Articles

Found 2 Documents
Search

 1 
ANALISA KEGAGALAN POLISHED ROD PADA POMPA ANGGUK Eka Febriyanti; Dr. Ir. Amin Suhadi, M.Eng.; Laili Novita Sari
Majalah Ilmiah Pengkajian Industri Vol. 13 No. 2 (2019): Majalah Ilmiah Pengkajian Industri
Publisher : BRIN

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.29122/mipi.v13i2.3172

Abstract

Tulisan ini membahas tentang kerusakan polished rod akibat material yang digunakannya bersifat getas dan memiliki mikrostruktur yang tidak homogen. Pemeriksaan pada polished rod dari pompa angguk  menggunakan metode pengamatan visual, fraktografi makro, metalografi, uji kekerasan, analisa komposisi kimia, pemeriksaan SEM, serta uji komposisi produk korosi dengan EDX. Hasil pemeriksaan visual dan uji penetran menunjukkan adanya retak melintang yang menyebar pada satu sisi permukaan polished rod menunjukkan bahwa polished rod mengalami pembebanan bending sebelum patah. Sedangkan hasil pemeriksaan fraktografi memperlihatkan adanya daerah patahan getas dengan pola radial mark yang menandakan bahwa jenis pembebanan merupakan beban statis dengan alur perambatan yang berlangsung cepat. Selain itu, hasil pengamatan metalografi memperlihatkan bahwa struktur mikro pada polished rod bersifat tidak homogen yang terdiri atas ferit-perlit, bainit, dan martensit yang bersifat getas.  Jadi, dapat disimpulkan bahwa penyebab kerusakan adalah ketidakhomogenan pada mikrostruktur dan sifat material yang bersifat getas yang berperan sebagai konsentrasi tegangan. Dengan tertahannya sistem kerja pompa angguk menyebabkan satu sisi polished rod mengalami pembebanan bending sampai material tidak mampu lagi menahan beban lalu patah.
FATIGUE AND CORROSION PHENOMENON ON FAILURE OF WATER WALL TUBE BOILER Eka Febriyanti; Amin Suhadi; Laili Novita Sari
Majalah Ilmiah Pengkajian Industri Vol. 14 No. 1 (2020): Majalah Ilmiah Pengkajian Industri
Publisher : BRIN

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.29122/mipi.v14i1.3565

Abstract

Water wall tube is one of a boiler components which has a function to transform water to be vapour so that it is normally called steam generating tubes. Any failure on wall tube will affect to the whole boiler system.  The purpose of this research is to find out root cause of failure of wall tube in order to avoid similar case in the future.  Research is conducted by examining and testing the specimens on all aspects including visual, fractography, metallography, chemical analysis, hardness test and tensile test. Examination on the fracture surface by fractographic method found the evidence of fatigue fracture with the presence of beachmark. Another examination on uninstalled boiler tube shows indication of fabrication defect and trans-granular cracks which allowed corrosive agent infiltrated into the microstructure of the tube. However, the result of chemical analysis and tensile test indicated that the tubes investigated are in accordance with ASTM A 210 Grade C specifications. Therefore, the failure of the tube is not caused by wrong material selection, but through the combination of fatigue fracture and corrosion attack where initiated at fabrication defect that acted as stress raisers.
Co-Authors Amin Suhadi Dr. Ir. Amin Suhadi, M.Eng. Eka Febriyanti