Karakteristik Beton Mutu Tinggi dengan Substitusi Slag Baja dan Slag Nikel Sebagai Agregat Kasar Komang Saka Suwindu; Desi Sandy
Paulus Civil Engineering Journal Vol 2 No 1 (2020): Volume 2 No.1, Maret 2020
Publisher : Program Studi Teknik Sipil UKI Paulus-Makassar

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (331.768 KB) | DOI: 10.52722/pcej.v2i1.115

Abstract

This study aims to determine the value of compressive strength, split tensile, and flexural strength in high quality concrete with variations in the substitution of steel slag and nickel slag as a substitute for coarse aggregate. Concrete tests performed include compressive strength, split tensile strength, and flexural strength. The research process starts from checking the characteristics of slag, and fine aggregate then mix designs and make test specimens in the form of cylinders of 150 mm x 300 mm as many as 36 pieces and beams of 150 mmx 150 mm x 600 mm as many as 9 pieces. The results showed the substitution of steel slag and nickel slag on compressive strength, split tensile strength, and flexural strength, the greater the percentage of nickel slag, the greater the increase in compressive strength, split tensile strength and flexural strength. Compressive strength value with 20% nickel slag substitution increased 3.347%; and for 30% nickel slag substitution increased by 4.603%. The value of split tensile strength with 20% nickel slag substitution increased by 30.137%; and for 30% nickel slag substitution increased by 46.585%. The value of flexural strength with substitution of 20% nickel slag increased 31.674%; and for 30% nickel slag substitution increased by 66.179%. The relationship between compressive strength and average tensile strength obtained in high quality concrete with nickel slag substitution 0%, 20%, 30% at 28 days is 9.3%. The relationship of compressive strength with the average flexural strength obtained in high quality concrete with nickel slag substitution of 0%, 20%, 30% at 28 days is 0.621 .
Karakteristik Beton Mutu Tinggi dengan Substitusi Slag Baja dan Slag Nikel Sebagai Agregat Kasar Komang Saka Suwindu; Parung, Herman; Sandy, Desi
Paulus Civil Engineering Journal Vol. 2 No. 1 (2020): PCEJ, Vol.2, No.1, March 2020
Publisher : Universitas Kristen Indonesia Paulus

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.52722/j1j6f785

Abstract

Penelitian ini bertujuan untuk mengetahui nilai kuat tekan, tarik belah, dan kuat lentur pada beton mutu tinggi dengan variasi subtitusi slag baja dan slag nikel sebagai pengganti agregat kasar. Pengujian beton yang dilakukan adalah meliputi kuat tekan, tarik belah, dan kuat lentur. Proses penelitian dimulai dari pemeriksaaan karakteristik slag, dan agregat halus kemudian melakukan mix design dan membuat benda uji berupa silinder 150 mm x 300 mm sebanyak 36 buah dan balok 150 mmx 150 mm x 600 mm sebanyak 9 buah. Hasil penelitian menunjukkan subtitusi slag baja dan slag nikel terhadap kuat tekan, kuat tarik belah, dan kuat lentur adalah semakin besar presentase slag nikel maka semakin besar kenaikan kuat tekan, kuat tarik belah dan kuat lentur. Nilai kuat tekan dengan subtitusi slag nikel 20% meningkat 3,347%; dan untuk subtitusi slag nikel 30% meningkat sebanyak 4,603%. Nilai kuat tarik belah dengan subtitusi slag nikel 20% meningkat 30,137%; dan untuk subtitusi slag nikel 30% meningkat sebanyak 46,585%. Nilai kuat lentur dengan subtitusi slag nikel 20% meningkat 31,674%; dan untuk subtitusi slagnikel 30% meningkat sebanyak 66,179%. Hubungan kuat tekan dengan kuat tarik belah rata-rata yang diperoleh pada beton mutu tinggi dengan subtitusi slag nikel 0%, 20%, 30% pada umur 28 hari adalah 9,3%. Hubungan kuat tekan dengan kuat lentur ratarata diperoleh pada beton mutu tinggi dengan subtitusi slag nikel 0%, 20%, 30% pada umur 28 hari adalah 0,621 .