Article Per Year (5 Year)
p-Index From 2020 - 2025
0
P-Index
This Author published in this journals
All Journal Jurnal Keramik dan Gelas Indonesia Jurnal Keramik dan Gelas Indonesia
Toni Kristiantoro
Pusat Penelitian Elektronika dan Telekomunikasi – LIPI
Chemical Engineering, Chemistry & Bioengineering Chemistry Civil Engineering, Building, Construction & Architecture Electrical & Electronics Engineering Materials Science & Nanotechnology

Published : 2 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 2 Documents
Search

 1 
Characterization of Magnetic and Density Properties on Barium Ferrite with MnO2 Addition Ratih Resti Astari; Handoko Setyo Kuncoro; Didit Nur Rahman; Toni Kristiantoro
Jurnal Keramik dan Gelas Indonesia Vol 26, No 1 (2017): Jurnal Keramik dan Gelas Indonesia
Publisher : Balai Besar Keramik

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (3276.338 KB) | DOI: 10.32537/jkgi.v26i1.3912

Abstract

The addition of MnO2 in synthesis of barium ferrite magnet were prepared by powder metallurgy method with variation formula of MnO2 0%, 0.1%, 0.2%, 0.3%, 0.5% and 1% sintered at 1175 ºC. Material characterization includes X-Ray Diffraction (XRD), Scanning Electron Microscope (SEM) and permagraph were employed to investigate the effect of MnO2 addition to magnetic properties and sample density. Hysteresis curve using permagraph showed that the addition of MnO2 have an effect on the increasing of magnetic properties and density. Remanence induction (Br), coercivity (Hc) and density (ρ) reached the maximum value of 1.36 kG, 2.757 kOe and 4.29 g/cm3  respectively  on different formula MnO2. The best value of MnO2 addition could be concluded on the addition MnO2 of 0.3% with Br = 1.36 kG, Hc = 2.683 kOe, and ρ = 4.29 g/cm3. The XRD results showed the formed of barium ferrite phase in the sintered sample at 1175ºC. While the SEM result revealed that the addition of MnO2 affected the density of barium ferrite particles.
Characterization of Magnetic and Density Properties on Barium Ferrite with MnO2 Addition Ratih Resti Astari; Handoko Setyo Kuncoro; Didit Nur Rahman; Toni Kristiantoro
Jurnal Keramik dan Gelas Indonesia Vol 26, No 1 (2017): Jurnal Keramik dan Gelas Indonesia
Publisher : Balai Besar Keramik

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.32537/jkgi.v26i1.3912

Abstract

The addition of MnO2 in synthesis of barium ferrite magnet were prepared by powder metallurgy method with variation formula of MnO2 0%, 0.1%, 0.2%, 0.3%, 0.5% and 1% sintered at 1175 ºC. Material characterization includes X-Ray Diffraction (XRD), Scanning Electron Microscope (SEM) and permagraph were employed to investigate the effect of MnO2 addition to magnetic properties and sample density. Hysteresis curve using permagraph showed that the addition of MnO2 have an effect on the increasing of magnetic properties and density. Remanence induction (Br), coercivity (Hc) and density (ρ) reached the maximum value of 1.36 kG, 2.757 kOe and 4.29 g/cm3  respectively  on different formula MnO2. The best value of MnO2 addition could be concluded on the addition MnO2 of 0.3% with Br = 1.36 kG, Hc = 2.683 kOe, and ρ = 4.29 g/cm3. The XRD results showed the formed of barium ferrite phase in the sintered sample at 1175ºC. While the SEM result revealed that the addition of MnO2 affected the density of barium ferrite particles.