Desulfurisasi Batubara Menggunakan Larutan Ekstrak Belimbing Wuluh (Everrhoa Bilimbi L) Amin, Muhammad; Birawidha, David Candra; Isnugroho, Kusno; Hendronursito, Yusuf; Muttaqqi, Muhammad Al; Prilitasari, Nurbaiti Marsas
Jurnal Presipitasi : Media Komunikasi dan Pengembangan Teknik Lingkungan Vol 16, No 2 (2019): Juli 2019
Publisher : Universitas Diponegoro

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (334.292 KB) | DOI: 10.14710/presipitasi.v16i2.44-52

Abstract

Desulphurization process can improve the quality of coal and reduce the environmental pollution. In this study, the method used for desulphurization process was a leaching method using wuluh starfruit extract as a leaching agent. Starfruit extract obtained by grinded, filtered and extracted the starfruit solution. Coal was crushed by using a grinding ball mill, sifted to obtain samples of 80 mesh, 120 mesh, and 150 mesh. Coal was added with starfruit extract, heated on a hotplate stirrer at a temperature of 110oC, 300 rpm of stirring speed and 3, 4 , 5 hours of leaching time. Leachate solution were analyzed using XRF test. The results of the study showed that 80, 120 and 150 mesh could produce 1.777%, 1.556% and 1.053% of sulfur, respectively. Maximum decrease of sulfur occurred in 150 mesh with 5 hours of leaching time which could reach 0.261% of concentration. Ash content also could decreased from 11.43% to 6.18% and fixed carbon content from 42.15% rose to 51.33%. The desulphurization process using starfruit extract was influenced by the grain size of the coal and the contact time of leaching. The finer the grain size of the coal and the longer the leach contact time, the smaller the sulfur content obtained in the coal after the desulfurization process was carried out
Processing of granite quarry solid waste into industrial high silica materials using leaching process with HCl concentration variation Hendronursito, Yusup; Amin, Muhammad; Sumardi, Slamet; Marjunus, Roniyus; Clarasati, Frista; Birawidha, David Candra; Muttaqqi, Muhammad Al; Isnugroho, Kusno
Jurnal Riset Teknologi Pencegahan Pencemaran Industri Vol. 11 No. 2 (2020)
Publisher : Balai Besar Standardisasi dan Pelayanan Jasa Pencegahan Pencemaran Industri

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.21771/jrtppi.2020.v11.no2.p43-50

Abstract

This study was aimed to increase granite's silica content using the leaching process with HCl concentration variation. The granite used in this study came from Lematang, South Lampung. This study aims to determine the effect of variations in HCl concentration, particle size, and rotational speed on the crystalline phase and chemical elements formed in the silica product produced from granite. The HCl concentration variations were 6.0 M, 7.2 M, 8.4 M, and 9.6 M, the variation in particle size used was 270 and 400 mesh. Variations in rotational speed during leaching were 500 and 750 rpm. Granite powder was calcined at 1000 ÂșC for 2 hours. Characterization was performed using X-Ray Fluorescence (XRF), X-Ray Diffraction (XRD), and Inductively Coupled Plasma-Optical Emission Spectroscopy (ICP- OES). The results showed that the silica content increased with increasing HCl concentration, the finer the particle size, and the higher the rotational speed. XRF analysis showed that the silica with the highest purity was leached with 9.6 HCl with a particle size of 400 mesh and a rotational speed of of 750 rpm, which was 73.49%. Based on the results above, by leaching using HCl, the Si content can increase from before. The XRD diffractogram showed that the granite powder formed the Quartz phase.