Article Per Year (5 Year)
p-Index From 2020 - 2025
0.408
P-Index
This Author published in this journals
All Journal Jurnal Teknologi Jurnal Inovasi Teknologi Terapan
Abdallah, Fajar
Unknown Affiliation
Agriculture, Biological Sciences & Forestry Chemical Engineering, Chemistry & Bioengineering Civil Engineering, Building, Construction & Architecture Computer Science & IT Electrical & Electronics Engineering Mechanical Engineering

Published : 2 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 2 Documents
Search

 1 
Analisis Pemanfaatan Serat Resam Sebagai Bahan Komposit Untuk Bahan Pembuatan Ujung Joran Pancing Abdallah, Fajar; Rollastin, Boy; Harwadi, Harwadi
Jurnal Inovasi Teknologi Terapan Vol. 3 No. 1 (2025): Jurnal Inovasi Teknologi Terapan
Publisher : Politeknik Manufaktur Negeri Bangka Belitung

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.33504/jitt.v3i1.252

Abstract

Fishing has transformed from a traditional livelihood into an increasingly popular hobby among people, involving various age groups and locations. Fishing rods, as the main tool in the fishing process, function to catch fish by reducing the load and providing lifting power. This study aims to explore the use of resam fiber as an alternative material in making fishing rods, considering the limitations and high costs of graphite rods. The rod manufacturing process uses the Hand lay-up technique, where the resam fiber undergoes alkalization with 5% NaOH for 1, 2, and 3 hours, and variations in the number of fibers of 5, 10, and 15 strands. The results showed that specimens with 15 strands of fiber soaked for 2 hours produced the highest average tensile value of 44.6 MPa and the highest bending value of 57.6 MPa. This study shows the potential of resam fiber as a strong and affordable material for making fishing rods, providing a better alternative to graphite rods available on the market.
Komposit Berpenguat Serat Resam dengan Uji Tarik sebagai Material pada Pembuatan Joran Pancing Abdallah, Fajar; Rollastin, Boy; harwadi, harwadi
Jurnal Teknologi Vol 25, No 1 (2025): April 2025
Publisher : Politeknik Negeri Lhokseumawe

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.30811/teknologi.v25i1.6196

Abstract

This research aims to obtain the appropriate composition in the production of alternative materials for fishing rods with fiber-resin reinforcement, as well as to determine the tensile and bending test results for the alternative material to be used as fishing rods. This study uses a full factorial method to determine the number of spesimens to be made, with variations in fiber-resin composition: the number of fibers used is 5, 10, and 15 strands, with a resin-to-catalyst ratio of 50:1 and drying times of 1 hour, 2 hours, and 3 hours. Tensile strength tests were performed on 9 spesimens with 3 replications, and bending tests were conducted on 9 spesimens with 3 replications per spesimen, resulting in a total of 54 spesimens tested. Based on the best tensile test results, the spesimen with 15 strands of fiber soaked for 2 hours in a 5% NaOH solution achieved a tensile strength of 46.2 MPa, while the lowest tensile strength was obtained from the spesimen with 5 strands of fiber soaked for 2 hours, which was 19.9 MPa. The average tensile test results showed a maximum value of 38.4 MPa