EFEK PENAMBAHAN NANOCLAY TERHADAP SIFAT MEKANIK DARI BLENDING PET/PP Santoso, Heru; Dwigustono, Gatot
Jurnal Spektra Vol 16, No 1 (2015): Spektra: Jurnal Fisika dan Aplikasinya
Publisher : Jurnal Spektra

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

AbstrakDengan berkembangnya kemampuan rekayasa material, polimer blend menjadi salah satu metode untuk merekayasa material polimer yang cukup penting karena aplikasinya yang cukup luas. Dalam penelitian ini telah dilakukan proses blending (pencampuran) antara material polimer polietilena tereftalat (PET) dengan polipropilena (PP) dengan bantuan kompatibilizer PP-g-MA. Proses pencampuran menggunakan mesin ekstrusi jenis single screw dengan setting parameter suhu 210oC, 230oC, 265oC dan 275oC pada putaran 50 rpm. Pengaruh penambahan nano pada sistem campuran PET/PP/PP-g-MA terhadap sifat mekanik dilakukan dengan menambahkan nanoclay dengan konsentrasi 1, 3, 5, 7 dan 10 % (rasio berat). Hasil pencampuran PET/PP/PP-g-MA dan penambahan nanoclay dikarakterisasi sifat mekaniknya yaitu tensile strength, impact strength dan sifat termalnya dengan DSC, TGA serta morfologinya dengan SEM. Pada penelitian ini didapatkan nilai optimal dari penambahan kompatibilizer PP-g-MA pada konsentrasi 7% (rasio berat) dengan nilai kuat tarik sebesar 29,25 MPa. Penambahan nanoclay dalam sistem campuran PET/PP/PP-g-MA pada konsentrasi 7 % (rasio berat) berpengaruh terhadap sifat mekanik, termal dan sifat morfologinya. Semakin besar penggunaan nanoclay menyebabkan sifat E-modulus meningkat, kuat tarik menurun, elongasi menurun dan kekuatan impak juga menurun. Kekuatan mekanik terbesar dicapai pada penambahan nano nanoclay 1 % (rasio berat) dan nilai E-modulus terbesar pada penggunaan nano nanoclay 10% (rasio berat). Sifat termal pada penambahan nano clay didapatkan kecenderungan meningkatkan kestabilan termal dan menurunnya derajat kristalinitas PP campuran PET/PP/PP-g-MA/nanoclay. AbstractAdvancement of material engineering makes polymer blend as an important polymer material engineering method among other methods because of its wide applications. In this research, blending between polyethylene terephthalate (PET) and polypropylene (PP) polymer materials using compatibilizer PP-g-MA was produced. Single-screw extrusion machine with temperature parameters of  210oC, 230oC, 265oC and 275oC at 50 rpm was used during mixing process. The influence of nano supplementation on mixture system of PET/PP/PP-g-MA on mechanical properties was carried out by adding nano clay of 1, 3, 5, 7 and 10% (weight ratio). The mixing result of PET/PP/PP-g-MA and supplementation of nano clay was characterized mechanically (tensile strength, impact strength), thermally (DSC, TGA), and morphologically (SEM). Optimal value of compatibilizer PP-g-MA supplementation was obtained at concentration of 7% (weight ratio) with tensile strength of 29.25 MPa. Supplementation of nano clay into the system of 7% (weight ratio) influenced their mechanical, thermal, and morphological properties. The higher the ratio of nano clay, the higher the E-modulus property, the lower the tensile strength, the lower the elongation, and the lower the impact strength. The highest mechanical strength was obtained at nano clay supplementation of 1% (weight ratio) and the highest E-modulus value was obtained at nano clay supplementation of 10% (weight ratio). Thermal properties of nano supplementation tends to increase thermal stability and decrease crystallinity of PP mixed with PET/PP/PP-g-MA/nano clay.Keywords: blending PET/PP, compatibilizer PP-g-MA, single screw extrusion, nano clay.

Page 12 of 12 | Total Record : 111

 8   9   10   11   12 

Filter by Year

2010 2015


Reset
Filter By Issues
All Issue Vol 16, No 3 (2015): Spektra: Jurnal Fisika dan Aplikasinya Vol 16, No 2 (2015): Spektra: Jurnal Fisika dan Aplikasinya Vol 16, No 1 (2015): Spektra: Jurnal Fisika dan Aplikasinya Vol 15, No 2 (2014): Spektra: Jurnal Fisika dan Aplikasinya Vol 15, No 1 (2014): Spektra: Jurnal Fisika dan Aplikasinya Vol 14, No 2 (2013): Spektra: Jurnal Fisika dan Aplikasinya Vol 14, No 1 (2013): Spektra: Jurnal Fisika dan Aplikasinya Vol 13, No 1 (2012): Spektra: Jurnal Fisika dan Aplikasinya Vol 12, No 2 (2011): Spektra: Jurnal Fisika dan Aplikasinya Vol 11, No 1 (2011): Spektra: Jurnal Fisika dan Aplikasinya Vol 9, No 2 (2010): Spektra: Jurnal Fisika dan Aplikasinya More Issue