Article Per Year (5 Year)
p-Index From 2021 - 2026
0.562
P-Index
This Author published in this journals
All Journal Journal La Multiapp
Lucian Paunescu
Bilmetal Industries SRL Popesti Leordeni-Ilfov, Romania & Daily Sourcing & Research SRL Bucharest, Romania
Aerospace Engineering Automotive Engineering Chemical Engineering, Chemistry & Bioengineering Civil Engineering, Building, Construction & Architecture Engineering

Published : 3 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 3 Documents
Search

 1 
Granulated Expanded Glass Manufacturing Method Using Electromagnetic Waves Lucian Paunescu; Sorin Mircea Axinte; Felicia Cosmulescu; Marius Florin Dragoescu
Journal La Multiapp Vol. 2 No. 4 (2021): Journal La Multiapp
Publisher : Newinera Publisher

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.37899/journallamultiapp.v2i4.477

Abstract

The paper presents experimental results obtained in the process of experimental manufacture in a microwave oven of lightweight granulated glass aggregates. The process was conducted to obtain the highest dimensional class (between 18-23 mm), the almost spherical shape of the aggregates being facilitated by cold processing of raw spherical pellets (between 11-15 mm) containing the powder mixture formed by glass waste, borax. calcium carbonate, aqueous sodium silicate solution and water addition and then rotation of the high electromagnetic wave susceptible ceramic crucible containing raw pellets during the heat treatment at temperatures between 822-835 ºC. In terms of quality, the expanded glass aggregate granules are almost similar to those manufactured in conventional rotary kilns heated by burning fuel, having the following characteristics: bulk density of 0.17 g/cm3, compressive strength of 2.2 MPa, thermal conductivity of 0.047 W/m·K, water absorption of 1 vol. % and pore size between 0.3-0.6 mm. The experimental product has not yet been tested as a raw material in the manufacture of some light weight concretes, but the use of similar granulated glass aggregates manufactured in the world confirms the ability of this aggregate type to produce light weight and energy efficient concretes for building construction.
Granulated Expanded Glass Manufacturing Method Using Electromagnetic Waves Lucian Paunescu; Sorin Mircea Axinte; Felicia Cosmulescu; Marius Florin Dragoescu
Journal La Multiapp Vol. 2 No. 5 (2021): Journal La Multiapp
Publisher : Newinera Publisher

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.37899/journallamultiapp.v2i5.478

Abstract

The paper presents experimental results obtained in the process of experimental manufacture in a microwave oven of lightweight granulated glass aggregates. The process was conducted to obtain the highest dimensional class (between 18-23 mm), the almost spherical shape of the aggregates being facilitated by cold processing of raw spherical pellets (between 11-15 mm) containing the powder mixture formed by glass waste, borax. calcium carbonate, aqueous sodium silicate solution and water addition and then rotation of the high electromagnetic wave susceptible ceramic crucible containing raw pellets during the heat treatment at temperatures between 822-835 ºC. In terms of quality, the expanded glass aggregate granules are almost similar to those manufactured in conventional rotary kilns heated by burning fuel, having the following characteristics: bulk density of 0.17 g/cm3, compressive strength of 2.2 MPa, thermal conductivity of 0.047 W/m·K, water absorption of 1 vol. % and pore size between 0.3-0.6 mm. The experimental product has not yet been tested as a raw material in the manufacture of some light weight concretes, but the use of similar granulated glass aggregates manufactured in the world confirms the ability of this aggregate type to produce light weight and energy efficient concretes for building construction.
Cellular Glass Manufactured by Microwave Irradiation of Residual Glass, Eggshell and Borax Lucian Paunescu; Sorin Mircea Axinte; Felicia Cosmulescu
Journal La Multiapp Vol. 2 No. 5 (2021): Journal La Multiapp
Publisher : Newinera Publisher

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.37899/journallamultiapp.v2i5.479

Abstract

The paper presents an improved method of manufacturing cellular glass using residual glass (91 %), sodium borate (5 %), eggshell waste (4 %) and added water (9 %). Compared to methods using eggshell as an expanding agent producing cellular glass with low compression strength, the technique adopted by the authors is original by the addition of sodium borate, which contributes to increasing the compression strength and the use of the unconventional electromagnetic wave heating method, which ensures very economical specific energy consumption. The optimal variant of cellular glass had the following characteristics: density of 0.40 g/cm3, porosity of 81 %, heat conductivity of 0.086 W/m·K, compression strength of 4.3 MPa and the cell dimension between 0.3-0.9 mm. The specific energy consumption of the process was 0.80 kWh/kg. The product has adequate features for using as a heat insulation material under conditions of quite high mechanical loading.
Co-Authors Felicia Cosmulescu Marius Florin Dragoescu Marius Florin Dragoescu Sorin Mircea Axinte Sorin Mircea Axinte