Kualitas Glulam Samama dengan Kombinasi Kayu Mangium dan Mahoni (The Quality of Samama Glulam and Its Combination with Mangium and Mahogany Wood) Tekat D Cahyono; Fauzi Febrianto; Syarif Ohorella
Jurnal Ilmu dan Teknologi Kayu Tropis Vol 15, No 1 (2017): Jurnal Ilmu dan Teknologi Kayu Tropis
Publisher : Masyarakat Peneliti Kayu Indonesia

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (357.544 KB) | DOI: 10.51850/jitkt.v15i1.351

Abstract

Previous study on several types of samama glulam had shown the MOE and MOR which is not meet JAS 2007. The recent study addressed the glulam construction from samama wood combined with two commercial woods to improve the quality of resulting glulam. Mangium (Acacia mangium) and mahogany (Swietenia mahogany) woods were laminated with samama wood using isocyanate adhesive at a spread rate of 200 g m-2 and then clamped with 30 cm gap between the clamp for 3 hours. Nine types of glulam were made with and without a combination of 1 cm lamina from the three types of wood species. The results showed the difference of density between samama glulam with the other types. Furthermore, the moisture content, hot water delamination, cold water delamination, MOE and MOR of the products have met the requirements of JAS 2007 for structural wood. Bonding strengths of most types of glulam have met the standard except for samama and mahogany glulam without the combination. The results of this study strengthened the potency of samama as glulam material for the structural application.Keywords: glulam, mahogany, mangium, samama, structural.
Physical and Mechanical Properties of Samama Wood (Antocephalus macropylus Roxb.) Grown in Mollucas Island Tekat D Cahyono; Syarif Ohorella; Fauzi Febrianto
Jurnal Ilmu dan Teknologi Kayu Tropis Vol 10, No 1 (2012): Jurnal Ilmu dan Teknologi Kayu Tropis
Publisher : Masyarakat Peneliti Kayu Indonesia

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (229.039 KB) | DOI: 10.51850/jitkt.v10i1.123

Abstract

People are less interest to the fast growing species since the quality is inferior compared to commercial wood. A research has been done to identify the physical and mechanical properties of samama wood (Antocephalus macrophylus (Roxb.)) from Mollucas island. Eight years old samama wood with diameter of 30 - 45 cm and height of 8 – 11 meter were used as samples. The parameters measured were moisture content (MC), specific gravity (SG), tangential and radial shrinkages, bending strength (MOR and MOE), tension and compression strengths parallel to grain and hardness. The result showed that the MC of samama wood decreased from bottom to upper and from outer to inner parts, while SG decreased from bottom to upper and from inner to outer part. Tangential and radial shrinkages of samama wood were much affected by vertical position. The MOE and MOR of samama wood decreased from bottom to upper part, while tension and compression strengths parallel to grain direction decreased form inner to outer part. On the other hand, hardness of samama wood decreased from bottom to upper and from inner to outer parts. Based on PKK NI5-1961 classification, samama wood belonged to strength class of III and IV.Key words: mechanical properties, Mollucas Island, physical properties, samama wood
Kualitas Kayu Lapis dari Finir Bagian Juvenil dan Dewasa Samama (The Quality of Plywood Made from Juvenile and Mature Wood Veneer of Samama Tekat D Cahyono; Imam Wahyudi; Trisna Priadi; Fauzi Febrianto
Jurnal Ilmu dan Teknologi Kayu Tropis Vol 15, No 2 (2017): Jurnal Ilmu dan Teknologi Kayu Tropis
Publisher : Masyarakat Peneliti Kayu Indonesia

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (319.981 KB) | DOI: 10.51850/jitkt.v15i2.394

Abstract

This study designed 7 types of plywood that were arranged by juvenile and mature part of samama (Anthocephalus macrophyllus) wood, The adhesive used was urea formaldehyde with addition of hardener (NH4Cl) in ratio of 100:1 (weight/weight). The adhesive was applied on both surfaces of core veneer, which were loose and tight surfaces, with glue spread was 150 g m-2. The veneers were arranged in accordance with the research design and the resulted structures were then hot pressed at 110 C for 30 seconds per mm of the plywood’s thickness. The pressure was 10 kg cm-2. The results showed that bonding strength of plywood made from juvenile samama veneer was lower than that of the mature one, although the value was still met SNI standard for type I interior plywood. Furthermore, plywood’s moisture content was also met the requirement of the standard. Plywood density was increased by 11-12% from that of the wood. These findings suggest the suitability of both juvenile and mature wood of samama for the material of good quality plywood. Further studies on determination of other veneer-based products, such as laminated veneer lumber (LVL), were then recommended.Keywords: juvenile, mature, plywood, samama, urea formaldehyde
Some Chemical Properties and Natural Durability of Samama Wood (Antocephalus macrophylus Roxb.) against Subterranean Termite Tekat D Cahyono; Syarif Ohorella; Fauzi Febrianto
Jurnal Ilmu dan Teknologi Kayu Tropis Vol 10, No 2 (2012): Jurnal Ilmu dan Teknologi Kayu Tropis
Publisher : Masyarakat Peneliti Kayu Indonesia

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (210.59 KB) | DOI: 10.51850/jitkt.v10i2.116

Abstract

Samama wood (Antocephalus macrophylus Roxb.) is an endemic wood of Sulawesi and Moluccas. This wood belongs to the 3rd class of wood strength. However, its natural durability against termite attack is still unknown. Therefore, the research about its extractives, ash content, heating value, and natural durability is paramount to appropriate usage of the wood. The samples were prepared from samama wood with diameter and height of 30-45 cm and 8.2-11.4 m, respectively. The results indicated that the extractive solubility in hot water, cold water and ethanol benzene were 7.83, 3.86, and 4.47%, respectively. The ash content was 1.31%, meanwhile the heating value was 4059 cal g-1. Based on its weight loss value, according to SNI 01-7207-2006 standard, the natural durability of samama wood against subterranean termite (Coptotermes curvignathus) is classified as in the 2nd class.Key words : Antocephalus macrophylus, extractives, heating value, natural durability, subterranean termite
Physical and Mechanical Properties of Samama Wood Glulam Tekat D Cahyono; Syarif Ohorella; Fauzi Febrianto; Trisna Priadi; Imam Wahyudi
Jurnal Ilmu dan Teknologi Kayu Tropis Vol 12, No 2 (2014): Jurnal Ilmu dan Teknologi Kayu Tropis
Publisher : Masyarakat Peneliti Kayu Indonesia

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (391.208 KB) | DOI: 10.51850/jitkt.v12i2.74

Abstract

In the present research, four types of samama wood (Anthocephallus macrophyllus) glulam of (3 x 6 x 120) cm3 (thickness, width, length) in size were prepared. Two types of glulam were assembled with the same thickness of lamina and two other types were assembled with lamina of different thickness. The result showed that the average moisture content and densities of the glulam were of 12.48% and 0.41, respectively. The MOE, MOR, and shear strength of the glulam were in the average of 6.08 GPa, 33.06 MPa, 30.08 kg cm-2, respectively. The highest MOE and MOR were obtained by the D type glulam. All types of the produced glulam contributed to the increase of MOE and MOR by 31 and 23% of those of its solid wood, respectively.Keywords: glulam, mechanical properties, physical properties, samama wood