Penelitian pengaruh perbandingan rss dengan SBR dan PBN terhadap ketahanan sobek dan kekerasan kompon talang karet Asrilah Asrilah; Siti Rochani
Majalah Kulit, Karet, dan Plastik Vol 10, No 20 (1995): Majalah Barang Kulit, Karet, dan Plastik
Publisher : Center for Leather, Rubber, and Plastic Ministry of Industry, Indonesia

The objective of this research is to know the influence variation in application RSS, SBR and PBN of Rubber gutter Compound to physical properties in tear resistance and hardness. Rubber gutter Compound is made from natural Rubber (RSS) wich be mixed by sintetics Rubber (RSS) and addition of ingredients such as : softener, activator filler antioxidant, accelerator and vulcanizing agent. It should be carried out using base formula by varying RSS/SBR 40/ 60; 50/50; 60;40 part and PBN 1; 1,5 and 2 part. Statistically prove that variation in application RSS/SBR and PBN influenced physical properties of the result test. The application RSS/SBR 60/40 part PBN 1,5 part will give the best compound with the tear resistance 11,05N/mm2 and hardness 72,33 Shore A. INTISARI Penelitian ini bertujuan untuk mengetahui pengaruh RSS dengan SBR dan PBN terhadap ketahan sobek dan kekrasan kompon talang karet. Kompon talang karet dibuat dari karet alam dan karet sintetis dengan ditambahkan bahan- bahan pembantu seperti bahan pelunak, pengaktif, pengisi anti oksidan, pencepat, dan zat pemvulkanisasi. Pembuatan kompon tersebut dikerjakan dengan formulasi sebagai berikut : RSS/SBR : 40/60; 50/50; 60/40 bagian PBN : 1; 1,5 ; 2 bagian. Setelah diuji ternyata secara perhitungan statistik variasi penggunaan RSS/SBR 60/40 bagian PBN berpengaruh terhadap sifat-sifat fisis kompon tersebut. Kompon yang paling baik sifat-sifat fisisnya adalah kompon yang menggunakan RSS/SBR 60/40 bagian dari PBN 1,5 bagian dengan hasil uji ketahanan sobek 11,05N/mm2 dan kekerasan 172,33 Shore A.

Pengaruh variasi filler CaCO3 terhadap sifat fisis tegangan putus dan perpanjangan putus kompon sol karet untuk sepatu kanvas Asrilah Asrilah
Majalah Kulit, Karet, dan Plastik Vol 9, No 17 (1994): Majalah Barang Kulit, Karet, dan Plastik
Publisher : Center for Leather, Rubber, and Plastic Ministry of Industry, Indonesia

The objective of this research is to know the influence of calcium carbonate as filler of the physical properties tensile strength and elongation at break rubber sole for canvas shoes. Rubber sole compound is made from natural rubber and addition of ingredient such as : filler, anti oxidant, accelerator, softener, activator and vulcanizing agent. It should be carried out using base formula by variying calcium carbonate 65, 70, 75, 80, 85 and 90 part. Statistically prove that calcium carbonate influenced physical properties of the result test. The application calcium carbonate 65 – 80 part will give the best compound with the tensile strength 13,93 N/mm2 and elongation at break 424,77%, fulfilled the specification of SII 1406 – 85 “Sepatu kanvas untuk olah raga”. INTISARI Penelitian ini bertujuan untuk mengetahui pengaruh filler CaCO3 terhadap sifat fisis tegangan putus dan perpanjangan putus kompon sol karet untuk sepatu kanvas. Kompon sol karet tersebut dibuat dari karet alam, ditambah berapa bahan pembantu seperti, bahan pengisi, anti oksidan, bahan pencepat, bahan pelunak, pengaktif dan pemvulkanisasi, dengan formula tertentu. Jumlah filler CaCO3 kompon dibuat bervariasi yaitu 65, 70, 75, 80, 85 dan 90 bagian. Perhitungan statistic menunjukkan bahwa calcium carbonat berpengaruh terhadap sifat fisika yang diuji. Hasil uji terbaik dengan jumlah calcium carbonat antara 65 – 80 bagian, dengan nilai tegangan putus 13,93 N/mm2 dan nilai perpanjangan putus 424,77% memenuhi persyaratan SII 1406 – 85 “Sepatu kanvas untuk olah raga”.

Pengaruh anti oksidan phenyl beta naphtylamine (PBN), dan variasi rss dengan SBR terhadap sifat fisika kompon talang karet Siti Rochani; Asrilah Asrilah
Majalah Kulit, Karet, dan Plastik Vol 12, No 25 (1998): Majalah Barang Kulit, Karet, dan Plastik
Publisher : Center for Leather, Rubber, and Plastic Ministry of Industry, Indonesia

The aim of the research was to find some important characteristics of rubber gutter compound such as tensile strength, elongation at break, and constant deflection because of adding Phenyl Beta Naphtylamine on it. Rubber gutter compound was made from mixing of natural (RSS) and synthetic rubber (SBR) and some aditives such Zink Oxide, Stearic Acid, Napthenic Oil, HAF black, Phenyl Beta Naphtylamine, Mercapto Benz Thiazol Disulfide, Diphenyl Guanidine and Sulphur. Three compositions of RSS/SBR and Phenyl Beta Naphtylamine were used in the research, namely 40/60; 50/50; 60/40, and 1 : 1,5 ; 2 respectively. A statistical procedure was used to analyze the data of the physical characteristic of rubber gutter compound produced. The results were compared to the data of the physical characteristic of rubber gutter compound produced. The results were compared to the physical strength of rubber gutter available in the market. From the statistical analyses they denoted that the levels of Phenyl Beta Naphtylamine gave significant effects on elongation at break and constant deflection however there was no effect on tensile strength. The composition levels of RSS /SBR could produce compounds which were significant difference in the tensile strength, elongation at break and constant deflection. Compounds resulted from this research had better tensile strength and elongation compared to rubber gutter available in the market. INTISARI Penelitian ini bertujuan untuk mendapatkan karakteristik kompon talang karet terutama sifat-sifat penting seperti tegangan putus, perpanjangan putus dan pampat tetap, karena penambahan anti oksidan Phenyl Beta Naptylamine. Kompon talang karet dibuat dari campuran karet alam (RSS) dan karet sintetis (SBR) dengan enambahan bahan pembantu yaitu Zink Oksida, Asam Stearat, Naphtenic Oil, HAF black, Phenyl Beta Naphtylamine, Mercapto Benz Thiazol Disulphyte, Diphenyl Guanidine dan Sulfur. Campuran RSS dengan SBR di variasi dengan perbandingan 40/60; 50/50; dan 60/40, sedang Phenyl Beta Naphtylamine yang ditambahkan adalah 1; 1,5; dan 2 bagian. Kompon yang didapatkan, setelah diuji, hasilnya dianalisa dengan perhitungan statistik, serta dibandingkan dengan hasil uji talang karet dari pasaran. Dari hasil analisa statistik variasi Phenyl Beta Naphtylamine berpengaruh nyata pada sifat perpanjangan putus dan pampat tetap, sedangkan pada sifat tegangan putus tidak berbeda nyata. Variasi pencampuran RSS dengan SBR memberikan perbedaan yang nyata pada sifat fisis tegangan putus, perpanjangan putus dan pampat tetap. Dibandingkan dengan beberapa contoh yang diambil dari pasaran, kompon hasil penelitian mempunyai tegangan putus dan perpanjangan putus yang lebih baik.

Penelitian konversi hubungan timbal balik antara kulit kambing segar menjadi kulit garaman dan kulit pikel sebagai produk perdagangan A Buchori; Rosma Radja Gukguk; Asrilah Asrilah
Majalah Kulit, Karet, dan Plastik Vol 14, No 26 (1999): Majalah Barang Kulit, Karet, dan Plastik
Publisher : Center for Leather, Rubber, and Plastic Ministry of Industry, Indonesia

The aim of this research is to determine the conversion of value goatskin to knowtge mutual relation ship initiating betwen fresh goatskin, preserevation goatskin and pickle goatskin. The raw material used in this research in the form of primary data fresh goatskin and salted goatskin come frome of butchering animal and leather collector/preservators in Ypgyakarta Special Region (DIY) and secondary data from IRDLAI tanning Process Labolators in the from of second data of pickle goatskin come from salted foatskin. Data analvesed using statisik method with mean calculation and deviation standaerd. The result of the research could to know several conversion of goatskin possobilility can used in the Indonesian leather Industry ad commersial commondity. INTISARI Penelitian ini bertujuan untuk menentukan harga konversi kulit kambing sebafai alat untuk mengetahui hubungan timbale balik antara kulit kambing segar menjadi kulit kambing awetan dan kulit kambing pikel. Materi yang digunakan dalam penelitian ini adalah berupa data primer kulit kambing segar dan kulit kambing awet garam yang berasal dari rumah pemotongan hewan dan pengumpul/pengawet kulit di Daerah Istimewa Yogyakarta (DIY) dan data sekunder dari laboratorium proses penyamajab BBKKP berupa data luas kulit kambing pikel yang berasal dari kulit garaman. Analisis data menggunakan metode statistic dengan menghitung mean (rata-rata) dan standart deviasi. Dari hasil penelitian dapat diketahui konversi kulit kambing yang kemungkinan digunakabn industry kulit di Indonesia sebagai produk perdagangan.

Penelitian pengaruh variasi china clay dan naphthenic oil terhadap perpanjangan tetap dan tegangan putus kompon karet untuk lis pintu almari es A Buchori; Asrilah Asrilah
Majalah Kulit, Karet, dan Plastik Vol 12, No 24 (1997): Majalah Barang Kulit, Karet, dan Plastik
Publisher : Center for Leather, Rubber, and Plastic Ministry of Industry, Indonesia

The aim of this research is to know the influence of filer china clay naphthenic oil to the physical properties of permanent set and tensile strength rubber compound for refrigerator gasket. It makes from natural rubber ( pale crepe ) and synthetic rubber (SBR 1502 ) as raw material with addition of ingredients such as : softener, activator, filler, antioxidant, accelerator, coloring and vulcanizing agent. It should be carried out using base formula by varying china clay : 30; 40 ; and 50 parts and naphthenic oil : 5,0 ; 7,5 and 10 parts for 9 compound then should be tested their physical properties permanent set and tensile strength. The result of the test statistically prove that china clay and naphthenic oil influence the physical properties for permanent set by china clay 30 parts and naphthenic oil 5 parts, the value 1,24%, for tensile strength by china clay 50 parts and naphthenic oil 5 parts, the value 102,6081 Kg/Cm2. INTISARI Penelitian ini bertujuan untuk mengetahui pengaruh bahan pengisi china clay dan naphthenic oil sebagai bahanpelunak terhadap sifat fisis perpanjangan tetap dan tegang putus kompon lis pintu almari es. Kompon karet untuk lis pintu almari es fibuat dari bahan baku karet alam ( pale crepe )dan sintesis ( SBR 1502 ) ditambah dengan bahan pembantu antara lain : bahan pelunak, pengaktif, pengisi, antioksidan, penepat, pewarna dan zat pemvulkanisasi china clay : 30 ; 40 dan 50 bagian dan apththenic oil : 5,0 ; 7,5 dan 10 bagian. Didapat 9 kompon dan diuji sifat- sifat fisis perpanjang tetap dan tegang putus. Perhitungan statistic menunjukkan bahwa china clay dan naphthenic oil berpengaruh terhadap sifat fisis yang diuji. Hasil terbaik untuk perpanjang tetap adalah jumlah china clay 30 bagian dan naphthenic oil bagian dengan nilai 1,24%, untuk tegangan putus tertinggi jumlah china clay 50 bagian dengan naphthenic oil 5 bagian dengan nilai 102,6081 Kg/Cm2.

Penelitian pengaruh naphthenic oil dan HAF black terhadap sifat pampat tetap pada kompon lis kaca mobil Abuchori Abuchori; Asrilah Asrilah; Sri Brataningsih Puji Lestari
Majalah Kulit, Karet, dan Plastik Vol 11, No 21 (1996): Majalah Barang Kulit, Karet, dan Plastik
Publisher : Center for Leather, Rubber, and Plastic Ministry of Industry, Indonesia

The objective of the research is to know the influence of naphthenic oil and HAF black properties of the compression set by constant load and constant deflection rubber strip compound. Rubber strip compound is made from natural rubber (RSS) and synthetic rubber (SBR 1502) with the addition of ingredient such as softener, activator, filler, anti oxidant, accelerator and vulcanizing agent. It should be carried out using base formula by varrying naphtenic oil 3; 5 and 7 parts and carbon black 45; 50 and 55 parts for 9 compounds, then it should be tested their physical properties, compression set by constant load and constant deflection. The test is actually able to fullfill the specification of SII 1999-86 “Lis karet kaca kendaraan bermotor”. The result of the test statistically prove that naphthenicc oil and HAF black influence the physical properties. INTISARI Penelitian ini bertujuan untuk mengetahui pengaruh naphthenic oil and HAF black terhadap sifat pampat tetap dengan constant load dan constant deflection kompon lis kaca mobil. Lis kaca mobil dibuat dari campuran bahan baku karet alam (RSS) dan karet sintetik (SBR 1502) dengan ditambahkan bahan-bahan pembantu (ingridient) seperti bahan pelunak, pengaktif, pengisi, anti oksidant, percepat dan zat pemvulkanisasi dengan formula dasar dibuat kompon lis kaca mobil dengan memvariasikan bagian naphthenic oil : 3; 5 dan 7 bagian serta carbon black : 45; 50 dan 55 bagian. Didapat 9 kompon dan diuji sifat-sifat fisi pampat tetap menggunakan constant load dan constant deflextion hasil uji memenuhi persyaratan SII 1999-86 “Lis kaca kendaraan bermotor”. Perhitungan statistik menunjukkan bahwa naphthenic oil dan carbon black berpengaruh terhadap sifat fisis yang diuji.

Title

Found 6 Documents
Search

Abstract

Abstract

Abstract

Abstract

Abstract

Abstract

Title Search

Found 6 Documents Search

Abstract

Abstract

Abstract

Abstract

Abstract

Abstract

Title

Found 6 Documents
Search