KARAKTERISTIK LAPISAN HOT DIP ALUMINIZING PADA BAJA TAHAN KARAT MARTENSITIK 13Cr Moch. Syaiful Anwar; Mikhael Kevin; Alfirano Alfirano; Efendi Mabruri
Metalurgi Vol 34, No 3 (2019): Metalurgi Vol. 34 No. 3 Desember 2019
Publisher : National Research and Innovation Agency (BRIN)

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (407.301 KB) | DOI: 10.14203/metalurgi.v34i3.462

Abstract

Pada material aplikasi suhu tinggi, pelapisan permukaan merupakan hal penting dalam memberikan ketahanan oksidasi dan korosi temperatur tinggi, ketahanan erosi dan abrasi.Hot dip Aluminizing merupakan metode alternatif pelapisan yang dapat digunakan, karena lebih murah daripada PVD dan paduan Co. Perlakuan permukaan, komposisi lelehan Al dan Al – Si, dan parameter proses seperti temperatur dan waktu pencelupan berpengaruh terhadap komposisi intermetalik dan struktur mikronya. Baja dilapisi lelehan Al murni, Al – 5% Si, Al - 11% Si, dan Al – 15% Si pada temperature dan waktu celup yang brvariasi. Si memberikan pengaruh terhadap perubahan morfologi antara substrat dengan interface intermetalik dan mencegah kemungkinan terjadinya stress konsentrasi akibat morfologi finger-like. Pada waktu pencelupan yang sama sebesar 3 menit dari 4 variasi komposisi coating yang berbeda, ketebalan lapisan coating terbesar adalah sampel Al – 15% Si dengan temperature 800oC, sedangkan ketebalan lapisan intermetalik terbesar adalah sampel Al murni dengan temperatur 861oC dengan nilai ketebalan masing-masing sebesar 480µm dan 46,8 µm.