Search

 1 
PENGARUH MALEATED NATURAL RUBBER (MNR) TERHADAP SIFAT MEKANIK VULKANISAT KARET DENGAN FILLER ARANG AKTIF TEMPURUNG KELAPA Popy Marlina; Hari Adi Prasetya
Jurnal Dinamika Penelitian Industri Vol 31, No 1 (2020): JURNAL DINAMIKA PENELITIAN INDUSTRI
Publisher : Balai Riset dan Standardisasi Industri Palembang

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.28959/jdpi.v31i1.6016

Abstract

Penelitian ini bertujuan memanfaatkan limbah tempurung kelapa sebagai bahan pengisi alternative vulkanisat karet. Peningkatan karakteristik vulkanisat karet yang dihasilkan, dilakukan dengan cara menambahkan bahan penghubung maleated natural rubber (MNR) yang akan berperan sebagai material penghubung, antara bahan pengisi arang tempurung kelapa yang bersifat polar dan karet alam yang non polar. Penelitian dilakukan dalam skala laboratorium dengan faktor perlakuan perbandingan jumlah bahan pengisi arang aktif tempurung kelapa (ATK) dan carbon black (CB) 0/45; 22,5/22,5; 45/0 phr dan waktu penyimpanan 1 hari, 2 hari, dan 3 hari, pengulangan setiap perlakuan sebanyak 3 (tiga) kali. Karakteristik arang tempurung kelapa yang diamati kadar karbon terikat hasil aktivasi arang aktif tempurung kelapa dan perubahan sifat mekanik vulkanisat karet meliputi kekerasan, tegangan putus dan perpanjangan putus diamati sebelum dan sesudah pengusangan. Kadar karbon terikat hasil penelitian ini sebesar 80%, sesuai dengan standar SNI 06-3730-1995, kualitas arang aktif minimal 65%. Nilai kekerasan, tegangan putus, dan perpanjangan putus, tidak mengalami perubahan signifikan sebelum dan sesudah pengusangan dengan penambahan maleated natural rubber (MNR).
CHARACTERISTICS OF RUBBER SHEET WITH RAW MATERIAL OF COMPOSITE MODIFICATIONS - LATEX Popy Marlina; Hari Adi Prasetya
Jurnal Dinamika Penelitian Industri Vol 28, No 2 (2017): JURNAL DINAMIKA PENELITIAN INDUSTRI
Publisher : Balai Riset dan Standardisasi Industri Palembang

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (462.809 KB) | DOI: 10.28959/jdpi.v28i2.3081

Abstract

Natural starch can be made into modified starch with the desired properties or as needed. Composite of starch and natural rubber for the made of rubber sheets as an alternative to reduce the use of natural rubber in large quantities. The research aimed to study the characteristics of sheets rubber with composite modified starch - latex. The experimental research used non Factorial Completely Randomized Design and each treatments was replicated three times. Single factor of starch and latex modification ratio (Treatment A Starch modification: latex = 1: 1 (500 ml: 500 ml, Treatment B Starch modification:latex = 1:2 (500 ml: 1000 ml and Treatment C Starch modification:latex = 2:1 (1000 ml: 500 ml)). The parameters were plasticity (Po), plasticity resistance index (PRI), mooney viscosity and dirt content. Results showed that the comparison treatment of starch and latex modifications have a influence on the characteristics of sheet rubber meet the quality requirements of Standard Indonesian Rubber (SIR) 20 SNI 06-1903-2000 and standard quality commercial sheets rubber with charactheristics plasticity (Po), plasticity resistance index (PRI), mooney viscosity and dirt content.
KOMPOSIT KARET ALAM DAN NANOSILIKA SEKAM PADI TERHADAP SIFAT MEKANIK DAN REOLOGI VULKANISAT KARET Popy Marlina; Hari Adi Prasetya
Jurnal Dinamika Penelitian Industri Vol 30, No 1 (2019): JURNAL DINAMIKA PENELITIAN INDUSTRI
Publisher : Balai Riset dan Standardisasi Industri Palembang

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (460.038 KB) | DOI: 10.28959/jdpi.v30i1.5094

Abstract

Nanosilika sekam padi dapat digunakan sebagai bahan pengisi alternatif dalam pembuatan vulkanisat karet.  Penelitian ini bertujuan untuk mengetahui pengaruh nanosilika sekam padi terhadap sifat mekanik dan reologi vulkanisat karet dan dibandingkan dengan bahan pengisi carbon black pada pembuatan vulkanisat karet. Pengaruh konsentrasi nanosilika sekam padi (10, 20, 30, 40 dan 50 phr) pada masing- masing konsentrasi terhadap kekerasan, pampatan tetap, modulus 300%, modulus torsi, laju pemasakan optimum, dan waktu scorch. Penelitian eksperimental menggunakan Rancangan Acak Lengkap non Faktorial dan setiap perlakuan diulang sebanyak tiga kali.  Hasil pengujian mekanis dan reologi  menunjukkan tren dan tidak ada perbedaan nilai yang signifikan antara nanosilika sekam padi dan carbon black yang digunakan sebagai bahan pengisi. Perlakuan terbaik diperoleh pada konsentrasi nanosilika sekam padi 30 phr, dan konsentrasi carbon black 40 phr.  Vulkanisat karet dengan bahan pengisi carbon black menunjukkan kekerasan, modulus 300%, modulus torsi yang lebih tinggi, namun laju pemasakan optimum, pampatan tetap, dan waktu scorch lebih rendah dari pada  nanosilika sekam padi. Nanosilika sekam padi dapat menjadi pengganti carbon black yang baik untuk produk-produk karet dengan biaya dan pampatan tetapnya dipersyaratkan.