Pengaruh Variasi Chelating Agent terhadap Karakteristik Produk pada Sintesis Elektrolit Padat NaMn2-xMgxO4 dengan Metode Sol-Gel Sefthymaria Sefthymaria; Rahmad Nuryanto; Taslimah Taslimah
Jurnal Kimia Sains dan Aplikasi Vol 18, No 3 (2015): Volume 18 Issue 3 Year 2015
Publisher : Chemistry Department, Faculty of Sciences and Mathematics, Diponegoro University

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (798.426 KB) | DOI: 10.14710/jksa.18.3.79-84

Abstract

Telah dilakukan penelitian mengenai pengaruh variasi chelating agent pada sintesis elektrolit padat NaMn2-xMgxO4 dengan metode sol-gel. Penelitian ini bertujuan untuk mengetahui pengaruh variasi asam (asam askorbat, asam sitrat dan asam maleat) sebagai chelating agent terhadap kristalinitas, ukuran kristal, konduktivitas dan morfologi dari material yang dihasilkan. Tahapan penelitian ini meliputi pencampuran reagen, evaporasi, pengeringan dan kalsinasi. Produk kalsinasi dikarakterisasi menggunakan XRD, multimeter dan SEM-EDS. Mineral penyusun elektrolit padat meliputi NaMnO2, MnO2 MgO dan Na2O. Kristalinitas terendah dan konduktivitas tertinggi dimiliki oleh produk yang menggunakan asam askorbat sebagai chelating agent, dengan nilai konduktivitas 1,91 x 10-4 Scm-1; ukuran kristal 26,09 nm dan ukuran aglomerasi 0,66 μm. Elektrolit padat NaMn2-xMgxO4 yang dihasilkan untuk variasi chelating agent asam askorbat memiliki formula spinel NaMn1,32Mg0,68O4.