 1 (2018): April
Publisher : Department of Mechanical Engineering Education

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.21831/dinamika.v3i1.19115

Abstract

This research is aimed to study the characteristics of cast grinding balls produced by CV Baja Ellips Ceper, Klaten. The samples were taken from three tapping. One group was quenched in water while the other was not. The studied characteristics comprised of chemical composition, microstructure, hardness and wear. The result shows that the grinding balls have the chemical composition of medium-strength cast iron. However, the microstructure shows cementite and pearlite that indicates the structure of a white cast iron. The hardness of quenched and unquenched grinding balls are 60 HRC and 57 HRC, respectively. The hardness is consistent from the edges to the middle of the grinding balls. The specific wear of quenched grinding balls and unquenched grinding balls is 3.32963 x 10-06 mm2/kg and 5.032 x 10-06 mm2/kg, respectivelyPenelitian ini bertujuan untuk mengetahui karakteristik grinding balls produksi CV Baja Ellips Ceper Klaten yang dibuat dengan menggunakan proses pengecoran. Sampel grinding balls diambil dari tiga kali tapping yang berbeda. Satu kelompok dicelup dingin dalam air dan yang tidak dicelup dingin. Karakterisasi yang dilakukan meliputi komposisi kimia, struktur mikro, kekerasan dan keausan. Hasil penelitian menunjukkan bahwa komposisi kimia dari bola penggiling termasuk dalam kelas besi tuang kekuatan sedang. Struktur mikro yang tampak adalah sementit dan perlit yang menunjukkan struktur besi tuang putih. Kekerasan grinding balls yang dicelup dingin adalah 60 HRC sedangkan yang tanpa dicelup dingin sebesar 57 HRC. Kekerasan grinding balls konsisten dari bagian tepi sampai bagian tengah. Keausan spesifik grinding balls yang dicelup dingin dan tanpa dicelup dingin berturut-turut 3,32963 x 10-06 mm2/kg dan 5,032 x 10-06 mm2/kg