Studi Awal Sintesis dan Karakterisasi Bi(Pb)-Sr-Ca-Cu-O dengan Penambahan Carbon Nanotube dan TiO2 Menggunakan Metoda Reaksi Padatan dan Proses Sintering Berulang [Preliminary Study Synthesis and Characterization of Bi(Pb)-Sr-Ca-Cu-O By Addition of Carbon Nanotube and TiO2 Using Solid Reaction Method and Recurrent Sintering Process] Syahfina, Rizki; Siswayanti, Bintoro; Yudanto, Sigit Dwi; Imaduddin, Agung; Suhada, Nurul; Amri, Fauzan; Harahap, Mukti Hamjah
Metalurgi Vol 32, No 3 (2017): Metalurgi Vol. 32 No. 3 Desember 2017
Publisher : Pusat Penelitian Metalurgi dan Material - LIPI

Bi1.6Pb0.4Sr2Ca2Cu3O10+δ with the addition of carbon nanotubes (CNT) and TiO2 have been synthesized using solid state reaction method with the repeated sintering process. 0.1 wt % of CNT and 5 wt% of TiO2 have been added to analyze the effect on the synthesizing of 2223 phases. The samples were analyzed using XRD (X-ray diffractometer) and SEM (Scanning Electron Microscopy). Based on the XRD results, 2223 and 2212 were formed. The addition of CNTs and TiO2 reduced the intensity of 2223 phases. This is due to the addition of CNTs and TiO2 as an impurity and prevent the formation of the phases. Also, the repeated sintering process led to the increase of 2223 phase, and the decrease of 2212 phase. However, the repeated sintering process in the B-CNT and B-TiO samples eliminates the impurities phase thus increasing the volume fraction 2223 and decreasing the volume fraction 2212. Based on morphological structure through SEM observation, the addition of CNT in the Bi(Pb)-2223 samples formed longer plates with large porosity spaces while the addition of TiO2 formed clumps on the Bi(Pb)-2223 morphological structure. However, the repeated sintering process improves the morphological structure of B-CNT and B-TiO becomes increasingly denser and the smaller porosity space.AbstrakTelah dilakukan sintesis Bi1,6Pb0,4Sr2Ca2Cu3O10+δ dengan penambahan CNT (carbon nanotube) dan penambahan TiO2 menggunakan metode reaksi padatan dengan proses sintering berulang. Penambahan CNT sebesar 0,1 %berat dan TiO2 sebesar 5 %berat dan sintering berulang dilakukan untuk mempelajari pengaruhnya terhadap pembentukan fasa 2223 beserta pengotornya, dan mempelajari perubahan morfologi Bi1,6Pb0,4Sr2Ca2Cu3O10+δ. Bi1,6Pb0,4Sr2Ca2Cu3O10+δ yang dibuat dianalisis dengan XRD (x-ray diffractometer) dan SEM (scanning electron microscopy). Berdasarkan hasil XRD, penambahan 0,1 %berat CNT dan TiO2 sebesar 5 %berat pada superkonduktor Bi(Pb)-2223 diketahui menghasilkan fasa 2223, fasa 2212, dan juga fasa pengotor. Namun proses sintering berulang mampu mengurangi fasa impuritas, meningkatkan fraksi volume 2223, serta menurunkan fraksi volume 2212. Berdasarkan pengamatan struktur morfologi melalui SEM, penambahan CNT pada superkonduktor Bi(Pb)-2223 membentuk serpihan memanjang dengan ruang porositas yang besar sedangkan penambahan TiO2 membentuk gumpalan pada struktur morfologi Bi(Pb)-2223. Proses sintering berulang mampu memperbaiki struktur morfologi B-CNT dan B-TiO menjadi semakin rapat dan ruang porositas yang semakin kecil.

PERGESERAN SUHU KRITIS SUPERKONDUKTOR Bi-Pb-Sr-Ca-Cu-O PADA MEDAN MAGNET TINGGI[The Shift In Critical Temperature Of Bi – Pb – Sr – Ca – Cu – O Superconductors In High Magnetic Field] Imaduddin, Agung; Yudanto, Sigit Dwi; Siswayanti, Bintoro; Hendrik, Hendrik
Metalurgi Vol 29, No 3 (2014): Metalurgi Vol.29 NO.3 Desember 2014
Publisher : Pusat Penelitian Metalurgi dan Material - LIPI

PERGESERAN SUHU KRITIS SUPERKONDUKTOR Bi-Pb-Sr-Ca-Cu-O PADA MEDAN MAGNETTINGGI. Pada penelitian ini dipelajari proses pembuatan pelet superkonduktor Bi-Sr-Ca-Cu-O sebagai dasarprekursor bahan pada kawat superkonduktor yang diberi doping unsur Pb untuk menggantikan Bi, dan dibuatdengan memakai metoda pencampuran basah. Sampel yang dibuat dianalisa dengan XRD (X-ray diffractometer),EDS (energy dispersive spectroscopy) dan juga hambatan jenis listrik (resistivity) pada suhu rendah dan padamedan magnet tinggi. Berdasarkan hasil XRD dab EDS, diketahui bahwa fasa yang terbentuk adalah fasa 2212,namun terlihat juga bahwa unsur C masih banyak tersisa di dalam sampel. Dari hasil pengukuran hambatan jenislistriknya, diketahui bahwa sampel ini memiliki suhu kritis awal superkonduktor (TC onset) sebesar 79K, dan suhukritis akhir (TC final) sebesar 48K. Pengukuran hambatan jenis listrik sampel terhadap suhu juga dilakukan padamedan magnet 2 dan 4 T. TC bergeser ke suhu yang lebih rendah akibat adanya medan magnet. Pergeseran TCjuga menunjukkan bahwa sampel ini memiliki fasa 2212. Pada suhu di atas 79K terlihat sifat semikonduktorpada sampel ini, yang menunjukkan masih banyaknya unsur pengotor yang bersifat semikonduktor. AbstractThis work studied the process of making bulk Bi-Sr-Ca-Cu-O superconducting materials as the precursor material of superconducting wire, which was given Pb doping to substitute Bi. The sampel was prepared using wet mixing method. Analyzed by XRD (X-ray diffractometer), EDS (energy dispersive spectroscopy) and electrical resistivity at low temperatures and high magnetic fields. Based on the results of XRD and EDS, it is known that it formed 2212 phase, but a lot of element of C still remains in the sampel. According to the results of resistivity measurement, it shows that this sampel has initial critical temperature (TC onset) at 79K, and final critical temperature (TC final) at 48K. The measurements of the resistivity were also carried out on the magnetic field of 2 and 4 T. TC shifts to lower temperatures due to the presence of a magnetic field. The shift of TC also indicates that the sample has phase of 2212. At temperatures above 79K, visible property of semiconductor appeared, which indicates there are many impurities that are semiconductors.

STUDI KONDUKTIVITAS ARUS BOLAK-BALIK MATERIAL Ca3Co2O6 Yudanto, Sigit Dwi
Metalurgi Vol 29, No 2 (2014): Metalurgi Vol.29 No.2 Agustus 2014
Publisher : Pusat Penelitian Metalurgi dan Material - LIPI

STUDI KONDUKTIVITAS ARUS BOLAK-BALIK MATERIAL Ca3Co2O6. Penelitian yang dilakukanbertujuan untuk membuat material yang mempunyai karakteristik sebagai material termoelektrik danmempelajari pengaruh suhu terhadap sifat konduktivitas arus bolak-balik material. Material Ca3Co2O6merupakan material yang mempunyai karakter sebagai material termoelektrik. Sintesis material Ca3Co2O6dilakukan dengan menggunakan metode reaksi padat. Bahan baku CaCO3 dan CoCO3 digerus denganmenggunakan planetary ball mill, kemudian dijadikan pelet dan disinter pada suhu 1000°C yang ditahan selama20 jam. Pola difraksi sinar-X menunjukkan bahwa fasa Ca3Co2O6 telah terbentuk, tetapi masih terdapat fasa lain,yaitu fasa CoO dan Co3O4. Penghalusan pola difraksi sinar-X dilakukan dengan menggunakan metode Rietvield.Penghalusan menghasilkan fraksi berat fasa, Ca3Co2O6 : CoO : Co3O4 = 71,28 : 22,12 : 6,6. Parameter kisiCa3Co2O6 hasil penghalusan adalah a = 9,0719 Å, dan c = 10,3755 Å. Massa jenis Ca3Co2O6 berdasarkanperhitungan adalah 4,501 gr/cm3. Konduktivitas arus bolak-balik Ca3Co2O6 tertinggi sebesar 1,3218 x 10-3 S/cmpada suhu 400°C.

PREPARASI, SINTESIS Dan KARAKTERISASI MATERIAL CaMnO3 [Preparation, Synthesis and Characterization of CaMnO3 Material] Yudanto, Sigit Dwi
Metalurgi Vol 30, No 2 (2015): Metalurgi Vol.30 No.2 Agustus 2015
Publisher : Pusat Penelitian Metalurgi dan Material - LIPI

CaMnO3 merupakan senyawa oksida dengan potensi aplikasi yang cukup luas, salah satunya yaitu thermoelectric. Sintesis CaMnO3 menggunakan bahan baku gugus karbonat berhasil dilakukan melalui metode reaksi padatan. Sintesis diawali dengan pencampuran kedua bahan baku secara stoikiometri dan dilanjutkan dengan penggerusan, kalsinasi, peletisasi dan penyinteran pada variasi suhu 1100, 1200 dan 1250oC. Pengamatan XRD menunjukkan kecenderungan pola difraksi yang sama pada tiap temperatur serta menunjukkan terbentuknya fasa tunggal CaMnO3. Nilai parameter kisi kristal CaMnO3 hasil penghalusan menggunakan metode Rietvield dengan sistem kristal orthorombic dan space group Pnma adalah a = ~5,26 Å; b = ~7,44 Å; dan c = ~5,27 Å. Mikrostruktur yang ditampilkan oleh mikroskop elektron menunjukkan bahwa semakin tinggi suhu, ukuran butir akan semakin kecil dan kerapatan butir semakin meningkat. AbstractCaMnO3 is metal oxide compound with wide potential applications i.e thermoelectric. Synthesis of CaMnO3using carbonat groups material has been succesfully carried out through solid state reaction method. It isstarted by mixing of both CaCO3 and MnCo3 raw materials at a stoichimometri composition and followed bygrinding, calcinating, pelletizing and sintering at various temperatures of 1100 oC, 1200 oC and 1250 oC. XRaydiffraction results for all specimens show similar pattern at each temperature condition, namely theformation of single phase CaMnO3. Crystal lattice from refinement with Rietviled method that has beenidentified in orthorombic crystal system and Pnma space group was a = ~5,26 Å; b = ~7,44 Å; dan c = ~5,27Å. Microstructure of CaMnO3 phase shows that increasing temperature will increase grain density and reducegrain space.

ANALISIS STRUKTUR DAN PEMODELAN KRISTAL CALCIUM MANGANESE OXIDE (CaMnO3) Yudanto, Sigit Dwi; Yuswono, Yuswono
Metalurgi Vol 29, No 1 (2014): Metalurgi Vol.29 No.1 April 2014
Publisher : Pusat Penelitian Metalurgi dan Material - LIPI

ANALISIS STRUKTUR DAN PEMODELAN KRISTAL CALCIUM MANGANESE OXIDE (CaMnO3).Material CaMnO3 mempunyai sifat magnet dan listrik yang baik sehingga dapat diaplikasikan sebagai materialmagnetoresistan dan termoelektrik. Sintesis Ti doping calcium manganese oxide (CaMnO3) dilakukan denganmenggunakan metode mechanical milling yang dilanjutkan dengan reaksi sintering. Sintesis dilakukan untukmengetahui pengaruh doping Ti sebesar 0,2 %berat terhadap struktur kristal CaMnO3. Analisis struktur Tidoping calcium manganese oxide (CaMnO3) dari hasil XRD (X-ray diffraction) menggunakan GSAS (generalstructure analysis system) dan bertujuan untuk mengetahui struktur kristal yang terbentuk dari hasilpendopingan. Analisis menggunakan model struktur kristal ortorombik (Pnma) berdasarkan hasil klarifikasi poladifraksi dengan ICDD (International Centre for Diffraction Data). Dari penghalusan pola difraksi sinar-Xdiperoleh parameter kisi a= 5,3010 Å, b= 7,4823 Å dan c= 5,2837Å. Nilai χ 2= 1,029 dan WRp = 4,96%. Massajenis hasil perhitungan adalah 4,488 gr/cm3.

Title

Found 5 Documents
Search

Abstract

Abstract

Abstract

Abstract

Abstract

Title Search

Found 5 Documents Search

Abstract

Abstract

Abstract

Abstract

Abstract

Title

Found 5 Documents
Search